Highly corrosion-resistant, rust-prevention coating material, highly corrosion-resistant steel, and steel structure

ABSTRACT

A highly corrosion-resistant, rust-prevention coating material comprising:
         an inorganic binder; and   Zn metal particles comprised of Zn and unavoidable impurities and dispersed in the binder at the rate of 30 mass % or greater based on a dry coating film,   wherein (i) the Zn metal particles include (i-1) fine-grain Zn metal particles of 0.05 to 5 μm peak grain diameter whose grain-diameter distribution has a grain-diameter frequency distribution with a single peak and a tail on either side of the peak and (i-2) coarse-grain Zn metal particles of 6 to 100 μm peak grain diameter whose grain-diameter distribution has a grain-diameter frequency distribution with another single peak and a tail on either side of the peak, and   wherein (ii) the percentage of all Zn metal particles accounted for by Zn metal particles of 0.05 to 5 μm grain diameter expressed in volume percentage is 5 to 99%.

FIELD OF THE INVENTION

This invention relates to a highly corrosion-resistant, rust-prevention coating material and a highly corrosion-resistant steel, particularly to a highly corrosion-resistant, rust-prevention coating material that exhibits outstanding corrosion resistance and rust prevention when applied to the surface of various types of steel, to a highly corrosion-resistant steel coated with the coating material, and to a steel structure including the steel.

DESCRIPTION OF THE RELATED ART

Rust-prevention coating materials containing large amounts of Zn particles, specifically zinc-rich paints, are in general use as rust-prevention coating materials against combating steel rusting. The Zn particles used in a zinc-rich paint are usually produced by the mist process. Zn particles (grains) produced by the mist process are spherical particles with a grain diameter distribution wherein the average grain diameter has a single frequency peak in the region of from several to several tens of μm.

The Zn particles are used mainly in the undercoating of heavy-duty corrosion preventive coating. The rust-prevention mechanism is characterized in utilizing the sacrificial corrosion protection effect of the Zn particles contained in the coating.

The rust-prevention performance of a zinc-rich paint coating therefore depends heavily on the sacrificial corrosion protection effect of the Zn particles. In some use environments, the rate of Zn consumption is so high that the protective effect with respect to the steel does not last very long.

Countermeasures include that of reducing the average grain diameter of the Zn particles in the coating material and that of increasing the coating thickness. But these expedients may lead to a decline in adherence to the steel and ready occurrence of coat cracking and sagging. In other words, it has been difficult to achieve a coating that offers excellent rust prevention performance while also being good in physical properties and easy to apply. The aforesaid countermeasures thus leave much to be desired.

In view of this situation, a need has been felt for the development of a high-performance zinc-rich paint that preserves the current merits of such paints and further exhibits sacrificial corrosion protection over the long term. A number of proposals for this purpose have been reported.

For example, Japanese Patent Publication (A) No. H08-151538 ('538) teaches an organic coating composition reduced in Zn particle and other metal content by addition of a bonding agent and metal powder of less than −750 mV potential.

Inventions aimed at improving corrosion resistance by combining new alloy particles have also been reported.

For example, Japanese Patent Publication (A) No. H01-3111178 ('178) teaches a zinc-rich paint containing Zn alloy particles and Mn particles in addition to Zn particles. And Japanese Patent Publication (A) No. 2001-164194 ('194) teaches a corrosion-resistant coating material containing Zn—Al—Mg alloy particles.

These inventions attempt to enhance corrosion resistance by combining Zn—Mg alloy particles and an organic resin such as epoxy resin or urethane resin.

In addition, Japanese Patent Publication (A) No. H02-73932 ('932) teaches use of an inorganic binder. The technology of this publication exploits the long-life performance of inorganic Zn—Mg particles having a metal structure composed of Zn and MgZn₂.

A number of other studies have approached the issue from the aspect of particle shape. For example, Japanese Patent Publication (A) No. 2002-285102 ('102) and Japanese Patent Publication (A) No. 2005-336431 ('431) teach inorganic corrosion resistant coating materials containing flaky particles of Zn—Mg alloy and corrosion-resistant steels coated with the coating materials.

SUMMARY OF THE INVENTION

Although '538 achieves corrosion resistance superior to that of conventional zinc-rich paints by using a binding agent and controlling metal powder potential, it is an ordinary organic coating material readily degraded in an environment involving a combination of elements like ultraviolet rays, moisture and oxygen, so that it is vulnerable to secondary issues such the need for relatively frequent maintenance.

Another problem with '538 that must be addressed is that it generates much toxic gas during baking.

'178 and '194 use mainly organic binders and '932 uses mainly an inorganic binder. All three teach use of high-corrosion-resistance particles such as Mg, Al and the like as metal particles.

They improve corrosion resistance by forming MgZn₂ and Mg₂Zn₁₁ intermetallic compounds. Specifically, the intermetallic compounds are present inside alloy particles whose surfaces are covered with an oxide layer or Zn and Mg solid solution phase.

The intermetallic compound phase having high corrosion resistance therefore cannot easily appear at the alloy particle surfaces. As a result, corrosion resistance is inadequate.

Moreover, when low-electrical-conductivity ZnCl₂.4Zn(OH)₂.H₂O forms in the main rust component, the sacrificial corrosion protection effect is not thoroughly manifested. This is another issue that must be overcome.

The alloy particles are most often produced by ingot fragmentation, the atomization process or the mist process. Reliable production of the alloy particles on an industrial scale is therefore impossible. This is another point requiring attention.

Although '102 and '431 teach flaky alloy particles, spray-coating of flaky alloy particles is difficult. Flaky alloy particles cannot achieve adequate coating film adherence by conventional airless spraying, so that improvement is necessary in this regard.

The object of this invention is therefore to provide a highly corrosion-resistant, rust-prevention coating material and a highly corrosion-resistant steel that exhibit corrosion resistance and rust prevention markedly superior to that obtainable heretofore. It achieves this object by, unlike what has been possible heretofore, producing Zn metal particles or Zn alloy particles that have two different peak grain diameters or average grain diameters, particularly Zn metal particles or Zn alloy particles having two peaks including one added on the fine-grain side, and combining these particles with an inorganic or organic binder.

In the present invention, Zn metal particles comprised of Zn and unavoidable impurities are dispersed in the binder of the rust-prevention coating material in an amount of 30 mass % or greater based on the dry coating film. The inventors accomplished the invention by taking advantage of the following fundamental knowledge acquired in the course of a broad-ranging study.

Outstanding corrosion resistance, rust prevention and coating property are exhibited when the Zn metal particles used have a grain diameter distribution including two peaks, namely, when the Zn metal particles used include both (i) fine-grain Zn metal particles of 0.05 to 5 μm peak grain diameter or 0.01 to 5 μm average grain diameter and (ii) coarse-grain Zn metal particles of 6 to 100 μm peak grain diameter or average grain diameter, and the percentage of all Zn metal particles accounted for by fine-grain Zn metal particles of 0.05 to 5 μm grain diameter expressed in volume percent is 5% to 99%.

The inventors further conducted a detailed study regarding the possibility of further improving the corrosion resistance and rust prevention offered by the aforesaid particles having a grain diameter distribution including two peaks.

As a result, they learned that a rust-prevention coating material excellent rust prevention can be obtained by using as the fine-grain Zn metal particles or coarse-grain Zn metal particles Zn alloy particles containing, in mass %, 0.01 to 30% Mg and further that a rust-prevention coating material of still more excellent rust prevention performance can be obtained by incorporating in the Zn alloy particles, in mass %, one or both of Al: 0.01 to 30% and Si: 0.01 to 3%.

The inventors also conducted studies focused on the shape and state of the Zn alloy particles and the Zn—Mg—Al—Si alloy particles containing one or both of Al: 0.01 to 30 mass % and Si: 0.01 to 3 mass %.

As a result, they ascertained that rust prevention improves, probably owing to improved spontaneous dissolving property, when the fine-grain alloy particles or coarse-grain alloy particles are not spherical but are shaped bodies that are formed by fragmentation or the like to have multiple flat or curved surfaces each enclosed by a single contour line and that have physical fragmentation (fracture) faces or cracks on the surfaces thereof.

A particularly noteworthy finding was that rust prevention improves dramatically when cracks of 0.01 μm or greater length and 0.01 μm or greater depth are present. The inventors further found that in this case a notable additional improvement in rust prevention is observed when one or more of the intermetallic compounds MgZn₂, Mg₂Zn₁₁, MgZn and Mg₂Zn₃ are present on the fragmentation surfaces.

The inventors further made an in-depth study with regard to a method for producing Zn metal particles having two grain-diameter frequency peaks in the grain-diameter distribution.

As a result, they discovered that Zn alloy particles that have not only a grain-diameter frequency peak like the conventional one but also a grain-diameter frequency peak farther to the fine-grain side than the conventional one and that exhibit even better corrosion resistance and rust prevention can be formed by producing primary particles by an ordinary method like the mist process or gas-atomization process and thereafter causing the particles to collide with one another or collide with another solid body.

The Zn alloy particles having the two grain-diameter frequency peaks exhibit excellent corrosion resistance and rust prevention when used as coating material pigment without modification. However, a further investigation revealed that when used as mixed with conventional, widely-employed Zn particle pigment produced by an ordinary method like the mist process or gas-atomization process, there is realized corrosion resistance and rust prevention far superior to that when conventional Zn particles are used alone.

The inventors further found that an organic coating material using the invention Zn metal particles or Zn alloy particles as pigment exhibits excellent corrosion resistance and rust prevention not heretofore achievable, even in a severe environment including a combination of organic coating material degrading factors like ultraviolet rays, moisture and oxygen.

The inventors further carried out a thorough study regarding the distribution of the Zn metal particles in the dry coating film and learned that an additional improvement in corrosion resistance and rust prevention can be achieved by concentrating the fine-grain Zn alloy particles in the film surface layer.

The present invention was accomplished based on the foregoing knowledge. The gist of the invention is as set out below.

(1) A highly corrosion-resistant, rust-prevention coating material comprising:

an inorganic binder; and

Zn metal particles comprised of Zn and unavoidable impurities and dispersed in the binder at the rate of 30 mass % or greater based on a dry coating film,

wherein (i) the Zn metal particles include (i-1) fine-grain Zn metal particles of 0.05 to 5 μm peak grain diameter whose grain-diameter distribution has a grain-diameter frequency distribution with a single peak and a tail on either side of the peak and (i-2) coarse-grain Zn metal particles of 6 to 100 μm peak grain diameter whose grain-diameter distribution has a grain-diameter frequency distribution with another single peak and a tail on either side of the peak, and

wherein (ii) the percentage of all Zn metal particles accounted for by Zn metal particles of 0.05 to 5 μm grain diameter expressed in volume percentage is 5 to 99%.

(2) A highly corrosion-resistant, rust-prevention coating material comprising:

an inorganic binder; and

Zn metal particles comprised of Zn and unavoidable impurities and dispersed in the binder at the rate of 30 mass % or greater based on a dry coating film,

wherein (i) the Zn metal particles include (i-1) fine-grain Zn metal particles of 0.01 to 5 μm average grain diameter whose grain-diameter distribution has a grain-diameter frequency distribution with a single peak and a tail on either side of the peak and (i-2) coarse-grain Zn metal particles of 6 to 100 μm average grain diameter whose grain-diameter distribution has a grain-diameter frequency distribution with another single peak and a tail on either side of the peak, and

wherein (ii) the percentage of the fine-grain Zn metal particles and coarse-grain Zn metal particles accounted for by the fine-grain Zn metal particles expressed in volume percentage is 5 to 99%.

(3) A highly corrosion-resistant, rust-prevention coating material according to (1) or (2), wherein the metal particles are Zn alloy particles containing, in mass %, Mg: 0.01 to 30% and a balance of Zn and unavoidable impurities.

(4) A highly corrosion-resistant, rust-prevention coating material according to (1) or (2), wherein the zinc metal particles are mixed particles including (a) zinc metal particles containing Zn and unavoidable impurities and (b) Zn alloy particles containing, in mass %, Mg: 0.01 to 30% and a balance of Zn and unavoidable impurities.

(5) A highly corrosion-resistant, rust-prevention coating material according to (3) or (4), wherein the Zn alloy particles further contain, in mass %, one or both of Al: 0.01 to 30% and Si: 0.01 to 3%.

(6) A highly corrosion-resistant, rust-prevention coating material according to any of (3) to (5), wherein the Zn alloy particles have physical fracture facets and/or cracks of 0.01 μm or greater length or cracks of 0.01 μm or greater depth, and Mg solid solution phase and Zn—Mg intermetallic compounds are present at the fragmentation faces and/or cracks

(7) A highly corrosion-resistant, rust-prevention coating material according to (6), wherein an average value of the aspect ratio (maximum grain diameter/minimum grain diameter) of the Zn alloy particles is 1 to 1.5.

(8) A highly corrosion-resistant, rust-prevention coating material according to (6) or (7), wherein the Zn—Mg intermetallic compounds are one or more of MgZn₂, Mg₂Zn₁₁, Mg₂Zn₃, MgZn and Mg₇Zn₃.

(9) A highly corrosion-resistant, rust-prevention coating material according to any of (3) to (8), wherein the Zn alloy particles are polyhedrons having multiple flat or curved surfaces each enclosed by a single contour line.

(10) A highly corrosion-resistant, rust-prevention coating material according to any of (3) to (9), which has dispersed in the binder thereof not only said fine-grain Zn alloy particles and coarse-grain Zn alloy particles but also Zn metal particles of an average grain diameter of 0.05 to 50 μm containing Zn and a balance of unavoidable impurities, wherein (a) the total volume percentage of all metal particles accounted for by Zn alloy particles of a grain diameter of 0.05 to 5 μm expressed in volume percentage is 5 to 99% and (b) the metal particles are in total dispersed in the binder at the rate of 30 mass % or greater based on a dry coating film.

(11) A highly corrosion-resistant, rust-prevention coating material according to (10), wherein the ratio, in mass %, of (amount of the fine-grain and coarse-grain Zn metal particles or amount of the fine-grain and coarse-grain Zn alloy particles): (amount of the Zn metal particles of an average grain diameter of 0.05 to 50 μm containing Zn and a balance of unavoidable impurities) is, when expressed as 1/x, such that x is 300.0 or less.

(12) A highly corrosion-resistant, rust-prevention coating material according to (11), wherein the Mg content of the mixed particles including the Zn alloy particles and the Zn metal particles of an average grain diameter of 0.05 to 50 μm containing Zn and a balance of unavoidable impurities is 0.01 to less than 30 mass % where the total of the mixed particles is defined as 100 mass %.

(13) A highly corrosion-resistant, rust-prevention coating material according to any of (1) to (12), wherein an organic binder is used instead of the inorganic binder.

(14) A highly corrosion-resistant steel coated with a highly corrosion-resistant, rust-prevention coating material set out in any of (1) to (13), wherein the thickness of the dry coating film is 2 to 700 μl and the fine-grain Zn metal particles and coarse-grain Zn metal particles or the fine-grain Zn alloy particles and coarse-grain Zn alloy particles are dispersed in the coating film.

(15) A highly corrosion-resistant steel coated with a highly corrosion-resistant, rust-prevention coating material set out in any of (3) to (13),

wherein the thickness of the dry coating film is 2 to 700 μm and the fine-grain Zn alloy particles and coarse-grain Zn alloy particles are dispersed in the coating film, and

wherein the content ratio of the fine-grain Zn alloy particles of a grain diameter of 0.05 to 5 μm in an outermost 10% thickness surface layer region of the dry film is twice or greater the content ratio of the fine-grain Zn alloy particles of a grain diameter of 0.05 to 5 μm in the whole dry film.

(16) A steel structure equipped partially or completely with the highly corrosion-resistant steel set out in (14) or (15).

This invention enables provision of highly corrosion-resistant coating material and highly corrosion-resistant steel that exhibit excellent corrosion-resistance and rust prevention unattainable using the metal particles added to conventional rust-prevention coating materials. It achieves this improvement over the prior art by producing Zn metal particles or Zn alloy particles having two grain-diameter frequency peaks in the grain-diameter frequency distribution and combining the particles with an inorganic or organic binder.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a diagram showing the grain-diameter distribution of the Zn metal particles contained in a conventional zinc-rich primer. It shows part of the results obtained by laser scattering particle distribution analysis. The horizontal axis is scaled for grain diameter (μm) represented as equivalent spherical diameter. The vertical axis is scaled for frequency distribution (%) represented as equivalent spherical volume.

FIG. 2 is a diagram showing and example of the grain-diameter distribution of Zn alloy particles contained in the invention highly corrosion-resistant, rust-prevention coating material. It shows part of the results obtained by laser scattering particle distribution analysis. The horizontal axis is scaled for grain diameter (μm) represented as equivalent spherical diameter. The vertical axis is scaled for frequency distribution (%) represented as equivalent spherical volume.

DETAILED DESCRIPTION OF THE INVENTION

The requirements specified by the present invention will be explained in detail.

The invention does not particularly specify the method of producing the Zn metal particles and Zn alloy particles used. The coarse-grain Zn metal particles and coarse-grain Zn alloy particles of the invention can, for example, be produced by general-purpose powder production methods such as the mist process or the atomization process.

The fine-grain Zn metal particles and fine-grain Zn alloy particles can be produced by the mist process or the atomization process. They can also be produced by a physical fragmentation method that causes Zn metal particles or Zn alloy particles produced by one of the foregoing processes to collide directly or indirectly with one another.

As specific physical fracture methods can be mentioned, for instance, that of adding Zn metal particles or Zn alloy particles obtained by the mist process or atomization process to toluene or xylene and jetting the so-obtained slurry so as to bring counterflows into collision with one another, and that of causing a jetted stream of the slurry to collide perpendicularly with a separate flat solid body.

The Zn metal particles or Zn alloy particles contained in the highly corrosion-resistant, rust-prevention coating material according to the invention must be composed of (i-1) fine-grain Zn metal particles or fine-grain Zn alloy particles of 0.05 to 5 μm peak grain diameter or 0.01 to 5 μm average diameter whose grain-diameter distribution has a grain-diameter frequency distribution with a single peak and a tail on either side of the peak and (i-2) coarse-grain Zn metal particles or coarse-grain Zn alloy particles of 6 to 100 μm peak grain diameter or average grain diameter whose grain-diameter distribution has a grain-diameter frequency distribution with another single peak and a tail on either side of the peak.

Although Zn metal particles that have a single grain-diameter frequency distribution peak, like those contained in conventional rust-prevention coating materials, can be produced at low cost, they are limited with regard to improvement of the metal particle filling factor because, on average, particles of the same size come to be evenly distributed in the coating film.

Although the approach to corrosion resistance improvement has been to reduce the peak grain diameter or average grain diameter of the metal particle grain-diameter distribution, thereby increasing the filling factor, or to increase film thickness, adequate corrosion resistance improvement has not been achieved because these measures cause film cracking and sagging.

In contrast, the present invention imparts two grain-diameter frequency peaks to the grain-diameter distribution of the Zn metal particles or Zn alloy particles, thus increasing the filling factor and making it possible to markedly improve corrosion resistance without application of a thick coat.

The grain-diameter distribution of the Zn metal particles and Zn alloy particles can be determined by dispersing the Zn metal particles or Zn alloy particles in an organic solvent such as toluene or xylene having a moisture content of 0.8% or less and conducting laser scattering particle distribution analysis in this state.

When the moisture content is high, caution is required because the grain diameters change owing to a reaction between the Zn metal particles or Zn alloy particles and water.

In accordance with the principle of laser scattering analysis, the grain-diameter distribution is determined from the equivalent spherical diameters of the Zn metal particle or Zn alloy particle grain diameters.

The grain-diameter distribution can be represented as a histogram by representing the grain diameter d (μm) logarithmically on the horizontal axis, defining 25 to 27 d segments on the logarithmic representation for the individual orders of magnitude change in d, and linearly representing the frequency (vol %) detected for every d segment on the vertical axis.

In this invention, fragmenting the Zn alloy particles so as to form physical fragmentation (fracture) facets or cracks on the surfaces thereof produces an improvement in corrosion resistance exceeding the improvement in corrosion resistance that can be realized by increasing the filling factor.

A “physical fragmentation (fracture) face” as termed with respect to the present invention means a face shaped by a portion of a spherical particle breaking away. As explained further later, the fact of the Zn alloy particles having physical fragmentation faces makes it possible to realize a considerable improvement in corrosion resistance and rust prevention.

A “crack” as termed with respect to the present invention means a fissure present at the spherical particle surface of a length of 0.01 μm or greater or a depth from the surface of 0.01 μm or greater. When the length or depth of the cracks is less than 0.01 μm, an adequate improvement in corrosion resistance cannot be obtained. A length or depth of 0.01 μm or greater is therefore necessary.

The cracks are often formed as a byproduct of the fragmentation for obtaining the physical fragmentation faces. Regarding the abundance of cracks, it is preferable for 1 or more cracks of 0.01 μm or greater length or depth to be seen in 20% or greater of the number of Zn alloy particles per field of observation when the Zn alloy particles are observed with a scanning electron microscope or the like.

When the peak grain diameter of the grain-diameter distribution of the fine-grain Zn metal particles or fine-grain Zn alloy particles is less than 0.05 μm, or when the average grain diameter thereof is less than 0.01 μm, loss from the surfaces tends to occur owing to mechanical removal or chemical extraction, so that adequate sacrificial corrosion protection cannot be obtained. Therefore, the lower limit of the peak grain diameter was defined as 0.05 μm and the lower limit of the average grain diameter as 0.01 μm.

Two grain diameter frequency peaks cannot be obtained when the peak grain diameter or average grain diameter of the fine-grain Zn metal particles or fine-grain Zn alloy particles exceeds 5 μm, so 5 μm was defined as the upper limit.

The peak grain diameter or average grain diameter of the grain-diameter distribution of the coarse-grain Zn metal particles or coarse-grain Zn alloy particles was defined as 6 μm or greater because when it is less than 6 μm, the corrosion resistance and rust prevention saturate and, in addition, it becomes impossible to obtain two grain diameter frequency peaks.

When the peak grain diameter or average grain diameter of the grain-diameter distribution of the coarse-grain Zn metal particles or coarse-grain Zn alloy particles exceeds 100 μm, stable spray coating or brush coating cannot be achieved. The upper limit was therefore defined as 100 μm.

When coating property and adherence are a concern in addition to corrosion resistance, it is preferable to define the peak grain diameter or average grain diameter of the grain-diameter distribution of the fine-grain Zn metal particles or fine-grain Zn alloy particles as 1 to 4 μm and the peak grain diameter or average grain diameter of the grain-diameter distribution of the coarse-grain Zn metal particles or coarse-grain Zn alloy particles as 6 to 20 μm.

Further, from the viewpoint of achieving stable spray coating, it is preferable to define the peak grain diameter or average grain diameter of the grain-diameter distribution of the fine-grain Zn metal particles or fine-grain Zn alloy particles as 1.5 to 2.5 μm and the peak grain diameter or average grain diameter of the grain-diameter distribution of the coarse-grain Zn metal particles or coarse-grain Zn alloy particles as 8.5 to 11.5 μm.

Insofar as the particle diameters are within the foregoing ranges, no limit is placed on the width ratios of the two different grain diameter frequency peaks. However, sharper grain diameter frequency peaks are preferable from the viewpoint of maximizing rust prevention performance.

Among all of the particles contained in the invention highly corrosion-resistant, rust-prevention coating material, i.e., among the combined total of the fine-grain Zn metal particles or fine-grain Zn alloy particles whose peak grain diameter or average grain diameter of the grain-diameter distribution is 0.05 to 5 μm and the coarse-grain Zn metal particles or coarse-grain Zn alloy particles whose peak grain diameter or average grain diameter of the grain-diameter distribution is 6 to 100 μm, the percentage of the particles accounted for by particles of 0.05 to 5 μm diameter, expressed in volume percentage, must be 5% or greater.

When the percentage is less than 5%, no pronounced improvement of corrosion resistance and rust prevention is observed.

The maximum percentage accounted for by particles of 0.05 to 5 μm diameter contained in the invention highly corrosion-resistant, rust-prevention coating material, expressed in volume percentage, is defined as 99% because corrosion resistance improves in proportion as the percentage of fine-grain Zn metal particles or fine-grain Zn alloy particles increases.

At greater than 99%, however, the excessive fine-grain Zn metal particles do not contribute to, but may detract from, the effect of improving corrosion resistance. The upper limit is therefore defined as 99%.

Insofar as the percentage of all Zn metal particles having two grain diameter frequency peaks accounted for by Zn metal particles of 0.05 to 5 μm diameter, expressed in volume percentage, is 5 to 99%, a dramatic improvement in corrosion resistance and rust prevention can be achieved even if Zn metal particles produced by the mist process or gas atomization process are combined.

From the viewpoint of the applied film, it is necessary for the fine-grain Zn metal particles or fine-grain Zn alloy particles and the coarse-grain Zn metal particles or coarse-grain Zn alloy particles to be present in a total amount of 30 mass % or greater based on the dry coating film. Excellent corrosion resistance and rust prevention cannot be realized when the content is less than 30 mass %.

In the present invention, the presence of the two grain diameter frequency peaks enables marked improvement of corrosion resistance and rust prevention even when Zn alloy particles obtained by adding Mg, Al, Si or the like to Zn are combined with conventional Zn metal particles.

The corrosion resistance and rust prevention improving effect produced by the Zn alloy particles or the mixed Zn metal particles and Zn alloy particles having two grain diameter frequency peaks is more pronounced than the corrosion resistance and rust prevention improving effect produced by the Zn alloy particles having two grain diameter frequency peak.

Reasons for this stronger corrosion resistance improvement include, among others, an increase in the grain-diameter frequency distribution on the fine-grain side attributable to Mg addition and exposure of physical fracture facets and cracks.

No substantial improvement in rust prevention performance is obtained when the Mg content of the Zn alloy particles is less than 0.01 mass % and rust prevention performance declines when the Mg content exceeds 30 mass %. Mg content is therefore defined as 0.01 to 30 mass %.

In order to enhance physical fragmentation property and crack occurrence by adding Mg to the Zn alloy, Mg is preferably added to a content of 0.5 to 15 mass %. As Mg is more expensive than Zn, an Mg content of 0.5 to 10 mass % is economically preferable.

The mixing ratio of the Zn metal particles and Zn alloy particles need not be defined insofar as the aforesaid composition limits are observed. However, Mg addition produces no substantial improvement in rust prevention at an Mg content of less than 0.01 mass %, while Mg addition has a reverse effect at a content exceeding 30 mass %. The total Mg content is therefore preferably 0.01 to 30 mass %.

Although corrosion resistance improves with increasing Mg content, Mg is a more expensive material than Zn. Since overall material cost is therefore increased by Mg addition, the total Mg content is preferably 0.01 to 10 mass % for optimum balance between corrosion resistance and economy.

Moreover, the inventors discovered that addition of general-purpose Zn metal particles of 2 to 20 μm average grain diameter to Zn alloy particles having two grain diameter frequency peaks in the grain-diameter distribution enables a major improvement in economy without loss of steel corrosion resistance enhancing effect.

However, in this case too, it is necessary for the volume percentage of the total of the Zn alloy particles and Zn metal particles accounted for by Zn alloy particles of 0.05 to 5 μm diameter to be 5 to 99% and for the Zn alloy particles and Zn metal particles to be dispersed in a total amount of 30 mass % or greater based on the dry coating film.

Further, as regards the mixing of the Zn alloy particles and Zn metal particles, it is preferable from the viewpoint of improving corrosion resistance and rust prevention to conduct the mixing under a condition whereby the ratio, in mass %, of (Zn alloy particle content %): (Zn metal particle content %) is, when expressed as 1/x, such that x is 300.0 or less.

When x exceeds 300.0, the effect of Zn alloy particle addition toward improvement of corrosion resistance and rust prevention ceases to be observed and x must therefore be made 300.0 or less.

When top priority is placed on corrosion resistance, it is preferable to increase the percentage of Zn alloy particles without limit so that the percentage of Zn metal particles approaches zero. However, in the interest of striking a practical balance between corrosion resistance and economy, the ratio (Zn alloy particle content %):(Zn metal particle content %) is preferably between 1:1 and 1:120. From the aspect of mixing stability, the ratio is preferably between 1:1 and 1:30.

In the present invention, the average grain diameter in the grain-diameter distribution of the Zn metal particles used in the mixture is, from the standpoint of optimizing economy and filling factor, preferably 2 to 50 μm, which is an intermediate grain diameter range in the grain-diameter distribution having two grain diameter frequency peaks.

It is worth noting that addition of general-purpose Zn metal particles of 2 to 50 μm average grain diameter to Zn metal particles having two grain diameter frequency peaks in the grain-diameter distribution makes it possible to achieve better economy while retaining the effect of steel corrosion resistance improvement.

In the present invention, corrosion resistance can be increased by adding one or both of Al and Si to the Zn alloy.

No effect of improving rust prevention performance is obtained when the Al content of the Zn alloy particles is less than 0.01 mass %. When Al is present at content exceeding 30 mass %, it impairs the physical fragmentation property by incorporating Mg in solid solution. Al content is therefore defined as 0.01 to 30 mass %.

From the aspects of rust prevention performance and ease of occurrence of physical fracture facets and/or cracks, Al content is preferably 0.01 to 10 mass %, and when physical fragmentation property is a primary concern, it is preferably 0.01 to 2 mass %

No effect of improving coating film adherence or physical fragmentation property is obtained when the Si content of the Zn alloy particles is less than 0.01 mass %. When Si is present at a content exceeding 3 mass %, corrosion resistance declines. Si content is therefore defined as 0.01 to 3 mass %. In order to maximize coating film adherence and corrosion resistance, Si content is preferably 0.1 to 1 mass %.

The mixing ratio of Al and Si in the coating film need not be defined insofar as the Al and Si contents are within the aforesaid ranges. From the viewpoint of corrosion resistance, the contents are preferably Al: 0.01 to 1.0 mass % and Si: 0.01 to 1.0 mass %.

The Zn alloy particles containing Mg contain intermetallic compounds and can be provided with physical fragmentation faces and/or cracks on their outer surface during the fine alloy particle production process.

The intermetallic compounds are compounds of Mg and Zn combined in simple whole-number ratios. Examples include MgZn₂, Mg₂Zn₁₁, MgZn, Mg₂Zn₃, and Mg₇Zn₃. Among these intermetallic compound, MgZn₂ and Mg₂Zn₁₁ are particularly preferable from the viewpoint of fragmentation property and corrosion resistance.

Corrosion resistance and rust prevention improve further when the metal particles are not spherical but are physically fragmented into the shape of sphere-like polyhedrons. The sphere-like polyhedrons are quasi-spheres formed by physical fragmentation of spherical particles. Polyhedrons having 2 or more faces are preferable for optimizing the balance among coating film adherence, economy and corrosion resistance. Polyhedrons having 6 or more faces are preferable for corrosion resistance improvement.

Such Zn metal particles and Zn alloy particles are dispersed in a vehicle (liquid binder) to obtain the highly corrosion-resistant, rust-prevention coating material of this invention. Usable vehicles include, for example, inorganic binders such as alkyl silicate and alkali silicate, and organic binders such as epoxy resin, urethane resin, phenoxy resin and polyester resin.

Other liquid binders are also usable, including any of the liquid binders used in zinc-rich paints. The coating material can be either of the emulsion type or the solvent type.

Other ordinary additives can be incorporated within ranges not impairing corrosion resistance For example, when the coating material is to be used to form a corrosion preventive primer coat, a third component such as boron can be added to enhance adherence with the topcoat.

In order to achieve rust prevention capability, the mixing of the Zn metal particles and Zn alloy particles with the binder must be conducted so that the total of fine Zn metal particles or fine-grain Zn alloy particles and coarse-grain Zn metal particles or coarse-grain Zn alloy particles are evenly dispersed in an amount of 30 mass % or greater based on the dry coating film. From the viewpoint of good balance among the three properties of corrosion resistance, workability and cuttablility, the amount dispersed is preferably 40 to 65 mass %.

By keeping the moisture content of the produced coating material at 0.8% or less, it is possible to ensure that the fine-grain and coarse-grain Zn metal particles and the fine-grain and coarse-grain Zn alloy particles maintain their suitable stability and reactivity performance, thereby enabling production of a corrosion preventive coating material excellent in rust prevention.

When the highly corrosion-resistant, rust-prevention coating material according to the present invention is prepared using an inorganic binder such as alkali silicate or alkyl silicate, it is preferable at the time of applying it to a steel plate or other steel material to pretreat the base material to some degree so as to ensure strong adherence.

Although application following treatment with a hand tool or power tool is acceptable, application after blasting is desirable for obtaining high bonding strength.

When an organic binder such as epoxy resin, urethane resin, phenoxy resin or polyester resin is used, good results can be obtained by direct application to the steel plate or material. However, a coated steel plate or the like having still more excellent corrosion resistance can be obtained by subjecting the surface to blasting, phosphating or chromating beforehand.

The reason for defining the lower limit of coating thickness as 2 μm is that a coated material of adequate corrosion resistance and rust prevention cannot be obtained when the coating is thinner than 2 μm. Although rust prevention improves with increasing coat thickness, the upper limit of coating thickness must be set at 700 μm from the viewpoint of adherence performance and for preventing coat cracking after drying and coating material sagging during application.

For optimum coat performance and economy, the preferred range of coat thickness is 5 to 50 μm in combination with an inorganic binder and 5 to 100 μm in combination with an organic binder.

Moreover, with regard to the distribution of 0.05 to 5 μm grain diameter Zn alloy particles in the coating, corrosion resistance and rust prevention tend to improve when the content ratio of Zn alloy particles of a grain diameter of 0.05 to 5 μm in an outermost 10% thickness surface layer region of the dry film is high. In order to secure this corrosion resistance and rust prevention improving effect without fail, the content ratio of Zn alloy particles of a grain diameter of 0.05 to 5 μm in the outermost 10% thickness surface layer region of the dry film should be made twice or greater the content ratio of the Zn alloy particles of a grain diameter of 0.05 to 5 μm in the whole dry film. This markedly increases the high corrosion resistance and rust prevention effect of the coating film when it is applied to a steel.

EXAMPLES

Concrete embodiments of the present invention are explained in the following.

First Set of Examples

The grain-diameter distribution and average diameter of the Zn metal particles and Zn alloy particles, and the total volume percentage of particles in the 0.05 to 5 μm grain-diameter range were determined by laser scattering particle distribution analysis.

Therefore, grain diameter was evaluated as equivalent spherical diameter and volume percentage was evaluated as the equivalent spherical volume of the particles.

A histogram for evaluating grain diameter-distribution was drawn by representing grain diameters of 0.05 μm and greater on the horizontal axis and representing the proportion of the number of particles whose grain diameters fell in grain-diameter intervals d_(n) to d_(n+1) (μm) of 0.05 μm and greater diameter on the vertical axis. Here, d_(n)+1=(1+α) d_(n), where n is a natural number and α is for convenience defined as 0.09 to 0.1.

The peak value was determined from this grain-diameter histogram. In the case where grain diameter is represented as equivalent spherical diameter and grain diameter is represented logarithmically, this method makes possible to draw a histogram that, for instance, has the 1 to 10 μm range divided into 25 to 27 equal grain diameter segments.

Specifically, the histogram was created by logarithmically representing grain diameter on the horizontal axis as equivalent spherical diameter, linearly representing in every equivalent spherical diameter segment of d_(n) to less than d_(n+1) on the vertical axis the frequency f_(n) of the particles contained in the segment as the equivalent spherical volume percentage (%) of the total equivalent spherical volume of all measured particles, plotting f_(n) for every (d_(n) d_(n+1))^(1/2), and connecting neighboring plots.

The peak value is therefore the grain diameter (d_(n) d_(n+1))^(1/2) at which frequency f_(n) exhibits maximum value.

The grain-diameter distribution and average grain diameter of particles of 0.01 to 0.05 μm average diameter were determined by laser scattering particle distribution analysis using an analyzer equipped with an ultraviolet semiconductor laser.

As termed with respect to the present invention, “fine grains” means grains that, as determined by grain-diameter distribution measurement using laser scattering particle distribution analysis, are Zn metal particles or Zn alloy particles of 0.05 to 5 μm peak grain diameter or 0.01 to 5 μm average diameter having a grain-diameter frequency distribution with a single peak and a tail on either side of the peak. The term “coarse grains” means grains that are Zn metal particles or Zn alloy particles of 6 to 100 μm peak grain diameter or 6 to 100 μm average grain diameter having a grain-diameter frequency distribution with another single peak and a tail on either side of the peak.

Grain diameter distributions obtained in Examples are shown in Tables 1 to 172 as expressed in either peak grain diameter or average grain diameter.

The state of Zn metal particles and Zn alloy particles was determined by observing 50 to 100 randomly extracted particles using a scanning electron microscope equipped with a field emission electron gun.

Particle fragmentation (fracture) facets and cracked surfaces were observed with a scanning electron microscope. Zn alloy particles in particular were examined for Zn and Mg distribution state and the atomic concentration ratios of the elements by mapping analysis using an energy-dispersive X-ray analyzer attached to a scanning electron microscope. It was checked whether Zn—Mg intermetallic compounds were present and the element ratios of those found were examined.

Presence of Zn—Mg intermetallic compounds and their types were determined based on the shape of the secondary electron image, color and shape of the backscattered electron image, the mapping analysis image, the result of Zn and Mg atomic concentration ratio measurement, and result of Zn alloy particle X-ray diffraction analysis.

Specifically, Zn alloy particles for which presence of MgZn₂, Mg₂Zn₁₁ or Mg₂Zn₃ was ascertained from the X-ray diffraction analysis results were measured with an energy-dispersive X-ray analyzer for physical fragmentation (fracture) facets on the surfaces of particles of 5 μm or greater grain diameter, MgZn₂, Mg₂Zn₁₁, or Mg₂Zn₃ was identified from the results of the Zn and Mg atomic concentration ratio measurement, and the shape and color thereof was ascertained from the secondary electron image and backscattered electron image of the surface thereof.

In the case of the surface of a fine particle of less than 5 μm grain diameter which, because of its small size, could not be accurately measured for element ratio with an energy-dispersive X-ray analyzer, presence of MgZn₂, Mg₂Zn₁₁ or Mg₂Zn₃ was inferred by comparing the secondary electron image and backscattered electron image with the secondary electron image and backscattered electron image of a region other than a physical fragmentation face.

On the other hand, in the case of Zn alloy particles having an Mg concentration of 20 to 30 mass %, MgZn and Mg₇Zn₃ were determined from the results of the atomic concentration ratio measurement.

FIG. 1 shows the grain-diameter distribution of Zn metal particles contained in a conventional zinc-rich primer, which can be considered to be typical of the Comparative Examples. FIG. 2 shows the grain-diameter distribution of Zn metal particles contained in a highly corrosion-resistant, rust-prevention coating material typical of the present invention.

The grain-diameter distribution of the conventional zinc-rich primer shown in FIG. 1 has a grain-diameter frequency peak at around 10 μm. In contrast, the grain-diameter distribution of the Invention Example shown in FIG. 2, while also having one grain-diameter frequency peak similar to that of the Comparative Example at around 10 μm, further has another grain-diameter frequency peak located 2 to 3 μm toward the fine-grain side from that of the Comparative Example.

In Comparative Examples 1 to 18 shown in Table 1, almost all of the particles are accounted for by spherical Zn metal particles of around 5 to 10 μm grain diameter produced by the mist processes. On the other hand, in all of the Invention Examples shown in Tables 2 to 5 and in Comparative Examples 19 to 49 shown in Tables 2 and 3, it can be seen that, with respect to the Zn metal particles and Zn alloy particles, the particles exhibiting two grain-diameter distributions had fragmentation (fracture) facets or cracks and were non-spherical, generally granular polyhedral particles of nearly spherical shape.

When the fragmentation (fracture) facets and cracked faces of the Zn alloy particles of the Invention Examples were observed as backscattered electron images, they were found to be divided into black regions with high Mg and white regions with low Mg content. An analysis of the black regions at the fragmentation faces and cracks of the particles of 5 μm or greater grain diameter revealed the presence of intermetallic compounds, chiefly of MgZn₂ and Mg₂Zn₁₁ but in some cases Mg₂Zn₃, MgZn and Mg₇Zn₃.

Second Set of Examples

Coated test pieces were prepared as Comparative Examples and Invention Examples under the conditions indicated in Tables 1 to 172. The Comparative Examples are shown in Tables 1 to 5 and the Invention Examples in Tables 6 to 172. The coating materials of the respective examples were prepared by ordinary methods. In all Comparative Examples and Invention Examples of Tables 1 to 3, Tables 6 to 22, Tables 43 and 44, and Tables 79 and 80, two types were separately prepared using either a commercially available ethylene silicate resin inorganic binder or a commercially available urethane resin organic binder.

In the Examples of Tables 4 and 5, Tables 23 to 42, Tables 45 to 78, Tables 81 to 98, and Tables 99 to 172, various resins were used as binders and the type of resin used in each Example is indicated.

All coating materials had a moisture content of 0.8 mass % or less. The thicknesses of the dried coats are given in the Tables.

Corrosion resistance was assessed by conducting the salt spray test of JIS K 5600 (5% NaCl spray; 35° C.). Coating test pieces measuring 150×70×3.2 mm were used. The bottom of each test piece was formed with an X-cut using a cutter. The evaluation adopted in the corrosion test was time to occurrence of red rust from the test piece surface. The test results are shown in the tables.

When time to red rusting was less than 900 hours, corrosion resistance was rated Poor and designated by the symbol P in the tables. When time to red rusting was 900 hours to less than 2,000 hours, corrosion resistance was rated acceptable (Good) and designated by the symbol G in the tables. When time to red rusting was 2,000 hours or greater, corrosion resistance was rated particularly good within the acceptable range (Excellent) and designated by the symbol E in the tables.

In comparison with the Comparative Examples 1 to 30, the Invention Examples exhibited outstanding corrosion resistance as evidenced by marked suppression of red rusting.

Tables 43 to 78 show corrosion test results with presence/absence on the particle surfaces of Mg solid solution phase and Zn intermetallic compounds, and presence/absence of MgZn₂ or Mg₂Zn₁₁.

It can be seen from Tables 43 to 78 that presence of Mg solid solution phase and Zn—Mg intermetallic compounds on the particle surfaces inhibited red rusting and that red rusting was markedly inhibited when the intermetallic compounds were MgZn₂ and/or Mg₂Zn₁₁ and in some cases MgZn₂, Mg₂Zn₁₁, Mg₂Zn₃, MgZn and/or Mg₇Zn₃.

Tables 79 to 98 show the corrosion test results obtained when the ratio of all particles accounted for by Zn alloy particles of a grain diameter of 0.05 to 5 μm in an outermost 10% thickness surface layer region of the dry film was varied.

The ratio of Zn alloy particles of a grain diameter of 0.05 to 5 μm in the outermost 10% thickness surface layer region was varied by applying coating materials varied in the ratio of Zn alloy particles of a grain diameter of 0.05 to 5 μm at the final stage of the coating.

It can be seen from Tables 79 to 98 that red rusting was markedly inhibited when the ratio of all particles accounted for by Zn alloy particles of a grain diameter of 0.05 to 5 μm in the outermost 10% thickness surface layer region was twice or greater the ratio in the whole dry film.

Tables 99 to 172 relate to Invention Examples in which Zn metal particles comprising Zn and unavoidable impurities and having a grain-diameter distribution whose peak grain diameter or average grain diameter was 2 to 50 μm were later added to and mixed with fine-grain Zn metal particles and coarse-grain Zn metal particles, or fine-grain Zn alloy particles and coarse-grain Zn alloy particles of Invention Examples, the mixed particles were used to prepare highly corrosion-resistant, rust-prevention coating materials, and the prepared coating materials were applied to steels and dried. The tables show the results of corrosion tests conducted on the so-prepared coated steels.

The results of the evaluation are shown in the Corrosion Test Results column. When time to red rusting was less than 900 hours, corrosion resistance was rated Poor and designated by the symbol P. When time to red rusting was 900 hours to less than 2,000 hours, corrosion resistance was rated acceptable (Good) and designated by the symbol G in the tables. When time to red rusting was 2,000 hours or greater, corrosion resistance was rated particularly good within the acceptable range (Excellent) and designated by the symbol E in the tables.

It can be seen from Tables 99 to 172 that when the coating material was prepared from Zn alloy particles having a grain-diameter distribution with two (fine particle and coarse particle) peaks and Zn metal particles having a grain-diameter distribution with only one peak falling between those of the fine particles and coarse particles, excellent corrosion resistance was exhibited in the case where the ratio, in mass % based on the dry coating film, of (Zn alloy particle content %):(Zn metal particle content %) was, expressed as 1/x, such that x was 300.0 or less.

It can also be seen that corrosion resistance was excellent even when Zn metal particles of 2 to 50 μm average grain diameter were later added to the fine-grain Zn metal particles and coarse-grain Zn metal particles.

TABLE 1 Metal grain Percent of diameter fine-grain Total distribution metal Metal grain metal Average (Ave grain grains chemical grain Coat Comparative grain diameter) (μm)) among metal component content content of thickness Time to Example diameter Fine grain Coarse grains (Mass %) coat (μm) red rusting No. (μm) metal grain metal (Vol %) Zn Mg Al Si (Mass %) Inorganic Organic Inorganic Organic Prior Art 1 4.77 — — — 100 0 0 0 33 15.6 5 P P Product 2 4.89 — — — 100 0 0 0 36 20.3 14 P P 3 5.05 — — — 100 0 0 0 39 24.5 50 P P 4 4.00 — — — 100 0 0 0 37 16 100 P P 5 5.11 — — — 100 0 0 0 32 55 150 P P 6 5.23 — — — 100 0 0 0 38 45 160 P P 7 5.39 — — — 100 0 0 0 47 65 170 P P 8 4.34 — — — 100 0 0 0 51 38 134 P P 9 4.32 — — — 100 0 0 0 52 42 167 P P 10 4.44 — — — 100 0 0 0 53 25 38 P P 11 4.60 — — — 100 0 0 0 49 32 268 P P 12 3.55 — — — 100 0 0 0 48 25 256 P P 13 4.66 — — — 100 0 0 0 46 36 234 P P 14 4.78 — — — 100 0 0 0 86 19 243 P P 15 6.54 — — — 100 0 0 0 88 28.6 132 P P 16 6.38 — — — 100 0 0 0 89 27 124 P P 17 4.58 — — — 100 0 0 0 90 195 87 P P 18 15.2 — — — 100 0 0 0 85 23 95 P P

TABLE 2 Metal grain diameter Percent of distribution fine-grain (Ave grain metal Total metal diameter) (μm)) grains Metal grain chemical grain Coat Comparative Average Coarse among metal component content content of thickness Time to Example grain diameter Fine grain grain grains (Mass %) coat (μm) red rusting No. (μm) metal metal (Vol %) Zn Mg Al Si (Mass %) Inorganic Organic Inorganic Organic Other 19 Deficient fine 5.6 12.8 42.04 94.5 5.5 50 23 97 P P metal grains in invention range 20 Deficient fine 0.005 6.4 38.41 93.2 6.8 30 18 94 P P metal grains in invention range 21 Deficient fine 0.007 7.8 66.80 95.6 3.2 1.2 31 38 78 P P metal grains in invention range 22 Deficient fine 0.008 13.5 76.50 87.6 4.7 5.7 2.0 42 42 213 P P metal grains in invention range 23 Deficient fine 5.1 121 43.60 94.6 5.4 38 55 93 P P metal grains in invention range 24 Deficient fine 5.6 113 34.20 78.4 15.6 3.0 3.0 53 16 97 P P metal grains in invention range 25 Deficient fine 0.005 134 5.95 90.0 10.0 66 55 99 P P metal grains in invention range 26 Deficient fine 5.3 103 6.43 80.5 15.3 4.2 77 45 102 P P metal grains in invention range 27 Deficient fine 0.006 105 78.90 91.5 7.5 1.0 54 16 105 P P metal grains in invention range 28 Deficient fine 4.5 125 44.12 95.7 3.5 0.1 0.8 39 19 177 P P metal grains in invention range 29 Deficient fine 3.6 113 5.70 82.2 17.8 35 23 99 P P metal grains in invention range 30 Deficient fine 2.7 105 67.80 91.9 3.6 2.7 1.8 65 16 56 P P metal grains in invention range 31 Deficient fine 0.5 101 14.70 70.8 26.7 2.5 55 8 100 P P metal grains in invention range

TABLE 3 Metal grain diameter distribution Percent of (Ave fine-grain Total grain diameter) metal metal (μm)) grains Metal grain chemical grain Coat Comparative Average Fine Coarse among metal component content content of thickness Time to Example grain diameter grain grain grains (Mass %) coat (μm) red rusting No. (μm) metal metal (Vol %) Zn Mg Al Si (Mass %) Inorganic Organic Inorganic Organic Other 32 Deficient 2.58 9.45 3.65 94.5 5.5 75 35 87 P P mixing ratio 33 Deficient 2.37 9.61 4.65 93.0 5.5 1.5 76 38 95 P P mixing ratio 34 Deficient 2.15 9.85 99.80 94.1 5.9 72 65 123 P P mixing ratio 35 Deficient 2.94 9.36 2.65 85.6 9.8 4.6 79 37 125 P P mixing ratio 36 Deficient 2.55 12.5 1.45 93.5 4.5 1.0 1.0 65 13 99 P P mixing ratio 37 Deficient coat 2.65 8.56 34.60 96.1 3.9 0.8 10 54 94 P P metal grains 38 Deficient coat 2.94 8.21 86.53 97.5 2.5 2.5 16 49 146 P P metal grains 39 Deficient coat 2.58 8.33 64.58 94.5 5.5 2.5 1.5 9 150 146 P P metal grains 40 Deficient 2.63 10.9 35.70 68.5 31.5 55 14 125 P P mixing ratio 41 Deficient 1.87 8.9 43.70 70.8 17.8 11.4 12 17 175 P P mixing ratio 42 Deficient 3.86 9.8 21.60 99.995 0.005 56 22 200 P P mixing ratio 43 Deficient 3.7 65.8 43.70 80.5 14.6 4.9 53 25 187 P P mixing ratio 44 Deficient 2.8 16.9 55.40 96.4 0.007 3.6 65 32 174 P P mixing ratio 45 Deficient 3.9 10.99 13.90 49.1 31.9 9.4 9.6 32 25 76 P P mixing ratio 46 Deficient 4.2 14.97 44.12 56.7 25.6 11.8 5.9 83 42 260 P P mixing ratio 47 Deficient 3.55 7.89 14.60 64.4 35.6 55 25 155 P P mixing ratio 48 Deficient 2.45 10.5 87.90 57.5 31.6 10.9 12 14 167 P P mixing ratio 49 Deficient 1.45 15.6 24.60 32.2 67.8 34 17 145 P P mixing ratio

TABLE 4 Ratio of (Zn metal grains Percent or Zn alloy Diameter of fine- grains):(Later- distribution grain added Average (peak metal Zn metal diameter diameter) of grains Zn alloy grains) of Zn metal among Zn grain Zn later- grains/Zn metal Chemical component content fracture metal Later- added Zn alloy grains grains/ of Zn metal grains/Zn surfaces grains/ added Comparative metal (μm) Zn alloy alloy grains or Ave Zn Zn Example grains Fine Coarse grains (Mass %) cracks aspect alloy metal No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio grains grains 50 — 5.6 12.8 5.66 70.7 27.5 1 0.8 Yes 1.12 — — 51 — 0.005 6.4 16.55 94.6 2.9 0 2.5 Yes 1.38 — — 52 — 0.007 7.8 21.55 94 4.5 0 1.5 Yes 1.22 — — 53 — 0.008 13.5 5.66 99.43 0.07 0 0.5 Yes 1.14 — — 54 — 5.1 121 33.66 96.82 3.1 0.04 0.04 Yes 1.02 — — 55 — 5.6 113 45.65 100 0 0 0 Yes 1.05 — — 56 — 0.005 134 49.88 68.84 29.5 0.06 1.6 Yes 1.36 — — 57 — 5.3 103 42.33 92.33 7.6 0.07 0 No 1.11 — — 58 — 0.006 105 65.44 100 0 0 0 Yes 1.07 — — 59 — 4.5 125 77.55 91.8 4.6 1.8 1.8 Yes 1.42 — — 60 — 3.6 113 96.55 82 8.3 9.2 0.5 Yes 1.38 — — 61 — 2.7 105 5.97 88.2 11.8 0 0 No 1.22 — — 62 — 0.5 101 87.77 86.06 12.9 0 1.04 No 1.14 — — 63 — 2.45 11.1 3.65 99.34 0.6 0 0.06 Yes 1.13 — — 64 — 1.85 8.92 4.65 96.82 3.1 0.04 0.04 Yes 1.02 — — 65 — 1.65 9.23 99.80 96.82 3.1 0.04 0.04 Yes 1.50 — — 66 — 2.45 9.05 2.65 100 0 0 0 No 1.13 — — 67 — 2.01 10.91 67.89 96.82 3.1 0.04 0.04 Yes 1.04 — — 68 — 1.99 11.12 56.89 96.82 3.1 0.04 0.04 Yes 1.02 — — 69 — 2.38 10.93 45.67 100 0 0 0 Yes 1.08 — — 70 — 2.49 9.34 34.67 68.5 31.5 No 1.15 — — 71 — 2.34 8.77 95.66 70.8 17.8 11.4 No 1.34 — — Coating details Mg Total content metal of all grain Comparative metal content Base Coat Example grains of coat resin thickness Coating No (Mass %) (Mass %) type (μm) method Corrosion Test Results 50 — 35 Alkali-silicate 2 Spray P 51 — 66 Alkyl silicate 37 Spray P 52 — 38 Alkali-silicate 12 Spray P 53 — 84 Alkyl silicate 160 Brush P 54 — 39 Alkali-silicate 5 Brush P 55 — 85 Alkyl silicate 12 Brush P 56 — 36 Alkali-silicate 2 Spray P 57 — 56 Alkyl silicate 18 Spray P 58 — 42 Alkyl silicate 23 Spray P 59 — 31 Epoxy resin 30 Brush P 60 — 88 Acrylic resin 77 Brush P 61 — 78 Urethane resin 254 Brush P 62 — 36 Polyester resin 47 Spray P 63 — 37 Epoxy resin 43 Spray P 64 — 45 Acrylic resin 322 Brush P 65 — 68 Urethane resin 25 Brush P 66 — 79 Polyester resin 700 Brush P 67 — 10 Alkali-silicate 22 Spray P 68 — 16 Acrylic resin 25 Spray P 69 — 9 Alkali-silicate 14 Spray P 70 — 90 Urethane resin 112 Spray P 71 — 43 Alkali-silicate 554 Spray P

TABLE 5 Percent Diameter of fine- distribution grain Average (peak metal diameter diameter) of grains Zn alloy of Zn metal among Zn grain later- grains/Zn metal Chemical component content fracture added Zn alloy grains grains/ of Zn metal grains/Zn surfaces Comparative metal (μm) Zn alloy alloy grains or Ave Example grains Fine Coarse grains (Mass %) cracks aspect No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio 72 — 3.99 27.6 34.21 100 0.005 Yes 1.25 73 — 1.02 21.9 7.88 80.5 14.6 4.9 Yes 1.19 74 — 0.05 22.5 92.32 96.4 0.007 3.6 Yes 1.18 75 — 2.01 17.5 11.22 49.1 31.9 9.4 9.6 No 1.24 76 — 1.51 6.99 55.66 56.7 25.6 11.8 5.9 Yes 1.11 77 — 2.38 7.65 78.99 64.4 35.6 Yes 1.27 78 — 2.35 9.25 35.87 57.5 31.6 10.9 Yes 1.31 79 — 2.57 9.56 42.04 32.2 67.8 No 1.26 80 23.5 1.99 11.12 95.66 80.5 14.6 4.9 Yes 1.02 81 5.96 2.38 10.93 34.21 96.4 0.007 3.6 Yes 1.50 82 10.64 2.49 9.34 7.88 49.1 31.9 9.4 9.6 No 1.13 83 16.5 0.006 105 92.32 86.06 12.9 0 1.04 Yes 1.04 84 7.95 4.5 125 11.22 99.34 0.6 0 0.06 Yes 1.02 85 7.95 1.02 21.9 4.65 96.82 3.1 0.04 0.04 Yes 1.08 86 9.64 0.05 22.5 99.80 91.8 4.6 1.8 1.8 No 1.15 87 0.96 2.01 17.5 95.66 82 8.3 9.2 0.5 Yes 1.02 88 5.26 1.51 6.99 34.21 88.2 11.8 0 0 Yes 1.50 89 13.5 2.38 7.65 7.88 86.06 12.9 0 1.04 No 1.13 90 13.5 2.35 9.25 92.32 99.34 0.6 0 0.06 Yes 1.04 91 9.64 2.57 9.56 11.22 96.82 2.4 0.04 0.04 Yes 1.02 92 16.5 2.35 9.25 55.66 99.5 0.5 0 0 Yes 1.08 93 58.2 2.57 9.56 78.99 99.34 0.6 0 0.06 Yes 1.15 Ratio of (Zn metal grains or Zn alloy grains):(Later- added Zn metal grains) Coating details Zn Mg Total metal Later- content metal grains/ added of all grain Comparative Zn Zn metal content Base Coat Corrosion Example alloy metal grains of coat resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 72 — — — 38 Urethane resin 150 Spray P 73 — — — 56 Alkali silicate 18 Spray P 74 — — — 89 Alkyl silicate 657 Brush P 75 — — — 32 Alkyl silicate 24 Spray P 76 — — — 55 Urethane resin 99 Spray P 77 — — — 79 Alkyl silicate 7 Spray P 78 — — — 49 Epoxy resin 100 Spray P 79 — — — 89 Alkyl silicate 27 Brush P 80 1 387 1.867 43 Alkali silicate 15 Spray P 81 1 198.7 0.047 38 Alkyl silicate 14 Spray P 82 1 36 0.500 56 Urethane resin 55 Spray P 83 1 1.5 0.012 89 Alkyl silicate 8 Spray P 84 1 0.008 1.587 32 Urethane resin 122 Brush P 85 1 1.4 2.833 55 Alkyl silicate 555 Spray P 86 1 4.2 2.673 79 Alkali silicate 19 Spray P 87 1 1.6 0.731 10 Alkyl silicate 25 Brush P 88 1 7.5 0.671 16 Alkyl silicate 58 Spray P 89 1 1.6 3.538 9 Alkyl silicate 685 Spray P 90 1 385 0.002 49 Alkali silicate 19 Brush P 91 1 270 0.009 89 Urethane resin 700 Spray P 92 1 195 0.003 89 Alkyl silicate 77 Spray P 93 1 2.9 0.154 79 Alkyl silicate 54 Spray P

TABLE 6 Diameter distribution of Zn metal Percent of fine Chemical grains/Zn alloy grain metal component content Zn alloy Total grains (Ave grain grains among Zn of Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thikness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 1 2.65 9.56 5.66 100 0 0 0 No 35 22 120 G G 2 0.05 6.50 16.55 100 0 0 0 No 66 18 77 G G 3 4.6 65.50 21.55 100 0 0 0 No 38 23 85 G G 4 3.56 13.50 5.66 100 0 0 0 No 84 25 126 G G 5 4.55 16.70 33.66 100 0 0 0 No 39 15 145 G G 6 2.15 9.89 45.65 100 0 0 0 No 85 19 120 G E 7 3.22 10.55 49.88 100 0 0 0 No 36 24 110 G G 8 2.99 9.64 42.33 100 0 0 0 No 56 15 105 G G 9 3.65 11.22 65.44 100 0 0 0 No 42 10 99 G G 10 4.55 13.50 77.55 100 0 0 0 No 31 7 120 G G 11 3.57 22.50 96.55 100 0 0 0 No 88 5.5 85 G G 12 1.99 8.56 5.97 100 0 0 0 No 78 17 102 G E 13 2.12 9.46 87.77 100 0 0 0 No 36 22 99 G G 14 2.45 11.10 86.55 100 0 0 0 No 37 26 134 G G 15 1.85 8.92 15.67 100 0 0 0 No 45 21 156 G G 16 1.65 9.23 31.55 100 0 0 0 No 68 17 121 G E 17 2.45 9.05 26.76 100 0 0 0 No 79 6 109 G E 18 2.01 10.91 67.89 100 0 0 0 No 47 10 89 G G 19 1.99 11.12 56.89 100 0 0 0 No 56 21 94 G G 20 2.38 10.93 45.67 100 0 0 0 No 37 34 103 G G

TABLE 7 Diameter distribution of Percent of fine Chemical Zn metal grains/Zn alloy grain metal component content Zn alloy Total grains (Ave grain grains among Zn of Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thickness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 21 2.49 9.34 34.67 100 0 0 0 No 90 21 111 G E 22 2.34 8.77 95.66 100 0 0 0 No 43 18 90 G G 23 3.99 27.60 34.21 100 0 0 0 No 38 19 109 G G 24 1.02 21.90 7.88 100 0 0 0 No 56 21 89 G G 25 0.05 22.50 92.32 100 0 0 0 No 89 17 99 G G 26 2.01 17.50 11.22 100 0 0 0 No 32 14 89 G G 27 1.51 6.99 55.66 100 0 0 0 No 55 16 134 G G 28 2.38 7.65 78.99 100 0 0 0 No 79 21 120 G E 29 2.35 9.25 35.87 96.0 4.0 0 0 Yes 47 20.3 189 E E 30 2.57 9.56 42.04 97.5 2.5 0 0 Yes 49 24.5 167 G G 31 2.56 9.84 6.55 98.4 1.6 0 0 Yes 52 16 156 G G 32 2.21 9.75 43.60 95.5 4.5 0 0 Yes 51 55 203 E E 33 2.64 9.85 44.12 96.2 3.8 0 0 No 53 45 206 G G 34 1.99 8.56 37.21 98.0 2.0 0 0 Yes 78 65 214 E E 35 2.94 8.21 43.38 94.5 5.5 0 0 Yes 83 38 256 E E 36 2.58 8.33 13.52 94.0 6.0 0 0 No 89 42 215 E E 37 2.37 8.00 44.94 97.5 2.5 0 0 Yes 90 25 245 E E 38 2.15 9.22 45.46 93.2 6.8 0 0 Yes 86 32 167 E E 39 2.96 9.36 35.96 94.5 5.5 0 0 Yes 53 25 158 G G 40 2.85 9.45 42.13 93.6 6.4 0 0 No 48 36 169 G G

TABLE 8 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thickness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 41 2.94 9.61 7.56 94.1 5.9 0 0 Yes 46 19 145 G G 42 2.11 9.85 43.69 93.5 6.5 0 0 Yes 47 28.6 167 E E 43 2.68 9.23 44.21 97.6 2.4 0 0 Yes 49 27 169 G G 44 2.99 9.08 39.51 94.5 5.5 0 0 Yes 83 195 160 E E 45 2.78 9.87 45.68 96.8 3.2 0 0 No 85 23 159 E E 46 2.96 9.46 65.58 95.4 4.6 0 0 No 90 23 157 E E 47 2.85 9.28 47.24 94.8 5.2 0 0 Yes 89 18 146 E E 48 2.64 9.45 47.76 97.5 2.5 0 0 Yes 88 55 148 E E 49 2.35 9.25 45.02 90.0 10.0 0 0 No 47 19 123 E E 50 2.12 9.46 47.02 92.5 7.5 0 0 Yes 47 42 213 E E 51 2.34 9.46 7.66 91.6 8.4 0 0 No 52 19 215 E E 52 2.33 9.46 15.20 90.8 9.2 0 0 No 52 28.6 224 E E 53 2.23 9.06 43.16 88.5 11.5 0 0 Yes 52 27 267 E E 54 2.12 9.30 49.33 87.5 12.5 0 0 Yes 88 195 243 E E 55 2.21 8.68 19.47 92.4 7.6 0 0 Yes 87 23 74 E E 56 1.38 8.53 69.55 91.6 8.4 0 0 Yes 89 23 63 E E 57 1.95 9.32 51.41 91.1 8.9 0 0 Yes 90 28.6 65 E E 58 2.26 8.95 75.88 90.6 9.4 0 0 Yes 91 27 98 E E 59 2.05 12.54 48.08 86.5 13.5 0 0 Yes 46 195 98 G G 60 1.65 8.70 66.85 92.5 7.5 0 0 Yes 47 23 97 E E

TABLE 9 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thickness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 61 2.35 8.55 7.68 91.1 8.9 0 0 Yes 47 23 94 E E 62 1.62 8.91 8.64 90.6 9.4 0 0 Yes 49 18 93 E E 63 1.88 9.91 16.58 89.4 10.6 0 0 Yes 50 55 75 G G 64 2.35 9.25 35.87 96.0 4.0 0 0 Yes 47 16.5 64 E E 65 2.57 9.56 42.04 97.5 2.5 0 0 Yes 48 25.4 62 G G 66 2.56 9.84 38.41 98.4 1.6 0 0 Yes 49 5.8 64 G G 67 2.21 9.75 6.99 95.5 4.5 0 0 Yes 51 42.5 75 E E 68 2.64 9.85 44.12 96.2 3.8 0 0 Yes 52 15.6 73 G G 69 2.65 8.56 66.99 98.0 2.0 0 0 Yes 88 8.4 65 E E 70 2.94 8.21 43.38 94.5 5.5 0 0 Yes 89 17.6 75 E E 71 2.58 8.33 39.75 94.0 6.0 0 0 Yes 87 19.8 73 E E 72 2.37 8.00 65.38 97.5 2.5 0 0 Yes 85 22.5 78 E E 73 2.15 9.22 45.46 93.2 6.8 0 0 Yes 83 24.6 125 E E 74 2.96 9.36 22.55 94.5 5.5 0 0 Yes 46 23.8 167 G G 75 2.85 9.45 42.13 93.6 6.4 0 0 Yes 48 15.2 28 G G 76 2.94 9.61 38.50 94.1 5.9 0 0 Yes 51 10.6 34 G G 77 2.11 9.85 64.13 93.5 6.5 0 0 Yes 51 10.7 256 E E 78 2.68 9.23 44.21 97.6 2.4 0 0 Yes 51 15 24 G G 79 2.99 9.08 39.51 94.5 5.5 0 0 Yes 88 10.5 96 E E 80 1.82 2.87 78.64 96.8 3.2 0 0 No 87 14.5 94 E E

TABLE 10 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thickness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 81 1.42 9.46 42.05 95.4 4.6 0 0 No 85 12.3 93 E E 82 2.12 9.28 64.58 94.8 5.2 0 0 No 82 8.6 95 E E 83 1.92 9.45 47.76 97.5 2.5 0 0 Yes 86 17.5 92 E E 84 2.11 9.63 24.10 96.3 3.7 0 0 Yes 45 12.6 95 E E 85 2.97 9.16 39.11 94.5 5.5 0 0 Yes 48 10.4 91 G G 86 2.36 10.39 19.65 95.5 4.5 0 0 Yes 50 10.9 90 E E 87 3.05 10.56 65.39 97.3 2.7 0 0 Yes 51 19 99 G G 88 2.15 10.74 48.57 95.8 4.2 0 0 Yes 51 25.6 98 E E 89 2.19 10.27 24.91 94.6 5.4 0 0 Yes 79 28.6 97 E E 90 2.48 11.50 39.92 94.7 5.3 0 0 No 81 24.7 94 E E 91 2.85 11.67 22.65 94.8 5.2 0 0 No 80 22.9 93 E E 92 2.75 11.85 66.20 96.1 3.9 0 0 No 82 52.3 83 E E 93 2.46 11.38 49.38 97.5 2.5 0 0 Yes 83 56.3 88 E E 94 2.71 12.61 30.58 94.0 6.0 0 0 Yes 46 33.3 89 G G 95 2.36 12.78 45.59 95.0 5.0 0 0 Yes 48 34.5 87 G G 96 2.16 9.57 28.32 97.2 2.8 0 0 Yes 51 23.5 86 E E 97 2.46 9.81 71.87 99.5 0.5 0 0 Yes 53 26.7 85 E E 98 2.49 8.43 53.05 94.6 5.4 0 0 Yes 54 38.5 89 E E 99 2.95 8.55 27.74 96.5 3.5 0 0 Yes 88 45.2 84 E E 100 2.36 8.22 42.75 96.7 3.3 0 0 Yes 89 36.9 88 E E

TABLE 11 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thickness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 101 2.21 9.44 23.29 96.5 3.5 0 0 No 90 35.8 86 E E 102 2.25 9.58 61.12 95.5 4.5 0 0 Yes 86 34.2 85 E E 103 2.44 9.67 44.30 95.8 4.2 0 0 Yes 85 31.2 83 E E 104 2.78 9.83 23.96 96.4 3.6 0 0 Yes 46 37.5 82 G G 105 2.15 10.07 44.09 95.7 4.3 0 0 Yes 47 12.5 81 E E 106 2.19 9.45 24.63 95.8 4.2 0 0 Yes 47 10.2 89 E E 107 2.48 9.30 62.46 96.8 3.2 0 0 Yes 48 14.5 96 E E 108 2.59 9.99 45.64 97.1 2.9 0 0 Yes 50 16.3 95 G G 109 2.47 9.58 25.30 96.3 3.7 0 0 Yes 86 15.8 99 E E 110 2.69 9.40 42.84 94.2 5.8 0 0 Yes 84 13.5 100 E E 111 2.57 9.57 25.44 95.6 4.4 0 0 Yes 83 12.7 123 E E 112 2.49 9.54 63.27 97.8 2.2 0 0 Yes 82 11.2 89 E E 113 2.68 9.58 46.45 94.5 5.5 0 0 Yes 81 16.5 87 E E 114 2.35 9.25 46.45 90.0 10.0 0 0 Yes 46 10.6 86 E E 115 2.48 10.04 50.91 92.5 7.5 0 0 No 47 10.7 84 E E 116 2.13 11.27 27.25 91.6 8.4 0 0 Yes 48 15 89 E E 117 1.93 11.44 42.26 90.8 9.2 0 0 Yes 51 10.5 100 E E 118 2.05 8.90 33.69 88.5 11.5 0 0 Yes 53 14.5 87 G G 119 1.42 8.75 48.70 87.5 12.5 0 0 Yes 88 12.3 89 E E 120 1.46 9.44 29.24 92.4 7.6 0 0 Yes 85 8.6 85 E E

TABLE 12 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thickness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 121 1.75 9.03 67.07 91.6 8.4 0 0 Yes 83 17.5 83 E E 122 1.86 8.85 50.25 91.1 8.9 0 0 Yes 82 12.6 86 E E 123 1.74 8.95 29.91 90.6 9.4 0 0 Yes 83 10.4 88 E E 124 1.96 12.54 87.50 86.5 13.5 0 0 Yes 47 10.9 80 G G 125 1.65 8.70 30.58 87.4 12.6 0 0 No 51 19 89 G G 126 2.35 8.55 68.41 88.5 11.5 0 0 No 52 25.6 89 G G 127 1.62 10.72 54.59 89.6 10.4 0 0 No 51 28.6 98 G G 128 2.25 9.90 34.25 89.4 10.6 0 0 No 52 24.7 96 G G 129 2.36 9.57 37.61 90.6 9.4 0 0 Yes 89 22.9 94 E E 130 2.24 10.79 45.60 90.3 9.7 0 0 Yes 85 52.3 123 E E 131 2.46 10.93 46.70 90.2 9.8 0 0 Yes 82 56.3 156 E E 132 1.56 11.02 41.22 91.5 8.5 0 0 Yes 87 33.3 234 E E 133 1.24 11.18 45.68 86.5 13.5 0 0 Yes 88 34.5 278 E E 134 1.68 11.42 22.02 85.5 14.5 0 0 Yes 49 23.5 134 G G 135 2.65 10.80 37.03 89.4 10.6 0 0 Yes 50 26.7 88 G G 136 2.22 10.65 28.46 90.6 9.4 0 0 Yes 51 38.5 98 E E 137 2.45 11.34 43.47 90.8 9.2 0 0 Yes 52 25.4 97 E E 138 2.23 11.62 35.19 91.6 8.4 0 0 Yes 53 5.8 94 G G 139 2.26 11.15 73.02 92.4 7.6 0 0 Yes 88 42.5 93 E E 140 2.72 12.38 56.20 88.8 11.2 0 0 Yes 85 15.6 75 E E

TABLE 13 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among Zn metal grains/Zn grain metal grain Coat Invention diameter) metal grains/ alloy grains fracture content of thickness Time to red Example (μm) Zn alloy grains (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 141 2.13 12.55 35.86 85.1 14.9 0 0 Yes 83 8.4 64 E E 142 1.98 9.34 93.45 92.5 7.5 0 0 Yes 81 17.6 62 E E 143 2.02 9.58 30.66 90.5 9.5 0 0 Yes 80 19.8 64 E E 144 2.21 9.88 74.21 91.4 8.6 0 0 Yes 47 22.5 75 E E 145 2.55 10.00 55.39 92.1 7.9 0 0 Yes 49 24.6 73 G G 146 1.92 10.67 30.08 86.3 13.7 0 0 Yes 50 23.8 65 G G 147 1.96 11.89 45.09 90.2 9.8 0 0 Yes 51 15.2 97 G G 148 2.11 12.03 41.41 89.5 10.5 0 0 No 52 10.6 85 G G 149 2.97 12.12 17.75 83.6 16.4 0 0 Yes 83 10.7 65 E E 150 2.36 12.28 32.76 92.4 7.6 0 0 No 88 15 78 E E 151 3.05 12.52 30.89 86.5 13.5 0 0 Yes 85 10.5 67 E E 152 2.57 11.90 45.90 86.2 13.8 0 0 No 83 14.5 78 E E 153 2.65 11.75 42.22 89.6 10.4 0 0 Yes 82 12.3 79 E E 154 2.54 12.44 18.56 89.4 10.6 0 0 No 47 8.6 78 G G 155 2.85 12.03 33.57 90.5 9.5 0 0 Yes 46 17.5 67 G G 156 2.75 10.61 31.70 87.2 12.8 0 0 Yes 49 28.6 67 G G 157 2.46 11.30 46.71 92.4 7.6 0 0 Yes 50 24.7 56 E E 158 2.71 11.58 47.89 91.5 8.5 0 0 Yes 51 22.9 85 V V 159 2.36 11.11 24.23 91 9 0 0 Yes 83 52.3 89 E E 160 2.16 12.34 39.24 88.8 11.2 0 0 Yes 82 56.3 89 E E

TABLE 14 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn metal Zn alloy Total alloy grains (Ave grain grains among grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 161 2.46 12.51 37.37 86.2 13.8 0 0 Yes 88 33.3 98 E E 162 2.49 11.64 50.38 92.4 7.6 0 0 Yes 85 34.5 96 E E 163 1.63 9.16 37.14 90.6 9.4 0 0 Yes 86 23.5 94 E E 164 1.51 9.46 13.48 91.4 8.6 0 0 Yes 47 26.7 123 E E 165 3.05 9.54 40.05 87.5 12.5 0 0 No 48 38.5 156 G G 166 2.57 9.56 38.18 88.5 11.5 0 0 No 50 25.4 234 G G 167 2.65 9.46 7.63 90.6 9.4 0 0 Yes 51 5.8 278 G G 168 2.54 11.99 37.95 91.4 8.6 0 0 Yes 52 42.5 134 G G 169 2.85 12.08 14.29 91.5 8.5 0 0 Yes 88 15.6 88 E E 170 2.75 12.24 40.86 89.6 10.4 0 0 No 89 42.5 98 E E 171 2.46 12.48 97.50 89.3 10.7 0 0 No 86 15.6 97 E E 172 2.71 11.86 13.30 92.1 7.9 0 0 Yes 87 8.4 94 E E 173 2.36 11.71 43.62 87.5 12.5 0 0 No 86 17.6 93 E E 174 2.46 11.35 56.93 91.9 7.5 0.6 0 Yes 46 22.5 75 E E 175 1.45 12.02 36.59 90.45 9.5 0.05 0 Yes 49 24.6 64 G G 176 2.42 13.24 39.95 91.38 8.6 0.02 0 Yes 35 23.8 62 G G 177 2.11 9.46 86.50 91.1 7.9 1 0 Yes 37 15.2 64 E E 178 2.97 13.47 32.87 81.1 13.7 5.2 0 No 36 10.6 134 G G 179 2.36 9.46 16.23 85.6 9.8 4.6 0 Yes 38 107 167 E E 180 3.05 13.87 37.40 89.5 10.5 0 0.001 Yes 48 15 38 G G

TABLE 15 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn metal Zn alloy Total alloy grains (Ave grain grains among grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 181 2.57 13.25 40.76 83 16.4 0 0.6 No 46 10.5 268 G G 182 2.65 13.10 87.31 95.3 3.9 0 0.8 Yes 52 14.5 256 G G 183 2.12 9.08 92.50 95 2.5 0 2.5 Yes 51 12.3 234 E E 184 1.65 9.87 17.93 92.5 6 0 1.5 No 50 8.6 243 E E 185 2.35 9.46 44.50 94.1 5 0 0.9 Yes 30 17.5 132 E E 186 1.63 9.28 96.50 96.7 2.8 0 0.5 Yes 38 12.6 124 E E 187 2.64 9.45 16.94 98.5 0.5 0.3 0.7 Yes 39 10.4 87 G G 188 2.35 9.25 88.12 94.58 5.4 0.02 0.005 Yes 83 10.9 95 E E 189 2.31 9.46 60.57 95.65 3.5 0.05 0.8 Yes 79 15 97 E E 190 2.62 9.46 39.48 89 3.3 5.2 2.5 Yes 75 10.5 94 E E 191 2.52 9.46 15.82 94.98 3.5 0.02 1.5 Yes 76 14.5 93 E E 192 2.24 13.32 49.57 89.5 5 4.6 0.9 Yes 72 12.3 88 E E 193 0.05 6.54 86.52 97.5 2.5 0 0.07 Yes 49 32 83 G G 194 2.42 6.35 90.98 93.5 6.5 0 0.11 Yes 51 25 88 E E 195 0.11 7.54 67.32 88.5 11.5 0 0.42 Yes 46 36 89 G G 196 1.92 8.64 82.33 97.6 2.4 0 0.65 No 49 19 87 E E 197 0.46 6.45 73.76 95.5 4.5 0 0.35 Yes 35 28.6 86 G G 198 0.77 6.48 88.77 97.3 2.7 0 2.7 Yes 37 27 85 G G 199 1.55 10.54 80.49 96.5 3.5 0 0.6 Yes 36 195 89 E E 200 1.23 12.54 88.60 93.2 6.8 0 1.8 Yes 38 23 84 G G

TABLE 16 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn metal Zn alloy Total alloy grains (Ave grain grains among grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 201 1.45 18.67 53.20 87.6 12.4 0 1.34 No 48 23 88 G G 202 1.64 19.45 98.71 98.5 1.5 0 0.75 Yes 46 18 86 G G 203 0.54 21.55 97.23 87.5 12.5 0 0.43 Yes 52 55 85 G G 204 1.85 7.54 70.16 95.4 4.6 5.8 0 No 51 19 83 E E 205 1.42 35.48 82.73 95.2 4.8 2.7 0 No 50 42 82 G G 206 0.06 65.22 68.54 92.5 7.5 0.6 0 Yes 30 19 81 G G 207 1.34 35.47 75.38 98.4 1.6 0.5 0 Yes 38 28.6 89 G G 208 1.58 15.24 90.39 97.1 2.9 0.2 0 Yes 39 27 89 G G 209 1.47 13.67 86.71 96.5 3.5 0.01 0 Yes 83 195 85 E E 210 1.64 6.45 63.05 97.4 2.6 0.06 0 Yes 79 23 83 E E 211 1.86 7.54 78.06 94.6 5.4 0.07 0 Yes 75 23 86 E E 212 0.25 14.32 98.71 93.6 6.4 0.05 0 Yes 76 25.4 88 E E 213 0.46 45.22 97.23 92.2 7.8 0.02 0 No 72 5.8 80 E E 214 0.77 48.57 70.16 94.4 5.6 0.65 0 Yes 71 42.5 89 E E 215 1.55 99.52 82.73 96.5 3.5 0.78 0 Yes 88 15.6 89 E E 216 1.23 13.64 98.71 97.3 2.7 0.99 0 Yes 82 8.4 98 E E 217 1.45 18.54 97.23 94.5 5.5 1.76 0 No 83 17.6 96 E E 218 1.64 7.54 70.16 90.6 9.4 7.8 0 Yes 81 19.8 94 E E 219 0.54 14.52 82.73 87.4 12.6 9.88 0 Yes 64 22.5 123 G G 220 1.85 13.75 86.54 88.4 11.6 4.65 0 Yes 69 24.6 156 G G

TABLE 17 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn metal Zn alloy Total alloy grains (Ave grain grains among grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 221 1.42 16.54 75.20 89.5 10.5 3.65 0 Yes 83 23.8 234 E E 222 2.3 9.80 82.73 95.2 4.8 8.99 0 Yes 50 15.2 95 E E 223 1.8 11.20 97.23 96.4 3.6 0 0.07 Yes 72 10.6 99 E E 224 1.92 7.99 38.92 95.3 4.5 0.2 0 Yes 51 32 94 E E 225 1.96 10.89 45.09 94.2 5.2 0.6 0 Yes 50 25 92 E E 226 2.25 11.03 41.46 91.45 8.5 0.05 0 Yes 30 36 87 E E 227 2.36 6.35 46.12 97.58 2.4 0.02 0 No 38 19 84 E E 228 2.24 7.54 46.64 95.9 3.1 1 0 Yes 39 28.6 100 E E 229 2.11 8.64 29.13 88.3 6.5 5.2 0 Yes 83 27 99 E E 230 2.97 11.90 41.70 90.5 4.9 4.6 0 Yes 79 195 86 G E 231 2.36 11.75 42.22 91.5 8.5 0 0.001 Yes 75 23 97 G E 232 3.05 12.44 46.93 86.85 12.5 0.05 0.6 Yes 76 23 32 G E 233 2.57 12.03 47.45 83.6 14.6 1 0.8 Yes 72 28.6 55 G E 234 1.88 9.91 12.60 91 6.5 0 2.5 Yes 71 27 57 E E 235 1.86 7.54 42.51 92.8 5.7 0 1.5 No 82 195 39 E E 236 1.57 8.64 43.03 95.7 3.4 0 0.9 Yes 83 23 67 E E 237 2.75 10.71 47.74 92.6 6.9 0 0.5 Yes 81 23 78 E E 238 0.54 21.55 97.23 93.4 5.6 0.3 0.7 Yes 64 25.4 79 G E 239 1.85 26.87 70.16 96.38 3.6 0.02 0.005 Yes 69 5.8 82 G E 240 1.42 35.48 82.73 92.12 7.8 0.04 0.04 Yes 83 42.5 81 E E

TABLE 18 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among metal grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 241 0.06 65.22 94.81 80.3 16.5 1 2.2 Yes 50 15.6 89 G E 242 1.34 35.47 96.54 79.94 18.4 0.06 1.6 Yes 72 19 96 G E 243 0.25 14.32 98.71 91.85 2.5 5.6 0.05 Yes 76 42 95 G E 244 0.46 45.22 97.23 91.4 4.3 4.2 0.1 Yes 72 23 99 G E 245 0.77 48.57 70.16 89.8 3.5 6.4 0.3 Yes 46 28.6 100 G E 246 1.55 99.52 82.73 84.9 2.6 9.6 2.9 Yes 52 5.8 123 G E 247 1.23 13.64 98.71 88.4 1.5 8.5 1.6 Yes 83 15.2 89 E E 248 2.94 9.61 7.56 94.1 5.9 0.65 0.07 Yes 46 19 145 G G 249 2.11 9.85 95.98 93.5 6.5 0.07 0 Yes 47 28.6 167 E E 250 2.68 9.23 68.91 97.6 2.4 0.08 2.5 Yes 49 27 169 G G 251 2.74 9.46 46.67 92.5 7.5 1.2 2.9 Yes 47 42 213 G G 252 2.13 9.46 7.66 91.6 8.4 1.8 1.8 Yes 52 19 215 E E 253 2.82 9.46 15.20 90.8 9.2 9.2 0.5 Yes 52 28.6 224 G G 254 1.88 9.91 16.58 89.4 10.6 8.9 0.8 Yes 50 55 75 G G 255 2.35 9.25 35.87 96.0 4.0 0 0.7 Yes 47 16.5 64 E E 256 2.57 9.56 42.04 97.5 2.5 0.02 0 Yes 48 25.4 62 G G 257 2.56 9.84 38.41 98.4 1.6 7.8 0 Yes 49 5.8 64 G G 258 2.21 9.75 6.99 95.5 4.5 0 0.5 Yes 51 42.5 75 E E 259 2.64 9.85 44.12 96.2 3.8 0.08 0 Yes 52 15.6 73 G G 260 2.68 9.23 44.21 97.6 2.4 2.7 0 No 51 15 24 G G

TABLE 19 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among metal grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 261 1.55 9.08 39.51 94.5 5.5 3.7 0 Yes 88 10.5 96 E E 262 1.88 9.87 78.64 96.8 3.2 1.8 0 No 87 14.5 94 E E 263 1.55 9.46 42.05 95.4 4.6 1.5 0 Yes 85 12.3 93 E E 264 2.85 9.28 64.58 94.8 5.2 0 2.9 Yes 82 8.6 95 E E 265 2.64 9.45 47.76 97.5 2.5 0 2.7 Yes 86 17.5 92 E E 266 2.36 10.39 19.65 95.5 4.5 0 0.05 Yes 50 10.9 90 E E 267 3.05 10.56 65.39 97.3 2.7 0 0.02 Yes 51 19 99 G G 268 2.57 10.74 48.57 95.8 4.2 0 0.08 Yes 51 25.6 98 G G 269 2.65 10.27 24.91 94.6 5.4 0 1.02 No 79 28.6 97 G E 270 2.54 11.50 39.92 94.7 5.3 0 1.05 No 81 24.7 94 G E 271 2.85 11.67 22.65 94.8 5.2 0 0.04 Yes 80 22.9 93 G E 272 2.75 11.85 66.20 96.1 3.9 3.6 0.03 Yes 82 52.3 83 G E 273 2.69 9.40 42.84 94.2 5.8 0.08 0.06 Yes 84 13.5 100 G E 274 2.57 9.57 25.44 95.6 4.4 0.6 0.02 Yes 83 12.7 123 G E 275 2.49 9.54 63.27 97.8 2.2 0.2 0.07 Yes 82 11.2 89 E E 276 2.68 9.58 46.45 94.5 5.5 0 1.11 Yes 81 16.5 87 G E 277 2.35 9.25 46.45 90.0 10.0 0 1.04 Yes 46 10.6 86 G G 278 2.48 10.04 50.91 92.5 7.5 0 0.06 Yes 47 10.7 84 E E 279 1.74 8.95 29.91 90.6 9.4 0 0.99 No 83 10.4 88 E E 280 2.25 9.90 34.25 89.4 10.6 0 0.45 Yes 52 24.7 96 E E

TABLE 20 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among metal grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 281 2.36 9.57 37.61 90.6 9.4 0.7 0 Yes 89 22.9 94 E E 282 2.24 10.79 45.60 90.3 9.7 0.5 0 Yes 85 52.3 123 E E 283 2.23 11.62 35.19 91.6 8.4 0.2 0 Yes 53 5.8 94 G G 284 2.26 11.15 73.02 92.4 7.6 0.07 0 Yes 88 42.5 93 E E 285 2.72 12.38 56.20 88.8 11.2 0.06 0 Yes 85 15.6 75 G E 286 2.11 12.03 41.41 89.5 10.5 0.13 0 No 52 10.6 85 G G 287 2.97 12.12 17.75 83.6 16.4 0.65 0 Yes 83 10.7 65 G E 288 2.36 12.28 32.76 92.4 7.6 0.27 0 Yes 88 15 78 G E 289 2.75 10.61 31.70 87.2 12.8 0.45 0.65 Yes 49 28.6 67 G G 290 2.46 11.30 46.71 92.4 7.6 0.33 0.99 Yes 50 24.7 56 G G 291 2.71 11.58 47.89 91.5 8.5 1 2.5 Yes 51 22.9 85 G G 292 2.36 11.11 24.23 91 9 0.87 1.8 Yes 83 52.3 89 G E 293 2.16 12.34 39.24 88.8 11.2 0.07 0 Yes 82 56.3 89 G E 294 2.46 12.51 37.37 86.2 13.8 0.27 0 Yes 88 33.3 98 G E 295 2.49 11.64 50.38 92.4 7.6 0.86 0 No 85 34.5 96 G E 296 2.71 11.86 13.30 92.1 7.9 0.65 0 Yes 87 8.4 94 G E 297 2.36 11.71 43.62 87.5 12.5 0.43 0 No 86 17.6 93 G E 298 1.96 10.89 56.93 91.9 7.5 0.6 0 Yes 46 22.5 75 E E 299 2.25 11.03 36.59 90.45 9.5 0.05 0 Yes 49 24.6 64 E E 300 2.42 13.24 39.95 91.38 8.6 0.02 0 Yes 35 23.8 62 G G

TABLE 21 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among metal grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 301 2.96 9.46 44.50 94.1 5 0 0.9 No 30 17.5 132 G G 302 2.85 9.28 96.50 96.7 2.8 0 0.5 Yes 38 12.6 124 G G 303 2.64 9.45 16.94 98.5 0.5 0.3 0.7 Yes 39 10.4 87 G G 304 2.35 9.25 88.12 94.58 5.4 0.02 0.005 Yes 83 10.9 95 E E 305 2.31 9.46 60.57 95.65 3.5 0.05 0.8 Yes 79 15 97 E E 306 2.62 9.46 39.48 89 3.3 5.2 2.5 Yes 75 10.5 94 G E 307 2.52 9.46 15.82 94.98 3.5 0.02 1.5 Yes 76 14.5 93 G E 308 2.24 13.32 49.57 89.5 5 4.6 0.9 Yes 72 12.3 88 G E 309 0.06 65.22 68.54 92.5 7.5 0.06 0.07 Yes 30 19 81 G G 310 1.34 35.47 75.38 98.4 1.6 0.99 0.01 Yes 38 28.6 89 G G 311 1.58 15.24 90.39 97.1 2.9 0.54 0.03 Yes 39 27 89 G G 312 1.47 9.28 86.71 96.5 3.5 0.02 0.07 Yes 83 195 85 E E 313 1.64 9.28 63.05 97.4 2.6 0.07 0.8 Yes 79 23 83 E E 314 1.86 16.54 78.06 94.6 5.4 0.09 0.03 Yes 75 23 86 G E 315 0.25 14.32 98.71 93.6 6.4 1.05 0.99 Yes 76 25.4 88 G E 316 0.46 45.22 97.23 92.2 7.8 2.6 0.54 Yes 72 5.8 80 G E 317 0.77 48.57 70.16 94.4 5.6 5.8 0.22 Yes 71 42.5 89 G E 318 1.55 99.52 82.73 96.5 3.5 6.8 0.91 Yes 88 15.6 89 G E 319 1.96 10.89 45.09 94.2 5.2 0.6 0.43 Yes 50 25 92 E E 320 2.25 11.03 41.46 91.45 8.5 0.05 0.32 Yes 30 36 87 E E

TABLE 22 Diameter distribution of Percent of fine Chemical component Zn metal grains/Zn grain metal content of Zn Zn alloy Total alloy grains (Ave grain grains among metal grains/Zn grain metal grain Coat Invention diameter) Zn metal alloy grains fracture content of thickness Time to red Example (μm) grains/Zn alloy (Mass %) surfaces coat (μm) rusting No Fine metal Coarse metal grains (Vol %) Zn Mg Al Si present? (Mass %) Inorganic Organic Inorganic Organic 321 2.36 12.12 46.12 97.58 2.4 0.02 0 Yes 38 19 84 G G 322 2.24 9.46 46.64 95.9 3.1 1 0 Yes 39 28.6 100 E E 323 2.11 12.52 29.13 88.3 6.5 5.2 0 No 83 27 99 G E 324 2.97 11.90 41.70 90.5 4.9 4.6 0 Yes 79 195 86 G E 325 2.36 9.46 42.22 91.5 8.5 0 0.001 Yes 75 23 97 E E 326 3.05 12.44 46.93 86.9 12.5 0 0.6 No 76 23 32 G E 327 2.57 12.03 47.45 84.6 14.6 0 0.8 Yes 72 28.6 55 G E 328 1.85 26.87 70.16 96.38 3.6 0.02 0.005 Yes 69 5.8 82 G G 329 1.42 35.48 82.73 92.12 7.8 0.04 0.04 Yes 83 42.5 81 G E 330 0.06 65.22 94.81 80.3 16.5 1 2.2 Yes 50 15.6 89 G G 331 1.34 35.47 96.54 79.94 18.4 0.06 1.6 Yes 72 19 96 G E 332 0.25 14.32 98.71 91.85 2.5 5.6 0.05 Yes 76 42 95 G E 333 0.46 45.22 97.23 91.4 4.3 4.2 0.1 Yes 72 23 99 G E 334 0.77 48.57 70.16 89.8 3.5 6.4 0.3 Yes 46 28.6 100 G G

TABLE 23 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 413 2.65 9.56 5.66 100 0 0 0 No — 35 Alkali silicate 2 Spray G 414 0.05 6.5 16.55 100 0 0 0 No — 66 Alkyl silicate 37 Spray E 415 4.6 65.5 21.55 100 0 0 0 No — 38 Alkali silicate 12 Spray E 416 3.56 13.5 5.66 100 0 0 0 No — 84 Alkyl silicate 160 Brush E 417 4.55 16.7 33.66 100 0 0 0 No — 39 Alkali silicate 5 Brush G 418 2.15 9.89 45.65 100 0 0 0 No — 85 Alkyl silicate 12 Brush E 419 3.22 10.55 49.88 100 0 0 0 No — 36 Alkali silicate 2 Spray G 420 2.99 9.64 42.33 100 0 0 0 No — 56 Alkyl silicate 18 Spray E 421 3.65 11.22 65.44 100 0 0 0 No — 42 Alkyl silicate 23 Spray E 422 4.55 13.5 77.55 100 0 0 0 No — 31 Epoxy resin 30 Brush E 423 3.57 22.5 96.55 100 0 0 0 No — 88 Acrylic resin 77 Brush E 424 1.99 8.56 5.97 100 0 0 0 No — 78 Urethane resin 254 Brush E 425 2.12 9.46 87.77 100 0 0 0 No — 36 Polyester resin 47 Spray E 426 2.45 11.1 86.55 100 0 0 0 No — 37 Epoxy resin 43 Spray E 427 1.85 8.92 15.67 100 0 0 0 No — 45 Acrylic resin 322 Brush E 428 1.65 9.23 31.55 100 0 0 0 No — 68 Urethane resin 20 Brush E 429 2.45 9.05 26.76 100 0 0 0 No — 79 Polyester resin 700 Brush E 430 2.01 10.91 67.89 100 0 0 0 No — 47 Alkali silicate 22 Spray E 431 1.99 11.12 56.89 100 0 0 0 No — 56 Alkyl silicate 25 Spray E 432 2.38 10.93 45.67 100 0 0 0 No — 37 Alkali silicate 14 Spray E 433 2.49 9.34 34.67 100 0 0 0 No — 90 Urethane resin 112 Spray E 434 2.34 8.77 95.66 100 0 0 0 No — 43 Alkali silicate 554 Spray E

TABLE 24 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 435 3.99 27.6 34.21 100 0 0 0 No — 38 Urethane resin 150 Spray E 436 1.02 21.9 7.88 100 0 0 0 No — 56 Alkali silicate 18 Spray E 437 0.05 22.5 92.32 100 0 0 0 No — 89 Alkyl silicate 657 Brush E 438 2.01 17.5 11.22 100 0 0 0 No — 32 Alkyl silicate 24 Spray E 439 1.51 6.99 55.66 100 0 0 0 No — 55 Urethane resin 99 Spray E 440 2.38 7.65 78.99 100 0 0 0 No — 79 Alkyl silicate 7 Spray E 441 1.99 8.56 5.97 100 0 0 0 No — 78 Epoxy resin 100 Spray E 442 2.49 9.34 34.67 100 0 0 0 No — 77 Alkyl silicate 27 Brush E 443 1.02 21.9 7.88 100 0 0 0 No — 56 Alkali silicate 15 Spray E 444 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 49 Alkyl silicate 14 Spray E 445 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 89 Urethane resin 55 Spray E 446 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 90 Alkyl silicate 8 Spray E 447 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 86 Urethane resin 122 Brush E 448 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 48 Alkyl silicate 555 Spray E 449 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 47 Alkali silicate 19 Spray E 450 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 47 Alkyl silicate 25 Brush E 451 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 47 Alkyl silicate 58 Spray E 452 2.37 8 44.94 94.3 5.7 0 0 No 1.07 52 Alkyl silicate 685 Spray E 453 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 52 Alkali silicate 19 Brush E 454 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 52 Urethane resin 700 Spray E 455 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 88 Alkyl silicate 77 Spray E 456 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 87 Alkyl silicate 54 Spray E

TABLE 25 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 457 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 89 Alkyl silicate 64 Spay E 458 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 90 Alkyl silicate 34 Brush E 459 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 91 Alkali silicate 28 Spay E 460 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 46 Urethane resin 109 Brush E 461 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 47 Alkyl silicate 15 Spay E 462 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 47 Alkyl silicate 14 Spay E 463 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 49 Alkyl silicate 18 Spay E 464 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 50 Alkali silicate 2 Spay G 465 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 87 Alkyl silicate 37 Spay E 466 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 83 Alkali silicate 12 Spay E 467 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 48 Alkyl silicate 160 Brush E 468 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 51 Alkali silicate 5 Brush E 469 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 51 Alkyl silicate 56 Brush E 470 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 87 Alkali silicate 2 Spay E 471 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 85 Alkyl silicate 18 Spay E 472 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 86 Alkyl silicate 23 Spay E 473 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 50 Epoxy resin 30 Brush E 474 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 51 Acrylic resin 77 Brush E 475 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 51 Urethane resin 655 Brush E 476 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 80 Polyester resin 47 Spay E 477 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 46 Epoxy resin 43 Spay E 478 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 51 Acrylic resin 52 Brush E

TABLE 26 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 479 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 86 Urethane resin 20 Brush E 480 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 85 Polyester resin 200 Brush E 481 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 82 Alkali silicate 22 Spray E 482 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 81 Alkyl silicate 25 Spray E 483 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 46 Alkali silicate 14 Spray E 484 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 47 Urethane resin 112 Spray E 485 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 48 Alkali silicate 24 Spray E 486 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 51 Urethane resin 150 Spray E 487 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 53 Alkali silicate 18 Spray E 488 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 88 Alkyl silicate 19 Brush E 489 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 85 Alkyl silicate 24 Spray E 490 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 83 Urethane resin 99 Spray E 491 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 82 Alkyl silicate 7 Spray E 492 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 83 Epoxy resin 100 Spray E 493 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 47 Alkyl silicate 27 Brush E 494 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 51 Alkali silicate 15 Spray E 495 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 52 Alkyl silicate 14 Spray E 496 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 51 Urethane resin 55 Spray E 497 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 52 Alkyl silicate 8 Spray E 498 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 89 Urethane resin 122 Brush E 499 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 85 Alkyl silicate 54 Spray E 500 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 82 Alkali silicate 19 Spray E

TABLE 27 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 501 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 87 Alkyl silicate 25 Brush E 502 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 88 Alkyl silicate 58 Spray E 503 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 49 Alkyl silicate 21 Spray E 504 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 50 Alkali silicate 19 Brush E 505 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 51 Urethane resin 56 Spray E 506 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 52 Alkyl silicate 77 Spray E 507 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 53 Alkyl silicate 12 Spray E 508 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 88 Alkyl silicate 64 Spray E 509 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 85 Alkyl silicate 34 Brush E 510 2.36 12.78 45.59 80 20 0 0 Yes 1.05 83 Alkali silicate 28 Spray E 511 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 81 Urethane resin 109 Brush E 512 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 80 Alkyl silicate 15 Spray E 513 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 47 Alkyl silicate 14 Spray E 514 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 49 Alkyl silicate 18 Spray E 515 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 50 Urethane resin 122 Brush E 516 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 51 Alkyl silicate 54 Spray E 517 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 52 Alkali silicate 19 Spray E 518 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 83 Alkyl silicate 25 Brush E 519 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 88 Alkyl silicate 58 Spray E 520 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 85 Alkyl silicate 21 Spray E 521 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 83 Alkali silicate 19 Brush E 522 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 82 Urethane resin 56 Spray E

TABLE 28 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 523 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 47 Alkyl silicate 77 Spray E 524 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 46 Alkyl silicate 54 Spray E 525 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 49 Alkali silicate 2 Spray G 526 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 50 Alkali silicate 20 Spray E 527 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 51 Alkali silicate 5 Spray G 528 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 83 Alkyl silicate 20 Spray E 529 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 82 Alkali silicate 15 Brush E 530 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 88 Alkyl silicate 57 Brush E 531 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 85 Alkali silicate 13 Brush E 532 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 86 Alkyl silicate 22 Brush E 533 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 47 Alkali silicate 20 Spray E 534 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 48 Alkyl silicate 27 Spray E 535 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 50 Alkali silicate 15 Spray E 536 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 51 Alkyl silicate 35 Spray E 537 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 52 Alkali silicate 34 Brush E 538 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 88 Alkyl silicate 45 Brush E 539 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 89 Alkali silicate 52 Brush E 540 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 86 Alkyl silicate 23 Brush E 541 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 87 Alkali silicate 5 Spray E 542 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 86 Alkyl silicate 52 Brush E 543 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 46 Alkali silicate 150 Brush E 544 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 49 Alkyl silicate 60 Brush E

TABLE 29 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 545 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 35 Alkali silicate 15 Spray E 546 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 37 Alkyl silicate 24 Spray E 547 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 36 Alkali silicate 34 Spray E 548 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 38 Alkyl silicate 20 Brush E 549 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 48 Alkali silicate 200 Brush E 550 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 46 Alkyl silicate 56 Brush E 551 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 51 Alkali silicate 34 Spray E 552 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 46 Alkyl silicate 2 Spray G 553 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 38 Alkali silicate 15 Spray E 554 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 48 Alkali silicate 10 Spray E 555 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 52 Alkyl silicate 125 Brush E 556 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 30 Alkali silicate 24 Brush E 557 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 76 Alkyl silicate 110 Brush E 558 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 72 Alkali silicate 24 Brush E 559 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 81 Alkyl silicate 2 Spray G 560 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 64 Alkali silicate 37 Spray E 561 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 69 Alkyl silicate 113 Brush E 562 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 83 Alkali silicate 2 Spray G 563 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 30 Alkyl silicate 75 Brush E 564 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 83 Alkali silicate 30 Brush E 565 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 75 Alkyl silicate 34 Brush E 566 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 76 Epoxy resin 124 Brush E

TABLE 30 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 567 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 72 Acrylic resin 15 Spray E 568 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 71 Urethane resin 23 Spray E 569 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 82 Polyester resin 157 Brush E 570 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 81 Epoxy resin 26 Spray E 571 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 83 Acrylic resin 38 Spray E 572 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 50 Urethane resin 160 Brush E 573 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 72 Polyester resin 27 Brush E 574 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 47 Epoxy resin 180 Brush E 575 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 47 Acrylic resin 26 Spray E 576 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 52 Urethane resin 180 Brush E 577 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 52 Polyester resin 15 Spray E 578 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 50 Epoxy resin 2 Spray G 579 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 46 Acrylic resin 28 Spray E 580 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 47 Urethane resin 30 Spray E 581 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 83 Polyester resin 2 Spray G 582 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 52 Epoxy resin 157 Brush E 583 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 89 Acrylic resin 28 Brush E 584 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 85 Alkyl silicate 130 Brush E 585 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 53 Alkyl silicate 29 Brush E 586 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 88 Epoxy resin 30 Brush E 587 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 85 Acrylic resin 120 Brush E 588 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 82 Urethane resin 187 Brush E

TABLE 31 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 589 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 83 Polyester resin 28 Spray E 590 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 88 Epoxy resin 5 Spray E 591 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 49 Acrylic resin 35 Spray E 592 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 50 Urethane resin 5 Spray G 593 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 51 Polyester resin 200 Brush E 594 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 83 Alkali silicate 25 Spray E 595 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 82 Alkali silicate 15 Spray E 596 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 88 Alkyl silicate 20 Spray E 597 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 85 Alkali silicate 18 Spray E 598 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 87 Alkyl silicate 22 Spray E 599 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 86 Alkali silicate 19 Spray E 600 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 46 Alkyl silicate 29 Spray E 601 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 49 Alkali silicate 23 Spray E 602 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 35 Alkyl silicate 21 Spray E 603 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 30 Alkali silicate 19 Spray E 604 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 76 Alkyl silicate 15 Spray E 605 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 72 Alkali silicate 18 Spray E 606 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 30 Alkyl silicate 22 Spray E 607 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 83 Alkyl silicate 21 Spray E 608 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 75 Alkyl silicate 29 Spray E 609 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 76 Alkali silicate 23 Spray E 610 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 72 Alkyl silicate 21 Spray E

TABLE 32 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (peak metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 611 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 83 Alkali silicate 19 Spray E 612 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 50 Alkyl silicate 21 Spray E 613 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 72 Alkali silicate 19 Spray E 614 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 50 Acrylic resin 654 Spray E 615 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 48 Alkali silicate 700 Spray E 616 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 75 Alkyl silicate 555 Spray E 617 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 55 Alkyl silicate 321 Spray E 618 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 38 Alkyl silicate 152 Brush E 619 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 48 Urethane resin 674 Spray E 620 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 76 Polyester resin 325 Spray E 621 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 72 Alkyl silicate 665 Spray E 622 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 75 Alkyl silicate 354 Brush E 623 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 76 Alkyl silicate 165 Spray E 624 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 72 Urethane resin 354 Spray E

TABLE 33 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (Ave metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 625 2.65 9.56 5.66 100 0 0 0 N — 35 Alkali silicate 2 Spray G 626 0.05 6.5 16.55 100 0 0 0 N — 66 Alkyl silicate 37 Spray E 627 4.6 65.5 21.55 100 0 0 0 N — 38 Alkali silicate 12 Spray E 628 3.56 13.5 5.66 100 0 0 0 N — 84 Alkyl silicate 160 Brush E 629 4.55 16.7 33.66 100 0 0 0 N — 39 Alkali silicate 5 Brush G 630 2.15 9.89 45.65 100 0 0 0 N — 85 Alkyl silicate 12 Brush E 631 3.22 10.55 49.88 100 0 0 0 N — 36 Alkali silicate 2 Spray G 632 2.99 9.64 42.33 100 0 0 0 N — 56 Alkyl silicate 18 Spray E 633 3.65 11.22 65.44 100 0 0 0 N — 42 Alkyl silicate 23 Spray E 634 4.55 13.5 77.55 100 0 0 0 N — 31 Epoxy resin 30 Brush E 635 3.57 22.5 96.55 100 0 0 0 N — 88 Acrylic resin 77 Brush E 636 1.99 8.56 5.97 100 0 0 0 N — 78 Urethane resin 254 Brush E 637 2.12 9.46 87.77 100 0 0 0 N — 36 Polyester resin 47 Spray E 638 2.45 11.1 86.55 100 0 0 0 N — 37 Epoxy resin 43 Spray E 639 1.85 8.92 15.67 100 0 0 0 N — 45 Acrylic resin 322 Brush E 640 1.65 9.23 31.55 100 0 0 0 N — 68 Urethane resin 20 Brush E 641 2.45 9.05 26.76 100 0 0 0 N — 79 Polyester resin 700 Brush E 642 2.01 10.91 67.89 100 0 0 0 N — 47 Alkali silicate 22 Spray E 643 1.99 11.12 56.89 100 0 0 0 N — 56 Alkyl silicate 25 Spray E 644 2.38 10.93 45.67 100 0 0 0 N — 37 Alkali silicate 14 Spray E

TABLE 34 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (Ave metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 645 2.49 9.34 34.67 100 0 0 0 No — 90 Urethane resin 112 Spray E 646 2.34 8.77 95.66 100 0 0 0 No — 43 Alkali silicate 554 Spray E 647 3.99 27.60 34.21 100 0 0 0 No — 38 Urethane resin 150 Spray E 648 1.02 21.90 7.88 100 0 0 0 No — 56 Alkali silicate 18 Spray E 649 0.05 22.50 92.32 100 0 0 0 No — 89 Alkyl silicate 657 Brush E 650 2.01 17.50 11.22 100 0 0 0 No — 32 Alkyl silicate 24 Spray E 651 1.51 6.99 55.66 100 0 0 0 No — 55 Urethane resin 99 Spray E 652 2.38 7.65 78.99 100 0 0 0 No — 79 Alkyl silicate 7 Spray E 653 1.99 8.56 5.97 100 0 0 0 No — 78 Epoxy resin 100 Spray E 654 2.49 9.34 34.67 100 0 0 0 No — 77 Alkyl silicate 27 Brush E 655 1.02 21.9 7.88 100 0 0 0 No — 56 Alkali silicate 15 Spray E 656 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 49 Alkyl silicate 14 Spray E 657 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 89 Urethane resin 55 Spray E 658 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 90 Alkyl silicate 8 Spray E 659 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 86 Urethane resin 122 Brush E 660 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 48 Alkyl silicate 555 Spray E 661 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 47 Alkali silicate 19 Spray E 662 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 47 Alkyl silicate 25 Brush E 663 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 47 Alkyl silicate 58 Spray E 664 2.37 8.00 44.94 94.3 5.7 0 0 No 1.07 52 Alkyl silicate 685 Spray E

TABLE 35 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (Ave metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 665 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 52 Alkali silicate 19 Brush E 666 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 52 Urethane resin 700 Spray E 667 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 88 Alkyl silicate 77 Spray E 668 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 87 Alkyl silicate 54 Spray E 669 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 89 Alkyl silicate 64 Spray E 670 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 90 Alkyl silicate 34 Brush E 671 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 91 Alkali silicate 28 Spray E 672 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 46 Urethane resin 109 Brush E 673 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 47 Alkyl silicate 15 Spray E 674 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 47 Alkyl silicate 14 Spray E 675 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 49 Alkyl silicate 18 Spray E 676 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 50 Alkali silicate 2 Spray G 677 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 87 Alkyl silicate 37 Spray E 678 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 83 Alkali silicate 12 Spray E 679 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 48 Alkyl silicate 160 Brush E 680 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 51 Alkali silicate 5 Brush G 681 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 51 Alkyl silicate 56 Brush E 682 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 87 Alkali silicate 2 Spray G 683 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 85 Alkyl silicate 18 Spray E 684 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 86 Alkyl silicate 23 Spray E

TABLE 36 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (Ave metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 686 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 51 Acrylic resin 77 Brush E 687 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 51 Urethane resin 655 Brush E 688 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 80 Polyester resin 47 Spray E 689 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 46 Epoxy resin 43 Spray E 690 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 51 Acrylic resin 52 Brush E 691 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 86 Urethane resin 20 Brush E 692 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 85 Polyester resin 200 Brush E 693 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 82 Alkali silicate 22 Spray E 694 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 81 Alkyl silicate 25 Spray E 695 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 46 Alkali silicate 14 Spray E 696 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 47 Urethane resin 112 Spray E 697 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 48 Alkali silicate 24 Spray E 698 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 51 Urethane resin 150 Spray E 699 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 53 Alkali silicate 18 Spray E 700 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 88 Alkyl silicate 19 Brush E 701 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 85 Alkyl silicate 24 Spray E 702 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 83 Urethane resin 99 Spray E 703 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 82 Alkyl silicate 7 Spray E 704 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 83 Epoxy resin 100 Spray E 705 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 47 Alkyl silicate 27 Brush E

TABLE 37 Granularity Percent of distribution fine-grain of Zn metal metal grains/ grains Zn alloy Coating details Zn alloy among Zn grain Total grains (Ave metal Chemical component fracture metal grain diameter) grains/ content of surfaces grain Invention (μm) Zn alloy Zn metal grains/Zn alloy or Ave content Coat Corrosion Example Fine Coarse grains grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 706 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 51 Alkali silicate 15 Spray E 707 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 52 Alkyl silicate 14 Spray E 708 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 51 Urethane resin 55 Spray E 709 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 52 Alkyl silicate 8 Spray E 710 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 89 Urethane resin 122 Brush E 711 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 85 Alkyl silicate 54 Spray E 712 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 82 Alkali silicate 19 Spray E 713 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 87 Alkyl silicate 25 Brush E 714 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 88 Alkyl silicate 58 Spray E 715 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 49 Alkyl silicate 21 Spray E 716 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 50 Alkali silicate 19 Brush E 717 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 51 Urethane resin 56 Spray E 718 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 52 Alkyl silicate 77 Spray E 719 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 53 Alkyl silicate 12 Spray E 720 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 88 Alkyl silicate 64 Spray E 721 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 85 Alkyl silicate 34 Brush E 722 2.36 12.78 45.59 80 20 0 0 Yes 1.05 83 Alkali silicate 28 Spray E 723 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 81 Urethane resin 109 Brush E 724 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 80 Alkyl silicate 15 Spray E 725 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 47 Alkyl silicate 14 Spray E

TABLE 38 Percent of Granularity fine-grain distribution of metal Zn metal grains Zn alloy Coating details grains/Zn alloy among Zn Chemical component grain Total grains (Ave metal content of Zn metal fracture metal grain diameter) grains/ grains/Zn alloy surfaces grain Invention (μm) Zn alloy grains or Ave content Coat Corrosion Example Fine Coarse grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 726 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 49 Alkyl silicate Spray E 727 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 50 Urethane resin 122 Brush E 728 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 51 Alkyl silicate 54 Spray E 729 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 52 Alkali silicate 19 Spray E 730 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 83 Alkyl silicate 25 Brush E 731 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 88 Alkyl silicate 58 Spray E 732 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 85 Alkyl silicate 21 Spray E 733 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 83 Alkali silicate 19 Brush E 734 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 82 Urethane resin 56 Spray E 735 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 47 Alkyl silicate 77 Spray E 736 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 46 Alkyl silicate 54 Spray E 737 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 49 Alkali silicate 2 Spray E 738 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 50 Alkali silicate 20 Spray E 739 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 51 Alkali silicate 5 Spray E 740 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 83 Alkyl silicate 20 Spray E 741 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 82 Alkali silicate 15 Brush E 742 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 88 Alkyl silicate 57 Brush E 743 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 85 Alkali silicate 13 Brush E 744 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 86 Alkyl silicate 22 Brush E 745 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 47 Alkali silicate 20 Spray E 746 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 48 Alkyl silicate 27 Spray E

TABLE 39 Percent of Granularity fine-grain distribution of metal Zn metal grains Zn alloy Coating details grains/Zn alloy among Zn Chemical component grain Total grains (Ave metal content of Zn metal fracture metal grain diameter) grains/ grains/Zn alloy surfaces grain Invention (μm) Zn alloy grains or Ave content Coat Corrosion Example Fine Coarse grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 747 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 50 Alkali silicate 15 Spray E 748 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 51 Alkyl silicate 35 Spray E 749 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 52 Alkali silicate 34 Brush E 750 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 88 Alkyl silicate 45 Brush E 751 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 89 Alkali silicate 52 Brush E 752 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 86 Alkyl silicate 23 Brush E 753 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 87 Alkali silicate 5 Spray E 754 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 86 Alkyl silicate 52 Brush E 755 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 46 Alkali silicate 150 Brush E 756 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 49 Alkyl silicate 60 Brush E 757 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 35 Alkali silicate 15 Spray E 758 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 37 Alkyl silicate 24 Spray E 759 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 36 Alkali silicate 34 Spray E 760 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 38 Alkyl silicate 20 Brush E 761 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 48 Alkali silicate 200 Brush E 762 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 46 Alkyl silicate 56 Brush E 763 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 51 Alkali silicate 34 Spray E 764 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 46 Alkyl silicate 2 Spray G 765 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 38 Alkali silicate 15 Spray E 766 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 48 Alkali silicate 10 Spray E

TABLE 40 Percent of Granularity fine-grain distribution of metal Zn metal grains Zn alloy Coating details grains/Zn alloy among Zn Chemical component grain Total grains (Ave metal content of Zn metal fracture metal grain diameter) grains/ grains/Zn alloy surfaces grain Invention (μm) Zn alloy grains or Ave content Coat Corrosion Example Fine Coarse grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 767 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 52 Alkyl silicate 125 Brush E 768 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 30 Alkali silicate 24 Brush E 769 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 76 Alkyl silicate 110 Brush E 770 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 72 Alkali silicate 24 Brush E 771 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 81 Alkyl silicate 2 Spray G 772 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 64 Alkali silicate 37 Spray E 773 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 69 Alkyl silicate 113 Brush E 774 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 83 Alkali silicate 2 Spray G 775 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 30 Alkyl silicate 75 Brush E 776 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 83 Alkali silicate 30 Brush E 777 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 75 Alkyl silicate 34 Brush E 778 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 76 Epoxy resin 124 Brush E 779 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 72 Acrylic Resin 15 Spray E 780 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 71 Urethane Resin 23 Spray E 781 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 82 Polyester resin 157 Brush E 782 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 81 Epoxy resin 26 Spray E 783 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 83 Acrylic resin 38 Spray E 784 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 50 Urethane resin 160 Brush E 785 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 72 Polyester resin 27 Brush E 786 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 47 Epoxy resin 180 Brush E

TABLE 41 Percent of Granularity fine-grain distribution of metal Zn metal grains Zn alloy Coating details grains/Zn alloy among Zn Chemical component grain Total grains (Ave metal content of Zn metal fracture metal grain diameter) grains/ grains/Zn alloy surfaces grain Invention (μm) Zn alloy grains or Ave content Coat Corrosion Example Fine Coarse grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 788 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 52 Urethane resin 180 Brush E 789 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 52 Polyester resin 15 Spray E 790 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 50 Epoxy resin 2 Spray G 791 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 46 Acrylic resin 28 Spray E 792 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 47 Urethane resin 30 Spray E 793 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 83 Polyester resin 2 Spray G 794 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 52 Epoxy resin 157 Brush E 795 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 89 Acrylic resin 28 Brush E 796 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 85 Alkyl silicate 130 Brush E 797 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 53 Alkyl silicate 29 Brush E 798 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 88 Epoxy resin 30 Brush E 799 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 85 Acrylic resin 120 Brush E 800 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 52 Urethane resin 187 Brush E 801 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 83 Polyester resin 28 Spray E 802 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 88 Epoxy resin 5 Spray E 803 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 49 Acrylic resin 35 Spray E 804 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 50 Urethane resin 5 Spray G 805 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 51 Polyester resin 200 Brush E 806 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 83 Alkali silicate 25 Spray E 807 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 82 Alkali silicate 15 Spray E

TABLE 42 Percent of Granularity fine-grain distribution of metal Zn metal grains Zn alloy Coating details grains/Zn alloy among Zn Chemical component grain Total grains (Ave metal content of Zn metal fracture metal grain diameter) grains/ grains/Zn alloy surfaces grain Invention (μm) Zn alloy grains or Ave content Coat Corrosion Example Fine Coarse grains (Mass %) cracks aspect of coat thickness Coating Test No metal metal (Vol %) Zn Mg Al Si present? ratio (Mass %) Base resin type (μm) method Results 808 2.57 13.25 40.76 81.4 18.6 0 0 Yes 1.16 88 Alkyl silicate 20 Spray E 809 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 85 Alkali silicate 18 Spray E 810 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 87 Alkyl silicate 22 Spray E 811 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 86 Alkali silicate 19 Spray E 812 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 46 Alkyl silicate 29 Spray E 813 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 49 Alkali silicate 23 Spray E 814 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 35 Alkyl silicate 21 Spray E 815 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 30 Alkali silicate 19 Spray E 816 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 76 Alkyl silicate 15 Spray E 817 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 72 Alkali silicate 18 Spray E 818 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 30 Alkyl silicate 22 Spray E 819 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 83 Alkyl silicate 21 Spray E 820 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 75 Alkyl silicate 29 Spray E 821 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 76 Alkali silicate 23 Spray E 822 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 72 Alkyl silicate 21 Spray E 823 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 83 Alkali silicate 19 Spray E 824 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 50 Alkyl silicate 21 Spray E 825 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 72 Alkali silicate 19 Spray E 826 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 50 Acrylic resin 654 Spray E 827 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 48 Alkali silicate 700 Spray E

TABLE 43 Percent of Zn alloy Mg Diameter fine-grain solid distribution of metal solution Zn metal grains phase grains/Zn alloy among Zn Chemical component and Zn—Mg Mg grains (Ave metal content of Zn metal intermetallic content Coat Average grain diameter) grains/ grains/Zn alloy compounds of all thickness Time to red Invention grain (μm) Zn alloy grains present on MgZn2 or metal (μm) rusting Example diameter Fine Coarse grains (Mass %) grain Mg2Zn11 grains Inor- Inor- No (μm) metal metal (Vol %) Zn Mg Al Si surfaces? present? (Mass %) ganic Organic Organic ganic 335 — 2.35 9.25 78.99 96.0 4.0 0 0 Yes Yes 92 24.6 125 E E 336 — 1.99 9.56 42.04 97.5 2.5 0 0 Yes Yes 80 23.8 167 E E 337 — 2.35 10 6.55 98.4 1.6 0 0 Yes Yes 67 15.2 88 E E 338 — 2.21 8.54 43.60 95.5 7.8 0 0 Yes Yes 77 10.6 56 E E 339 — 2.64 9.85 44.12 96.2 3.8 0 0 Yes Yes 53 10.7 256 E E 340 — 2.65 8.56 80.33 98.0 2.0 0 0 Yes No 78 15 24 E E 341 — 2.94 8.21 43.38 94.5 5.5 0 0 No No 83 10.5 96 G G 342 — 2.58 8.33 13.52 94.0 6.0 0 0 No No 89 14.5 94 G G 343 — 2.37 8.5 34.55 97.5 2.5 0 0.07 Yes Yes 90 12.3 93 E E 344 — 2.15 10.11 80.50 93.2 6.8 0 0.99 Yes Yes 45 8.6 95 E E 345 — 2.96 9.36 79.08 94.5 5.5 0 0 No No 53 17.5 92 G G 346 — 2.85 9.45 42.13 93.6 6.4 0 0 No No 48 12.6 95 G G 347 — 2.94 9.61 7.56 94.1 5.9 0 0 Yes No 46 10.4 91 E E 348 — 2.11 9.85 33.30 93.5 6.5 0 0 Yes No 47 10.9 90 E E 349 — 2.68 9.23 79.25 97.6 2.4 0 0 No No 49 19 99 G G 350 — 2.49 9.08 7.83 94.5 5.5 0 0.53 Yes Yes 83 25.6 115 E E 351 — 2.21 9.87 45.68 92.45 7.5 0 0.05 Yes Yes 35 18 97 E E 352 — 2.96 9.46 65.58 90.45 9.5 0.05 0 No No 90 24.7 94 G G 353 — 2.85 9.28 47.24 91.38 8.6 0.02 0 No No 89 22.9 93 G G 354 — 2.64 9.45 47.76 91.1 7.9 1 0 Yes No 88 52.3 83 G G

TABLE 44 Percent of Zn alloy Mg Diameter fine-grain solid distribution of metal solution Zn metal grains phase grains/Zn alloy among Zn Chemical component and Zn—Mg Mg Average grains (Ave metal content of Zn metal intermetallic content Coat grain grain diameter) grains/ grains/Zn alloy compounds of all thickness Time to red Invention di- (μm) Zn alloy grains present on MgZn2 or metal (μm) rusting Example ameter Fine Coarse grains (Mass %) grain Mg2Zn11 grains Inor- Inor- No (μm) metal metal (Vol %) Zn Mg Al Si surfaces? present? (Mass %) ganic Organic Organic ganic 355 — 2.35 9.25 80.06 81.1 13.7 5.2 0 Yes Yes 47 56.3 88 E G 356 — 2.12 9.46 47.02 85.6 9.8 4.6 0 No No 47 33.3 89 G G 357 — 1.76 9.46 7.66 89.5 10.5 0 0.001 No No 52 34.5 87 G G 358 — 2.12 9.46 15.20 91.2 8.8 0 0 Yes Yes 52 23.5 103 E E 359 — 1.65 9.06 86.28 96.1 3.9 0 0 Yes Yes 52 26.7 85 E E 360 — 2.12 10.99 49.33 97.5 2.5 0 0 Yes Yes 88 19.5 109 E E 361 — 2.21 8.08 5.99 94 6 0 0 Yes Yes 49 15 74 E E 362 — 1.99 8.53 69.55 99.4 0.6 0 0 Yes Yes 35 23 105 E E 363 — 1.95 9.32 86.45 91.6 7.9 0 0.5 No No 37 31.2 83 G G 364 — 1.76 8.95 75.88 98.5 0.5 0.3 0.7 No No 36 37.5 82 G G 365 — 1.48 10.21 48.08 88.43 11.5 0.02 0.05 Yes Yes 80 9.8 124 E E 366 — 1.65 8.7 66.85 95.73 3.5 0.12 0.65 Yes Yes 55 15.5 89 E E 367 — 2.35 9.86 7.68 92.09 7.8 0.06 0.05 No No 46 14.5 96 G G 368 — 1.62 8.91 8.64 95.49 3.5 0.02 0.99 Yes Yes 35 16.3 95 E E 369 — 1.88 9.91 16.58 93.96 5 0.54 0.5 Yes Yes 67 15.8 99 E E 370 — 2.35 9.25 35.87 91.45 8.5 0.05 0 No No 47 19 89 G G 371 — 2.57 9.56 42.04 97.13 2.4 0.02 0.45 Yes Yes 78 14.6 89 E E 372 — 2.56 9.84 38.41 94.58 5.4 0.02 0.11 Yes Yes 34 19.5 98 E E 373 — 2.21 9.75 6.99 95.65 6.8 0.05 0.8 No No 51 24.7 96 G G

TABLE 45 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase Any of of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 837 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 838 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 839 2.56 9.84 6.55 81.45 18.5 0 0.5 Yes 1.22 Yes Yes 840 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 841 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 842 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 843 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 844 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 845 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 846 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 847 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 848 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 849 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 850 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 851 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 852 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 853 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 854 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 855 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 856 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 837 49 Alkyl silicate 14 Spray E 838 89 Urethane resin 55 Spray E 839 90 Alkyl silicate 8 Spray E 840 86 Urethane resin 122 Brush E 841 48 Alkyl silicate 555 Spray E 842 47 Alkali silicate 19 Spray E 843 47 Alkyl silicate 25 Brush E 844 47 Alkyl silicate 58 Spray E 845 52 Alkyl silicate 685 Spray E 846 52 Alkali silicate 19 Brush E 847 52 Urethane resin 700 Spray E 848 88 Alkyl silicate 77 Spray E 849 87 Alkyl silicate 54 Spray E 850 89 Alkyl silicate 64 Spray E 851 90 Alkyl silicate 34 Brush E 852 91 Alkali silicate 28 Spray E 853 46 Urethane resin 109 Brush E 854 47 Alkyl silicate 15 Spray E 855 47 Alkyl silicate 14 Spray E 856 49 Alkyl silicate 18 Spray E

TABLE 46 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase and Any of of Zn metal among Zn Chemical component grain Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 857 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 858 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 859 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 860 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 861 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 862 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 863 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 864 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 865 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 866 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 867 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 868 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 869 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 870 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 871 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 872 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 873 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 874 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 875 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 876 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 857 50 Alkali silicate 2 Spray G 858 87 Alkyl silicate 37 Spray E 859 83 Alkali silicate 12 Spray E 860 48 Alkyl silicate 160 Brush E 861 51 Alkali silicate 5 Brush G 862 51 Alkyl silicate 56 Brush E 863 87 Alkali silicate 2 Spray G 864 85 Alkyl silicate 18 Spray E 865 86 Alkyl silicate 23 Spray E 866 50 Epoxy resin 30 Brush E 867 51 Acrylic resin 77 Brush E 868 51 Urethane resin 655 Brush E 869 80 Polyester resin 47 Spray E 870 46 Epoxy resin 43 Spray E 871 51 Acrylic resin 52 Brush E 872 86 Urethane resin 20 Brush E 873 85 Polyester resin 200 Brush E 874 82 Alkali silicate 22 Spray E 875 81 Alkyl silicate 25 Spray E 876 46 Alkali silicate 14 Spray E

TABLE 47 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase and Any of of Zn metal among Zn Chemical component grain Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 877 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 878 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 879 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 880 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 881 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 882 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 883 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 884 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 885 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 886 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 887 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 888 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 889 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 890 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 891 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 892 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 893 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 894 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 895 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 896 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 877 47 Urethane resin 112 Spray E 878 48 Alkali silicate 24 Spray E 879 51 Urethane resin 150 Spray E 880 53 Alkali silicate 18 Spray E 881 88 Alkyl silicate 19 Brush E 882 85 Alkyl silicate 24 Spray E 883 83 Urethane resin 99 Spray E 884 82 Alkyl silicate 7 Spray E 885 83 Epoxy resin 100 Spray E 886 47 Alkyl silicate 27 Brush E 887 51 Alkali silicate 15 Spray E 888 52 Alkyl silicate 14 Spray E 889 51 Urethane resin 55 Spray E 890 52 Alkyl silicate 8 Spray E 891 89 Urethane resin 122 Brush E 892 85 Alkyl silicate 54 Spray E 893 82 Alkali silicate 19 Spray E 894 87 Alkyl silicate 25 Brush E 895 88 Alkyl silicate 58 Spray E 896 49 Alkyl silicate 21 Spray E

TABLE 48 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase and Any of of Zn metal among Zn Chemical component grain Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 897 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 898 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 899 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 900 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 901 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 902 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 903 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 904 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 905 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 906 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 907 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 908 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 909 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 910 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 911 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 912 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 913 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 914 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 915 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 916 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 897 50 Alkali silicate 19 Brush E 898 51 Urethane resin 56 Spray E 899 52 Alkyl silicate 77 Spray E 900 53 Alkyl silicate 12 Spray E 901 88 Alkyl silicate 64 Spray E 902 85 Alkyl silicate 34 Brush E 903 83 Alkali silicate 28 Spray E 904 81 Urethane resin 109 Brush E 905 80 Alkyl silicate 15 Spray E 906 47 Alkyl silicate 14 Spray E 907 49 Alkyl silicate 18 Spray E 908 50 Urethane resin 122 Brush E 909 51 Alkyl silicate 54 Spray E 910 52 Alkali silicate 19 Spray E 911 83 Alkyl silicate 25 Brush E 912 88 Alkyl silicate 58 Spray E 913 85 Alkyl silicate 21 Spray E 914 83 Alkali silicate 19 Brush E 915 82 Urethane resin 56 Spray E 916 47 Alkyl silicate 77 Spray E

TABLE 49 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase and Any of of Zn metal among Zn Chemical component grain Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 917 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 918 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 919 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 920 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 921 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 922 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 923 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 924 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 925 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 926 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 927 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 928 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 929 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 930 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 931 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 932 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 933 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 934 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 935 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 936 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 917 46 Alkyl silicate 54 Spray E 918 49 Alkali silicate 2 Spray G 919 50 Alkali silicate 20 Spray E 920 51 Alkali silicate 5 Spray G 921 83 Alkyl silicate 20 Spray E 922 82 Alkali silicate 15 Brush E 923 88 Alkyl silicate 57 Brush E 924 85 Alkali silicate 13 Brush E 925 86 Alkyl silicate 22 Brush E 926 47 Alkali silicate 20 Spray E 927 48 Alkyl silicate 27 Spray E 928 50 Alkali silicate 15 Spray E 929 51 Alkyl silicate 35 Spray E 930 52 Alkali silicate 34 Brush E 931 88 Alkyl silicate 45 Brush E 932 89 Alkali silicate 52 Brush E 933 86 Alkyl silicate 23 Brush E 934 87 Alkali silicate 5 Spray E 935 86 Alkyl silicate 52 Brush E 936 46 Alkali silicate 150 Brush E

TABLE 50 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase and Any of of Zn metal among Zn Chemical component grain Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 937 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 938 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 939 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 940 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 941 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 942 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 943 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 944 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 945 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 946 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 947 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 948 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 949 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 950 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 951 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 952 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 953 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 954 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 955 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 956 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes 957 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 937 49 Alkyl silicate 60 Brush E 938 35 Alkali silicate 15 Spray E 939 37 Alkyl silicate 24 Spray E 940 36 Alkali silicate 34 Spray E 941 38 Alkyl silicate 20 Brush E 942 48 Alkali silicate 200 Brush E 943 46 Alkyl silicate 56 Brush E 944 51 Alkali silicate 34 Spray E 945 46 Alkyl silicate 2 Spray G 946 38 Alkali silicate 15 Spray E 947 48 Alkali silicate 10 Spray E 948 52 Alkyl silicate 125 Brush E 949 30 Alkali silicate 24 Brush E 950 76 Alkyl silicate 110 Brush E 951 72 Alkali silicate 24 Brush E 952 81 Alkyl silicate 2 Spray G 953 64 Alkali silicate 37 Spray E 954 69 Alkyl silicate 113 Brush E 955 83 Alkali silicate 2 Spray G 956 30 Alkyl silicate 75 Brush E 957 83 Alkali silicate 30 Brush E

TABLE 51 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase and Any of of Zn metal among Zn Chemical component grain Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 958 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 959 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 960 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 961 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 962 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 963 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 964 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 965 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 966 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 967 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 968 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 969 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 970 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 971 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 972 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 973 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 974 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 975 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 976 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes 977 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 958 75 Alkyl silicate 34 Brush E 959 76 Epoxy resin 124 Brush E 960 72 Acrylic resin 15 Spray E 961 71 Urethane resin 23 Spray E 962 82 Polyester resin 157 Brush E 963 81 Epoxy resin 26 Spray E 964 83 Acrylic resin 38 Spray E 965 50 Urethane resin 160 Brush E 966 72 Polyester resin 27 Brush E 967 47 Epoxy resin 180 Brush E 968 47 Acrylic resin 26 Spray E 969 52 Urethane resin 180 Brush E 970 52 Polyester resin 15 Spray E 971 50 Epoxy resin 2 Spray G 972 46 Acrylic resin 28 Spray E 973 47 Urethane resin 30 Spray E 974 83 Polyester resin 2 Spray G 975 52 Epoxy resin 157 Brush E 976 89 Acrylic resin 28 Brush E 977 85 Alkyl silicate 130 Brush E

TABLE 52 Percent of Granularity fine-grain Mg solid distribution metal solution (peak diameter) grains Zn alloy phase and Any of of Zn metal among Zn Chemical component grain Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 978 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 979 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 980 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 981 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 982 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 983 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 984 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 985 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 986 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 987 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 988 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 989 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 990 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 991 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 992 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 993 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 994 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 995 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 996 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes 997 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes Coating details Total metal grain Invention content Coat Corrosion Example of coat thickness Coating Test No (Mass %) Base resin type (μm) method Results 978 53 Alkyl silicate 29 Brush E 979 88 Epoxy resin 30 Brush E 980 85 Acrylic resin 120 Brush E 981 52 Urethane resin 187 Brush E 982 83 Polyester resin 28 Spray E 983 88 Epoxy resin 5 Spray E 984 49 Acrylic resin 35 Spray E 985 50 Urethane resin 5 Spray G 986 51 Polyester resin 200 Brush E 987 83 Alkali silicate 25 Spray E 988 82 Alkali silicate 15 Spray E 989 88 Alkyl silicate 20 Spray E 990 85 Alkali silicate 18 Spray E 991 87 Alkyl silicate 22 Spray E 992 86 Alkali silicate 19 Spray E 993 46 Alkyl silicate 29 Spray E 994 49 Alkali silicate 23 Spray E 995 35 Alkyl silicate 21 Spray E 996 30 Alkali silicate 19 Spray E 997 76 Alkyl silicate 15 Spray E

TABLE 53 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces?  998 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes  999 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes 1000 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes 1001 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes 1002 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes 1003 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes 1004 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes 1005 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes 1006 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes 1007 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes 1008 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes 1009 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes 1010 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes 1011 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes 1012 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes 1013 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes 1014 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes 1015 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes 1016 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes 1017 2.57 11.9 45.90 60.9 27.5 10.8 0.8 Yes 1.23 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results  998 Yes 72 Alkali silicate 18 Spray E  999 Yes 30 Alkyl silicate 22 Spray E 1000 Yes 83 Alkyl silicate 21 Spray E 1001 Yes 75 Alkyl silicate 29 Spray E 1002 Yes 76 Alkali silicate 23 Spray E 1003 Yes 72 Alkyl silicate 21 Spray E 1004 Yes 83 Alkali silicate 19 Spray E 1005 Yes 50 Alkyl silicate 21 Spray E 1006 Yes 72 Alkali silicate 19 Spray E 1007 Yes 50 Acrylic resin 654 Spray E 1008 Yes 48 Alkali silicate 700 Spray E 1009 Yes 75 Alkyl silicate 555 Spray E 1010 Yes 55 Alkyl silicate 321 Spray E 1011 Yes 38 Alkyl silicate 152 Brush E 1012 Yes 48 Urethane resin 674 Spray E 1013 Yes 76 Polyester resin 325 Spray E 1014 Yes 72 Alkyl silicate 665 Spray E 1015 Yes 75 Alkyl silicate 354 Brush E 1016 Yes 76 Alkyl silicate 165 Spray E 1017 Yes 72 Urethane resin 354 Spray E

TABLE 54 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1018 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes 1019 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes 1020 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes 1021 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes 1022 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes 1023 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes 1024 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No 1025 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No 1026 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes 1027 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes 1028 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No 1029 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No 1030 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes 1031 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes 1032 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No 1033 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes 1034 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes 1035 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No 1036 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No 1037 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1018 Yes 49 Alkyl silicate 14 Spray E 1019 Yes 89 Urethane resin 55 Spray E 1020 Yes 90 Alkyl silicate 8 Spray E 1021 Yes 86 Urethane resin 122 Brush E 1022 Yes 48 Alkyl silicate 555 Spray E 1023 Yes 47 Alkali silicate 19 Spray E 1024 Yes 47 Alkyl silicate 25 Brush E 1025 Yes 47 Alkyl silicate 58 Spray E 1026 Yes 52 Alkyl silicate 685 Spray E 1027 Yes 52 Alkali silicate 19 Brush E 1028 Yes 52 Urethane resin 700 Spray E 1029 Yes 88 Alkyl silicate 77 Spray E 1030 Yes 87 Alkyl silicate 54 Spray E 1031 Yes 89 Alkyl silicate 64 Spray E 1032 Yes 90 Alkyl silicate 34 Brush E 1033 Yes 91 Alkali silicate 28 Spray E 1034 Yes 46 Urethane resin 109 Brush E 1035 Yes 47 Alkyl silicate 15 Spray E 1036 Yes 47 Alkyl silicate 14 Spray E 1037 Yes 49 Alkyl silicate 18 Spray E

TABLE 55 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1038 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes 1039 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No 1040 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No 1041 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes 1042 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes 1043 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes 1044 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes 1045 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes 1046 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No 1047 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No 1048 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes 1049 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes 1050 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No 1051 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes 1052 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes 1053 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No 1054 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes 1055 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes 1056 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No 1057 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1038 Yes 50 Alkali silicate 2 Spray G 1039 Yes 87 Alkyl silicate 37 Spray E 1040 Yes 83 Alkali silicate 12 Spray E 1041 Yes 48 Alkyl silicate 160 Brush E 1042 Yes 51 Alkali silicate 5 Brush G 1043 Yes 51 Alkyl silicate 56 Brush E 1044 Yes 87 Alkali silicate 2 Spray G 1045 Yes 85 Alkyl silicate 18 Spray E 1046 Yes 86 Alkyl silicate 23 Spray E 1047 Yes 50 Epoxy resin 30 Brush E 1048 Yes 51 Acrylic resin 77 Brush E 1049 Yes 51 Urethane resin 655 Brush E 1050 Yes 80 Polyester resin 47 Spray E 1051 Yes 46 Epoxy resin 43 Spray E 1052 Yes 51 Acrylic resin 52 Brush E 1053 Yes 86 Urethane resin 20 Brush E 1054 Yes 85 Polyester resin 200 Brush E 1055 Yes 82 Alkali silicate 22 Spray E 1056 Yes 81 Alkyl silicate 25 Spray E 1057 Yes 46 Alkali silicate 14 Spray E

TABLE 56 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1058 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes 1059 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes 1060 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes 1061 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes 1062 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes 1063 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes 1064 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes 1065 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes 1066 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes 1067 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes 1068 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes 1069 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes 1070 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes 1071 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes 1072 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes 1073 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes 1074 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes 1075 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes 1076 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes 1077 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1058 Yes 47 Urethane resin 112 Spray E 1059 Yes 48 Alkali silicate 24 Spray E 1060 Yes 51 Urethane resin 150 Spray E 1061 Yes 53 Alkali silicate 18 Spray E 1062 Yes 88 Alkyl silicate 19 Brush E 1063 Yes 85 Alkyl silicate 24 Spray E 1064 Yes 83 Urethane resin 99 Spray E 1065 Yes 82 Alkyl silicate 7 Spray E 1066 Yes 83 Epoxy resin 100 Spray E 1067 Yes 47 Alkyl silicate 27 Brush E 1068 Yes 51 Alkali silicate 15 Spray E 1069 Yes 52 Alkyl silicate 14 Spray E 1070 Yes 51 Urethane resin 55 Spray E 1071 Yes 52 Alkyl silicate 8 Spray E 1072 Yes 89 Urethane resin 122 Brush E 1073 Yes 85 Alkyl silicate 54 Spray E 1074 Yes 82 Alkali silicate 19 Spray E 1075 Yes 87 Alkyl silicate 25 Brush E 1076 Yes 88 Alkyl silicate 58 Spray E 1077 Yes 49 Alkyl silicate 21 Spray E

TABLE 57 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1078 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes 1079 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes 1080 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes 1081 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes 1082 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes 1083 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes 1084 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes 1085 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes 1086 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes 1087 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes 1088 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes 1089 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes 1090 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes 1091 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes 1092 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes 1093 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes 1094 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes 1095 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes 1096 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes 1097 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1078 Yes 50 Alkali silicate 19 Brush E 1079 Yes 51 Urethane resin 56 Spray E 1080 Yes 52 Alkyl silicate 77 Spray E 1081 Yes 53 Alkyl silicate 12 Spray E 1082 Yes 88 Alkyl silicate 64 Spray E 1083 Yes 85 Alkyl silicate 34 Brush E 1084 Yes 83 Alkali silicate 28 Spray E 1085 Yes 81 Urethane resin 109 Brush E 1086 Yes 80 Alkyl silicate 15 Spray E 1087 Yes 47 Alkyl silicate 14 Spray E 1088 Yes 49 Alkyl silicate 18 Spray E 1089 Yes 50 Urethane resin 122 Brush E 1090 Yes 51 Alkyl silicate 54 Spray E 1091 Yes 52 Alkali silicate 19 Spray E 1092 Yes 83 Alkyl silicate 25 Brush E 1093 Yes 88 Alkyl silicate 58 Spray E 1094 Yes 85 Alkyl silicate 21 Spray E 1095 Yes 83 Alkali silicate 19 Brush E 1096 Yes 82 Urethane resin 56 Spray E 1097 Yes 47 Alkyl silicate 77 Spray E

TABLE 58 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1098 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes 1099 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes 1100 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes 1101 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes 1102 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes 1103 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes 1104 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes 1105 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes 1106 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes 1107 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes 1108 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes 1109 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes 1110 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes 1111 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes 1112 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes 1113 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes 1114 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes 1115 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes 1116 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes 1117 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1098 Yes 46 Alkyl silicate 54 Spray E 1099 Yes 49 Alkali silicate 2 Spray G 1100 Yes 50 Alkali silicate 20 Spray E 1101 Yes 51 Alkali silicate 5 Spray G 1102 Yes 83 Alkyl silicate 20 Spray E 1103 Yes 82 Alkali silicate 15 Brush E 1104 Yes 88 Alkyl silicate 57 Brush E 1105 Yes 85 Alkali silicate 13 Brush E 1106 Yes 86 Alkyl silicate 22 Brush E 1107 Yes 47 Alkali silicate 20 Spray E 1108 Yes 48 Alkyl silicate 27 Spray E 1109 Yes 50 Alkali silicate 15 Spray E 1110 Yes 51 Alkyl silicate 35 Spray E 1111 Yes 52 Alkali silicate 34 Brush E 1112 Yes 88 Alkyl silicate 45 Brush E 1113 Yes 89 Alkali silicate 52 Brush E 1114 Yes 86 Alkyl silicate 23 Brush E 1115 Yes 87 Alkali silicate 5 Spray E 1116 Yes 86 Alkyl silicate 52 Brush E 1117 Yes 46 Alkali silicate 150 Brush E

TABLE 59 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1118 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes 1119 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes 1120 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes 1121 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes 1122 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes 1123 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes 1124 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes 1125 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes 1126 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes 1127 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes 1128 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes 1129 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes 1130 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes 1131 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes 1132 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes 1133 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes 1134 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes 1135 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes 1136 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes 1137 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1118 Yes 49 Alkyl silicate 60 Brush E 1119 Yes 35 Alkali silicate 15 Spray E 1120 Yes 37 Alkyl silicate 24 Spray E 1121 Yes 36 Alkali silicate 34 Spray E 1122 Yes 38 Alkyl silicate 20 Brush E 1123 Yes 48 Alkali silicate 200 Brush E 1124 Yes 46 Alkyl silicate 56 Brush E 1125 Yes 51 Alkali silicate 34 Spray E 1126 Yes 46 Alkyl silicate 2 Spray G 1127 Yes 38 Alkali silicate 15 Spray E 1128 Yes 48 Alkali silicate 10 Spray E 1129 Yes 52 Alkyl silicate 125 Brush E 1130 Yes 30 Alkali silicate 24 Brush E 1131 Yes 76 Alkyl silicate 110 Brush E 1132 Yes 72 Alkali silicate 24 Brush E 1133 Yes 81 Alkyl silicate 2 Spray G 1134 Yes 64 Alkali silicate 37 Spray E 1135 Yes 69 Alkyl silicate 113 Brush E 1136 Yes 83 Alkali silicate 2 Spray G 1137 Yes 30 Alkyl silicate 75 Brush E

TABLE 60 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1138 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes 1139 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes 1140 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes 1141 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes 1142 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes 1143 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes 1144 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes 1145 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes 1146 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes 1147 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes 1148 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes 1149 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes 1150 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes 1151 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes 1152 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes 1153 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes 1154 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes 1155 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes 1156 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes 1157 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1138 Yes 83 Alkali silicate 30 Brush E 1139 Yes 75 Alkyl silicate 34 Brush E 1140 Yes 76 Epoxy resin 124 Brush E 1141 Yes 72 Acrylic resin 15 Spray E 1142 Yes 71 Urethane resin 23 Spray E 1143 Yes 82 Polyester resin 157 Brush E 1144 Yes 81 Epoxy resin 26 Spray E 1145 Yes 83 Acrylic resin 38 Spray E 1146 Yes 50 Urethane resin 160 Brush E 1147 Yes 72 Polyester resin 27 Brush E 1148 Yes 47 Epoxy resin 180 Brush E 1149 Yes 47 Acrylic resin 26 Spray E 1150 Yes 52 Urethane resin 180 Brush E 1151 Yes 52 Polyester resin 15 Spray E 1152 Yes 50 Epoxy resin 2 Spray G 1153 Yes 46 Acrylic resin 28 Spray E 1154 Yes 47 Urethane resin 30 Spray E 1155 Yes 83 Polyester resin 2 Spray G 1156 Yes 52 Epoxy resin 157 Brush E 1157 Yes 89 Acrylic resin 28 Brush E

TABLE 61 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1158 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes 1159 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes 1160 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes 1161 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes 1162 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes 1163 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes 1164 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes 1165 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes 1166 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes 1167 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes 1168 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes 1169 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes 1170 2.57 13.25 40.76 81.4 18.6 0 0 Yes 1.16 Yes 1171 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes 1172 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes 1173 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes 1174 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes 1175 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes 1176 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes 1177 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1158 Yes 85 Alkyl silicate 130 Brush E 1159 Yes 53 Alkyl silicate 29 Brush E 1160 Yes 88 Epoxy resin 30 Brush E 1161 Yes 85 Acrylic resin 120 Brush E 1162 Yes 52 Urethane resin 187 Brush E 1163 Yes 83 Polyester resin 28 Spray E 1164 Yes 88 Epoxy resin 5 Spray E 1165 Yes 49 Acrylic resin 35 Spray E 1166 Yes 50 Urethane resin 5 Spray G 1167 Yes 51 Polyester resin 200 Brush E 1168 Yes 83 Alkali silicate 25 Spray E 1169 Yes 82 Alkali silicate 15 Spray E 1170 Yes 88 Alkyl silicate 20 Spray E 1171 Yes 85 Alkali silicate 18 Spray E 1172 Yes 87 Alkyl silicate 22 Spray E 1173 Yes 86 Alkali silicate 19 Spray E 1174 Yes 46 Alkyl silicate 29 Spray E 1175 Yes 49 Alkali silicate 23 Spray E 1176 Yes 35 Alkyl silicate 21 Spray E 1177 Yes 30 Alkali silicate 19 Spray E

TABLE 62 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1178 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes 1179 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes 1180 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes 1181 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes 1182 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes 1183 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes 1184 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes 1185 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes 1186 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes 1187 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes 1188 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes 1189 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes 1190 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes 1191 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes 1192 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes 1193 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes 1194 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes 1195 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes 1196 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes 1197 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes 1198 2.57 11.9 45.90 60.9 27.5 10.8 0.8 Yes 1.23 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, content Coat Example Mg7Zn3 of coat thickness Coating No present? (Mass %) Base resin type (μm) method Corrosion Test Results 1178 Yes 76 Alkyl silicate 15 Spray E 1179 Yes 72 Alkali silicate 18 Spray E 1180 Yes 30 Alkyl silicate 22 Spray E 1181 Yes 83 Alkyl silicate 21 Spray E 1182 Yes 75 Alkyl silicate 29 Spray E 1183 Yes 76 Alkali silicate 23 Spray E 1184 Yes 72 Alkyl silicate 21 Spray E 1185 Yes 83 Alkali silicate 19 Spray E 1186 Yes 50 Alkyl silicate 21 Spray E 1187 Yes 72 Alkali silicate 19 Spray E 1188 Yes 50 Acrylic resin 654 Spray E 1189 Yes 48 Alkali silicate 700 Spray E 1190 Yes 75 Alkyl silicate 555 Spray E 1191 Yes 55 Alkyl silicate 321 Spray E 1192 Yes 38 Alkyl silicate 152 Brush E 1193 Yes 48 Urethane resin 674 Spray E 1194 Yes 76 Polyester resin 325 Spray E 1195 Yes 72 Alkyl silicate 665 Spray E 1196 Yes 75 Alkyl silicate 354 Brush E 1197 Yes 76 Alkyl silicate 165 Spray E 1198 Yes 72 Urethane resin 354 Spray E

TABLE 63 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1199 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes 1200 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes 1201 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes 1202 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes 1203 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes 1204 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes 1205 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No 1206 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No 1207 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes 1208 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes 1209 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No 1210 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No 1211 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes 1212 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes 1213 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No 1214 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes 1215 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes 1216 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No 1217 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, Number content Coat Example Mg7Zn3 of of coat thickness Coating No present? faces (Mass %) Base resin type (μm) method Corrosion Test Results 1199 Yes 2 49 Alkyl silicate 14 Spray E 1200 Yes 2 89 Urethane resin 55 Spray E 1201 Yes 2 90 Alkyl silicate 8 Spray E 1202 Yes 2 86 Urethane resin 122 Brush E 1203 Yes 6 48 Alkyl silicate 555 Spray E 1204 Yes 6 47 Alkali silicate 19 Spray E 1205 Yes 7 47 Alkyl silicate 25 Brush E 1206 Yes 6 47 Alkyl silicate 58 Spray E 1207 Yes 2 52 Alkyl silicate 685 Spray E 1208 Yes 7 52 Alkali silicate 19 Brush E 1209 Yes 2 52 Urethane resin 700 Spray E 1210 Yes 6 88 Alkyl silicate 77 Spray E 1211 Yes 6 87 Alkyl silicate 54 Spray E 1212 Yes 2 89 Alkyl silicate 64 Spray E 1213 Yes 2 90 Alkyl silicate 34 Brush E 1214 Yes 7 91 Alkali silicate 28 Spray E 1215 Yes 6 46 Urethane resin 109 Brush E 1216 Yes 7 47 Alkyl silicate 15 Spray E 1217 Yes 2 47 Alkyl silicate 14 Spray E

TABLE 64 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1218 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes 1219 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes 1220 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No 1221 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No 1222 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes 1223 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes 1224 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes 1225 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes 1226 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes 1227 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No 1228 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No 1229 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes 1230 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes 1231 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No 1232 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes 1233 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes 1234 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No 1235 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes 1236 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, Number content Coat Example Mg7Zn3 of of coat thickness Coating No present? faces (Mass %) Base resin type (μm) method Corrosion Test Results 1218 Yes 7 49 Alkyl silicate 18 Spray E 1219 Yes 6 50 Alkali silicate 2 Spray G 1220 Yes 7 87 Alkyl silicate 37 Spray E 1221 Yes 6 83 Alkali silicate 12 Spray E 1222 Yes 7 48 Alkyl silicate 160 Brush E 1223 Yes 6 51 Alkali silicate 5 Brush G 1224 Yes 2 51 Alkyl silicate 56 Brush E 1225 Yes 7 87 Alkali silicate 2 Spray G 1226 Yes 6 85 Alkyl silicate 18 Spray E 1227 Yes 6 86 Alkyl silicate 23 Spray E 1228 Yes 6 50 Epoxy resin 30 Brush E 1229 Yes 2 51 Acrylic resin 77 Brush E 1230 Yes 6 51 Urethane resin 655 Brush E 1231 Yes 7 80 Polyester resin 47 Spray E 1232 Yes 2 46 Epoxy resin 43 Spray E 1233 Yes 6 51 Acrylic resin 52 Brush E 1234 Yes 2 86 Urethane resin 20 Brush E 1235 Yes 6 85 Polyester resin 200 Brush E 1236 Yes 7 82 Alkali silicate 22 Spray E

TABLE 65 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1237 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No 1238 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes 1239 2.65 8.56 66.99 98.6 1.40 0 0 No 1.22 Yes 1240 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes 1241 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes 1242 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes 1243 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes 1244 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes 1245 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes 1246 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes 1247 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes 1248 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes 1249 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes 1250 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes 1251 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes 1252 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes 1253 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes 1254 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes 1255 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, Number content Coat Example Mg7Zn3 of of coat thickness Coating No present? faces (Mass %) Base resin type (μm) method Corrosion Test Results 1237 Yes 7 81 Alkyl silicate 25 Spray E 1238 Yes 2 46 Alkali silicate 14 Spray E 1239 Yes 2 47 Urethane resin 112 Spray E 1240 Yes 6 48 Alkali silicate 24 Spray E 1241 Yes 7 51 Urethane resin 150 Spray E 1242 Yes 6 53 Alkali silicate 18 Spray E 1243 Yes 7 88 Alkyl silicate 19 Brush E 1244 Yes 6 85 Alkyl silicate 24 Spray E 1245 Yes 2 83 Urethane resin 99 Spray E 1246 Yes 2 82 Alkyl silicate 7 Spray E 1247 Yes 6 83 Epoxy resin 100 Spray E 1248 Yes 7 47 Alkyl silicate 27 Brush E 1249 Yes 6 51 Alkali silicate 15 Spray E 1250 Yes 6 52 Alkyl silicate 14 Spray E 1251 Yes 2 51 Urethane resin 55 Spray E 1252 Yes 7 52 Alkyl silicate 8 Spray E 1253 Yes 2 89 Urethane resin 122 Brush E 1254 Yes 2 85 Alkyl silicate 54 Spray E 1255 Yes 6 82 Alkali silicate 19 Spray E

TABLE 66 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1256 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes 1257 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes 1258 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes 1259 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes 1260 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes 1261 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes 1262 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes 1263 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes 1264 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes 1265 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes 1266 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes 1267 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes 1268 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes 1269 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes 1270 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes 1271 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes 1272 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes 1273 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes 1274 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, Number content Coat Example Mg7Zn3 of of coat thickness Coating No present? faces (Mass %) Base resin type (μm) method Corrosion Test Results 1256 Yes 7 87 Alkyl silicate 25 Brush E 1257 Yes 7 88 Alkyl silicate 58 Spray E 1258 Yes 6 49 Alkyl silicate 21 Spray E 1259 Yes 7 50 Alkali silicate 19 Brush E 1260 Yes 7 51 Urethane resin 56 Spray E 1261 Yes 6 52 Alkyl silicate 77 Spray E 1262 Yes 7 53 Alkyl silicate 12 Spray E 1263 Yes 2 88 Alkyl silicate 64 Spray E 1264 Yes 7 85 Alkyl silicate 34 Brush E 1265 Yes 7 83 Alkali silicate 28 Spray E 1266 Yes 2 81 Urethane resin 109 Brush E 1267 Yes 6 80 Alkyl silicate 15 Spray E 1268 Yes 6 47 Alkyl silicate 14 Spray E 1269 Yes 7 49 Alkyl silicate 18 Spray E 1270 Yes 7 50 Urethane resin 122 Brush E 1271 Yes 6 51 Alkyl silicate 54 Spray E 1272 Yes 7 52 Alkali silicate 19 Spray E 1273 Yes 2 83 Alkyl silicate 25 Brush E 1274 Yes 2 88 Alkyl silicate 58 Spray E

TABLE 67 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution of Zn metal among Zn Chemical component grain phase and Zn—Mg grains/Zn metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or Ave present on Example Fine Coarse grains (Mass %) cracks aspect grain No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? 1275 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes 1276 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes 1277 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes 1278 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes 1279 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes 1280 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes 1281 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes 1282 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes 1283 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes 1284 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes 1285 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes 1286 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes 1287 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes 1288 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes 1289 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes 1290 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes 1291 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes 1292 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes 1293 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Any of Coating details MgZn2, Total Mg2Zn11, metal Mg2Zn3, grain Invention MgZn, Number content Coat Example Mg7Zn3 of of coat thickness Coating No present? faces (Mass %) Base resin type (μm) method Corrosion Test Results 1275 Yes 6 85 Alkyl silicate 21 Spray E 1276 Yes 7 83 Alkali silicate 19 Brush E 1277 Yes 6 82 Urethane resin 56 Spray E 1278 Yes 2 47 Alkyl silicate 77 Spray E 1279 Yes 2 46 Alkyl silicate 54 Spray E 1280 Yes 7 49 Alkali silicate 2 Spray G 1281 Yes 6 50 Alkali silicate 20 Spray E 1282 Yes 7 51 Alkali silicate 5 Spray G 1283 Yes 7 83 Alkyl silicate 20 Spray E 1284 Yes 6 82 Alkali silicate 15 Brush E 1285 Yes 2 88 Alkyl silicate 57 Brush E 1286 Yes 7 85 Alkali silicate 13 Brush E 1287 Yes 2 86 Alkyl silicate 22 Brush E 1288 Yes 2 47 Alkali silicate 20 Spray E 1289 Yes 7 48 Alkyl silicate 27 Spray E 1290 Yes 2 50 Alkali silicate 15 Spray E 1291 Yes 7 51 Alkyl silicate 35 Spray E 1292 Yes 2 52 Alkali silicate 34 Brush E 1293 Yes 6 88 Alkyl silicate 45 Brush E

TABLE 68 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1294 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 1295 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 1296 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 1297 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 1298 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes 1299 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 1300 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 1301 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 1302 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 1303 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 1304 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 1305 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 1306 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 1307 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 1308 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 1309 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 1310 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 1311 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 1312 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1294 6 89 Alkali silicate 52 Brush E 1295 7 86 Alkyl silicate 23 Brush E 1296 6 87 Alkali silicate 5 Spray E 1297 2 86 Alkyl silicate 52 Brush E 1298 2 46 Alkali silicate 150 Brush E 1299 2 49 Alkyl silicate 60 Brush E 1300 2 35 Alkali silicate 15 Spray E 1301 2 37 Alkyl silicate 24 Spray E 1302 2 36 Alkali silicate 34 Spray E 1303 6 38 Alkyl silicate 20 Brush E 1304 6 48 Alkali silicate 200 Brush E 1305 7 46 Alkyl silicate 56 Brush E 1306 6 51 Alkali silicate 34 Spray E 1307 2 46 Alkyl silicate 2 Spray G 1308 7 38 Alkali silicate 15 Spray E 1309 2 48 Alkali silicate 10 Spray E 1310 6 52 Alkyl silicate 125 Brush E 1311 6 30 Alkali silicate 24 Brush E 1312 2 76 Alkyl silicate 110 Brush E

TABLE 69 Percent of Granularity fine-grain distribution metal Mg solid (peak diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1313 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 1314 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 1315 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 1316 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 1317 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 1318 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes 1319 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 1320 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 1321 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 1322 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 1323 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 1324 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 1325 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 1326 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 1327 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 1328 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 1329 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 1330 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 1331 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1313 2 72 Alkali silicate 24 Brush E 1314 7 81 Alkyl silicate 2 Spray G 1315 6 64 Alkali silicate 37 Spray E 1316 7 69 Alkyl silicate 113 Brush E 1317 2 83 Alkali silicate 2 Spray G 1318 7 30 Alkyl silicate 75 Brush E 1319 6 83 Alkali silicate 30 Brush E 1320 7 75 Alkyl silicate 34 Brush E 1321 6 76 Epoxy resin 124 Brush E 1322 7 72 Acrylic resin 15 Spray E 1323 6 71 Urethane resin 23 Spray E 1324 2 82 Polyester resin 157 Brush E 1325 7 81 Epoxy resin 26 Spray E 1326 6 83 Acrylic resin 38 Spray E 1327 6 50 Urethane resin 160 Brush E 1328 6 72 Polyester resin 27 Brush E 1329 2 47 Epoxy resin 180 Brush E 1330 6 47 Acrylic resin 26 Spray E 1331 7 52 Urethane resin 180 Brush E

TABLE 70 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1380 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 1381 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 1382 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes Yes 1383 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 1384 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 1385 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 1386 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 1387 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 1388 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 1389 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 1390 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 1391 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 1392 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 1393 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 1394 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 1395 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 1396 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 1397 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 1398 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 1399 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1380 2 49 Alkyl silicate 14 Spray E 1381 2 89 Urethane resin 55 Spray E 1382 2 90 Alkyl silicate 8 Spray E 1383 2 86 Urethane resin 122 Brush E 1384 6 48 Alkyl silicate 555 Spray E 1385 6 47 Alkali silicate 19 Spray E 1386 7 47 Alkyl silicate 25 Brush E 1387 6 47 Alkyl silicate 58 Spray E 1388 2 52 Alkyl silicate 685 Spray E 1389 7 52 Alkali silicate 19 Brush E 1390 2 52 Urethane resin 700 Spray E 1391 6 88 Alkyl silicate 77 Spray E 1392 6 87 Alkyl silicate 54 Spray E 1393 2 89 Alkyl silicate 64 Spray E 1394 2 90 Alkyl silicate 34 Brush E 1395 7 91 Alkali silicate 28 Spray E 1396 6 46 Urethane resin 109 Brush E 1397 7 47 Alkyl silicate 15 Spray E 1398 2 47 Alkyl silicate 14 Spray E 1399 7 49 Alkyl silicate 18 Spray E

TABLE 71 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1400 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 1401 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 1402 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 1403 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 1404 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 1405 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 1406 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 1407 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 1408 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 1409 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 1410 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 1411 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 1412 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 1413 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 1414 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 1415 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 1416 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 1417 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 1418 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 1419 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1400 6 50 Alkali silicate 2 Spray G 1401 7 87 Alkyl silicate 37 Spray E 1402 6 83 Alkali silicate 12 Spray E 1403 7 48 Alkyl silicate 160 Brush E 1404 6 51 Alkali silicate 5 Brush G 1405 2 51 Alkyl silicate 56 Brush E 1406 7 87 Alkali silicate 2 Spray G 1407 6 85 Alkyl silicate 18 Spray E 1408 6 86 Alkyl silicate 23 Spray E 1409 6 50 Epoxy resin 30 Brush E 1410 2 51 Acrylic resin 77 Brush E 1411 6 51 Urethane resin 655 Brush E 1412 7 80 Polyester resin 47 Spray E 1413 2 46 Epoxy resin 43 Spray E 1414 6 51 Acrylic resin 52 Brush E 1415 2 86 Urethane resin 20 Brush E 1416 6 85 Polyester resin 200 Brush E 1417 7 82 Alkali silicate 22 Spray E 1418 7 81 Alkyl silicate 25 Spray E 1419 2 46 Alkali silicate 14 Spray E

TABLE 72 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1420 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 1421 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 1422 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 1423 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 1424 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 1425 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 1426 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 1427 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 1428 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 1429 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 1430 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 1431 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 1432 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 1433 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 1434 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 1435 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 1436 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 1437 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 1438 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 1439 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1420 2 47 Urethane resin 112 Spray E 1421 6 48 Alkali silicate 24 Spray E 1422 7 51 Urethane resin 150 Spray E 1423 6 53 Alkali silicate 18 Spray E 1424 7 88 Alkyl silicate 19 Brush E 1425 6 85 Alkyl silicate 24 Spray E 1426 2 83 Urethane resin 99 Spray E 1427 2 82 Alkyl silicate 7 Spray E 1428 6 83 Epoxy resin 100 Spray E 1429 7 47 Alkyl silicate 27 Brush E 1430 6 51 Alkali silicate 15 Spray E 1431 6 52 Alkyl silicate 14 Spray E 1432 2 51 Urethane resin 55 Spray E 1433 7 52 Alkyl silicate 8 Spray E 1434 2 89 Urethane resin 122 Brush E 1435 2 85 Alkyl silicate 54 Spray E 1436 6 82 Alkali silicate 19 Spray E 1437 7 87 Alkyl silicate 25 Brush E 1438 7 88 Alkyl silicate 58 Spray E 1439 6 49 Alkyl silicate 21 Spray E

TABLE 73 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1440 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 1441 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 1442 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 1443 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 1444 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 1445 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 1446 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 1447 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 1448 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 1449 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 1450 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 1451 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 1452 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 1453 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 1454 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 1455 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 1456 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 1457 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 1458 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 1459 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1440 7 50 Alkali silicate 19 Brush E 1441 7 51 Urethane resin 56 Spray E 1442 6 52 Alkyl silicate 77 Spray E 1443 7 53 Alkyl silicate 12 Spray E 1444 2 88 Alkyl silicate 64 Spray E 1445 7 85 Alkyl silicate 34 Bursh E 1446 7 83 Alkali silicate 28 Spray E 1447 2 81 Urethane resin 109 Bursh E 1448 6 80 Alkyl silicate 15 Spray E 1449 6 47 Alkyl silicate 14 Spray E 1450 7 49 Alkyl silicate 18 Spray E 1451 7 50 Urethane resin 122 Brush E 1452 6 51 Alkyl silicate 54 Spray E 1453 7 52 Alkali silicate 19 Spray E 1454 2 83 Alkyl silicate 25 Brush E 1455 2 88 Alkyl silicate 58 Spray E 1456 6 85 Alkyl silicate 21 Spray E 1457 7 83 Alkali silicate 19 Brush E 1458 6 82 Urethane resin 56 Spray E 1459 2 47 Alkyl silicate 77 Spray E

TABLE 74 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1460 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 1461 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 1462 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 1463 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 1464 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 1465 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 1466 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 1467 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 1468 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 1469 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 1470 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 1471 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 1472 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 1473 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 1474 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 1475 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 1476 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 1477 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 1478 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 1479 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1460 2 46 Alkyl silicate 54 Spray E 1461 7 49 Alkali silicate 2 Spray G 1462 6 50 Alkali silicate 20 Spray E 1463 7 51 Alkali silicate 5 Spray G 1464 7 83 Alkyl silicate 20 Spray E 1465 6 82 Alkali silicate 15 Brush E 1466 2 88 Alkyl silicate 57 Brush E 1467 7 85 Alkali silicate 13 Brush E 1468 2 86 Alkyl silicate 22 Brush E 1469 2 47 Alkali silicate 20 Spray E 1470 7 48 Alkyl silicate 27 Spray E 1471 2 50 Alkali silicate 15 Spray E 1472 7 51 Alkyl silicate 35 Spray E 1473 2 52 Alkali silicate 34 Brush E 1474 6 88 Alkyl silicate 45 Brush E 1475 6 89 Alkali silicate 52 Brush E 1476 7 86 Alkyl silicate 23 Brush E 1477 6 87 Alkali silicate 5 Spray E 1478 2 86 Alkyl silicate 52 Brush E 1479 2 46 Alkali silicate 150 Brush E

TABLE 75 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1480 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 1481 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 1482 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 1483 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 1484 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 1485 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 1486 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 1487 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 1488 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 1489 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 1490 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 1491 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 1492 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 1493 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 1494 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 1495 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 1496 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 1497 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 1498 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 1499 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1480 2 49 Alkyl silicate 60 Brush E 1481 2 35 Alkali silicate 15 Spray E 1482 2 37 Alkyl silicate 24 Spray E 1483 2 36 Alkali silicate 34 Spray E 1484 6 38 Alkyl silicate 20 Brush E 1485 6 48 Alkali silicate 200 Brush E 1486 7 46 Alkyl silicate 56 Brush E 1487 6 51 Alkali silicate 34 Spray E 1488 2 46 Alkyl silicate 2 Spray G 1489 7 38 Alkali silicate 15 Spray E 1490 2 48 Alkali silicate 10 Spray E 1491 6 52 Alkyl silicate 125 Brush E 1492 6 30 Alkali silicate 24 Brush E 1493 2 76 Alkyl silicate 110 Brush E 1494 2 72 Alkali silicate 24 Brush E 1495 7 81 Alkyl silicate 2 Spray G 1496 6 64 Alkali silicate 37 Spray E 1497 7 69 Alkyl silicate 113 Brush E 1498 2 83 Alkali silicate 2 Spray G 1499 7 30 Alkyl silicate 75 Brush E

TABLE 76 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1500 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 1501 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 1502 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 1503 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 1504 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 1505 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 1506 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 1507 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 1508 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 1509 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 1510 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 1511 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 1512 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 1513 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 1514 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 1515 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 1516 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 1517 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 1518 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 1519 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1500 6 83 Alkali silicate 30 Brush E 1501 7 75 Alkyl silicate 34 Brush E 1502 6 76 Epoxy resin 124 Brush E 1503 7 72 Acrylic resin 15 Spray E 1504 6 71 Urethane resin 23 Spray E 1505 2 82 Polyester resin 157 Brush E 1506 7 81 Epoxy resin 26 Spray E 1507 6 83 Acrylic resin 38 Spray E 1508 6 50 Urethane resin 160 Brush E 1509 6 72 Polyester resin 27 Brush E 1510 2 47 Epoxy resin 180 Brush E 1511 6 47 Acrylic resin 26 Spray E 1512 7 52 Urethane resin 180 Brush E 1513 2 52 Polyester resin 15 Spray E 1514 6 50 Epoxy resin 2 Spray G 1515 2 46 Acrylic resin 28 Spray E 1516 6 47 Urethane resin 30 Spray E 1517 7 83 Polyester resin 2 Spray G 1518 7 52 Epoxy resin 157 Brush E 1519 2 89 Acrylic resin 28 Brush E

TABLE 77 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1520 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 1521 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 1522 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 1523 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 1524 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 1525 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 1526 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 1527 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 1528 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 1529 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 1530 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 1531 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 1532 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 1533 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 1534 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 1535 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 1536 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 1537 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 1538 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 1539 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1520 2 85 Alkyl silicate 130 Brush E 1521 6 53 Alkyl silicate 29 Brush E 1522 7 88 Epoxy resin 30 Brush E 1523 6 85 Acrylic resin 120 Brush E 1524 7 52 Urethane resin 187 Brush E 1525 6 83 Polyester resin 28 Spray E 1526 2 88 Epoxy resin 5 Spray E 1527 2 49 Acrylic resin 35 Spray E 1528 6 50 Urethane resin 5 Spray G 1529 7 51 Polyester resin 200 Brush E 1530 6 83 Alkali silicate 25 Spray E 1531 6 82 Alkali silicate 15 Spray E 1532 2 88 Alkyl silicate 20 Spray E 1533 7 85 Alkali silicate 18 Spray E 1534 2 87 Alkyl silicate 22 Spray E 1535 2 86 Alkali silicate 19 Spray E 1536 6 46 Alkyl silicate 29 Spray E 1537 7 49 Alkali silicate 23 Spray E 1538 7 35 Alkyl silicate 21 Spray E 1539 6 30 Alkali silicate 19 Spray E

TABLE 78 Percent of Granularity fine-grain distribution metal Mg solid (Ave diameter) grains Zn alloy solution Any of of Zn metal among Zn Chemical component grain phase and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1540 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 1541 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 1542 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 1543 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 1544 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 1545 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 1546 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 1547 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 1548 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 1549 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 1550 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 1551 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 1552 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 1553 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 1554 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 1555 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 1556 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 1557 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 1558 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 1559 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 1560 2.57 11.9 45.90 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes Coating details Total metal grain Invention Number content Coat Example of of coat thickness Coating No faces (Mass %) Base resin type (μm) method Corrosion Test Results 1540 7 76 Alkyl silicate 15 Spray E 1541 7 72 Alkali silicate 18 Spray E 1542 6 30 Alkyl silicate 22 Spray E 1543 7 83 Alkyl silicate 21 Spray E 1544 2 75 Alkyl silicate 29 Spray E 1545 7 76 Alkali silicate 23 Spray E 1546 7 72 Alkyl silicate 21 Spray E 1547 2 83 Alkali silicate 19 Spray E 1548 6 50 Alkyl silicate 21 Spray E 1549 6 72 Alkali silicate 19 Spray E 1550 2 50 Acrylic resin 654 Spray E 1551 6 48 Alkali silicate 700 Spray E 1552 7 75 Alkyl silicate 555 Spray E 1553 7 55 Alkyl silicate 321 Spray E 1554 6 38 Alkyl silicate 152 Brush E 1555 7 48 Urethane resin 674 Spray E 1556 7 76 Polyester resin 325 Spray E 1557 6 72 Alkyl silicate 665 Spray E 1558 7 75 Alkyl silicate 354 Brush E 1559 6 76 Alkyl silicate 165 Spray E 1560 7 72 Urethane resin 354 Spray E

TABLE 79 Granularity Percent of distribution fine-grain Ratio of fine of Zn metal metal grains metal grains/ grains Total in coat Zn alloy among Zn Chemical component metal outermost Inven- grains (Ave metal content of Zn metal grain surface layer tion Average grain diameter) grains/ grains/Zn alloy content 10% thickness Coat Exam- grain (μm) Zn alloy grains of to total fine thickness Time to red ple diameter Fine Coarse grains (Mass %) coat metal grains (μm) rusting No (μm) metal metal (Vol %) Zn Mg Al Si (Mass %) (Mass %) Inorganic Organic Organic Inorganic 374 — 2.35 9.25 35.87 96.0 8.9 0 0 47 55.7 24.6 125 E E 375 — 2.49 9.56 42.04 97.5 7.8 0 0 80 64.5 23.8 167 E E 376 — 1.99 9.84 6.55 98.4 5.6 0 0 52 68.9 15.2 28 E E 377 — 2.21 8.64 66.80 95.5 10.2 0 0 89 64.7 10.6 34 E E 378 — 2.64 10.55 80.03 96.2 5.6 0 0 34 77.9 10.7 256 E E 379 — 2.55 8.56 67.55 98.0 7.8 0 0 78 43.7 15 24 G G 380 — 2.94 9.99 43.38 94.5 8.9 0 0 34 7.8 10.5 96 G G 381 — 1.98 8.98 13.52 94.0 6.0 0 0 89 16.0 14.5 94 G G 382 — 2.37 8.99 68.14 97.5 12.6 0 0 90 89.6 12.3 93 E E 383 — 2.15 9.22 81.37 93.2 6.8 0 0 86 11.8 8.6 95 G G 384 — 2.96 9.36 66.30 94.5 5.5 0 0 53 4.6 17.5 92 G G 385 — 2.85 9.45 42.13 93.6 6.4 0 0 48 2.5 12.6 95 G G 386 — 2.94 9.61 7.56 94.1 5.9 0 0 46 18.9 10.4 91 G G 387 — 2.11 9.85 66.89 93.5 6.5 0.54 0.55 47 75.9 10.9 90 E E 388 — 2.68 9.23 80.12 97.6 2.4 0 0.66 49 55.9 19 99 E E 389 — 1.99 9.08 39.51 94.5 5.5 0 0.07 83 53.8 25.6 98 E E 390 — 1.76 9.87 45.68 91.75 7.5 0.6 0.15 85 97.5 28.6 97 E E 391 — 2.66 9.46 65.58 90.4 9.5 0.05 0.05 90 88.4 24.7 94 E E 392 — 2.85 9.28 70.44 90.4 8.6 0.02 0.98 89 54.8 22.9 93 E E 393 — 2.64 9.45 83.67 91.1 7.9 1 0 88 45.7 52.3 83 G G

TABLE 80 Granularity Percent of distribution fine-grain Ratio of fine of Zn metal metal grains metal grains/ grains Total in coat Zn alloy among Zn Chemical component metal outermost Inven- grains (Ave metal content of Zn metal grain surface layer tion Average grain diameter) grains/ grains/Zn alloy content 10% thickness Coat Exam- grain (μm) Zn alloy grains of to total fine thickness Time to red ple diameter Fine Coarse grains (Mass %) coat metal grains (μm) rusting No (μm) metal metal (Vol %) Zn Mg Al Si (Mass %) (Mass %) Inorganic Organic Organic Inorganic 394 — 2.35 9.25 80.93 81.1 13.7 5.2 0 47 34.7 56.3 88 G G 395 — 2.12 9.46 47.02 89.2 9.8 1 0 47 57.9 33.3 89 E E 396 — 2.26 10.54 7.66 89.45 10.5 0.05 0 52 65.4 34.5 87 E E 397 — 1.76 9.55 15.20 82.93 16.4 0.07 0.6 52 87.9 23.5 86 E E 398 — 2.23 9.06 73.50 95.3 3.9 0 0.8 52 2.9 26.7 85 G G 399 — 2.12 9.3 49.33 95 2.5 0 2.5 88 12.6 195 243 G G 400 — 2.21 8.68 19.47 93.46 6 0 0.54 49 53.8 23 74 E E 401 — 1.38 8.53 69.55 94.1 5 0 0.9 35 17.8 23 63 G G 402 — 1.95 9.32 87.32 96.7 2.8 0 0.5 37 34.7 31.2 83 G G 403 — 1.26 8.95 75.88 98.5 0.5 0.3 0.7 36 76.8 37.5 82 E E 404 — 1.03 10.99 7.77 94.52 5.4 0.02 0.06 80 58.9 12.5 81 E E 405 — 1.65 8.7 43.55 95.65 3.5 0.05 0.8 48 50.8 10.2 89 E E 406 — 2.35 8.55 7.68 89 3.3 5.2 2.5 46 46.8 14.5 96 G G 407 — 1.62 9.99 8.64 94.98 3.5 0.02 1.5 52 23.7 16.3 95 G G 408 — 1.88 9.91 16.58 89.5 5 4.6 0.9 51 53.8 15.8 99 E E 409 — 2.35 9.25 35.87 91.45 8.5 0.05 0 47 53.8 19 89 E E 410 — 2.57 9.56 42.04 97.58 2.4 0.02 0 48 43.7 25.6 89 G G 411 — 2.56 9.84 38.41 94.58 0.56 0.02 0.06 49 55.9 28.6 98 E E 412 — 2.21 9.75 6.99 95.65 1.55 0.05 0.8 51 65.8 24.7 96 E E

TABLE 81 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Number Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 of No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? faces 1561 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 2 1562 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 2 1563 2.56 9.84 6.55 81.45 18.5 0 0.5 Yes 1.22 Yes Yes 2 1564 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 2 1565 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 6 1566 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 6 1567 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 7 1568 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 6 1569 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 2 1570 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 7 1571 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 2 1572 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 6 1573 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 6 1574 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 2 1575 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 2 1576 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 7 1577 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 6 1578 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 7 1579 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 2 1580 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes 7 Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention fine metal content Coat Example grains of coat thickness Coating No (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1561 55.7 49 Alkyl silicate 14 Spray E 1562 64.5 89 Urethane resin 55 Spray E 1563 68.9 90 Alkyl silicate 8 Spray E 1564 64.7 86 Urethane resin 122 Brush E 1565 77.9 48 Alkyl silicate 555 Spray E 1566 43.7 47 Alkali silicate 19 Spray E 1567 7.8 47 Alkyl silicate 25 Brush E 1568 16.0 47 Alkyl silicate 58 Spray E 1569 89.6 52 Alkyl silicate 685 Spray E 1570 11.8 52 Alkali silicate 19 Brush E 1571 4.6 52 Urethane resin 700 Spray E 1572 2.5 88 Alkyl silicate 77 Spray E 1573 18.9 87 Alkyl silicate 54 Spray E 1574 75.9 89 Alkyl silicate 64 Spray E 1575 55.9 90 Alkyl silicate 34 Brush E 1576 53.8 91 Alkali silicate 28 Spray E 1577 97.5 46 Urethane resin 109 Brush E 1578 88.4 47 Alkyl silicate 15 Spray E 1579 54.8 47 Alkyl silicate 14 Spray E 1580 45.7 49 Alkyl silicate 18 Spray E

TABLE 82 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Number Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 of No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? faces 1581 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 6 1582 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 7 1583 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 6 1584 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 7 1585 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 6 1586 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 2 1587 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 7 1588 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 6 1589 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 6 1590 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 6 1591 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 2 1592 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 6 1593 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 7 1594 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 2 1595 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 6 1596 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 2 1597 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 6 1598 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 7 1599 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 7 1600 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes 2 Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention fine metal content Coat Example grains of coat thickness Coating No (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1581 34.7 50 Alkali silicate 2 Spray G 1582 57.9 87 Alkyl silicate 37 Spray E 1583 65.4 83 Alkali silicate 12 Spray E 1584 87.9 48 Alkyl silicate 160 Brush E 1585 2.9 51 Alkali silicate 5 Brush G 1586 12.6 51 Alkyl silicate 56 Brush E 1587 53.8 87 Alkali silicate 2 Spray G 1588 17.8 85 Alkyl silicate 18 Spray E 1589 34.7 86 Alkyl silicate 23 Spray E 1590 76.8 50 Epoxy resin 30 Brush E 1591 58.9 51 Acrylic resin 77 Brush E 1592 50.8 51 Urethane resin 655 Brush E 1593 46.8 80 Polyester resin 47 Spray E 1594 23.7 46 Epoxy resin 43 Spray E 1595 53.8 51 Acrylic resin 52 Brush E 1596 53.8 86 Urethane resin 20 Brush E 1597 43.7 85 Polyester resin 200 Brush E 1598 55.9 82 Alkali silicate 22 Spray E 1599 65.8 81 Alkyl silicate 25 Spray E 1600 55.7 46 Alkali silicate 14 Spray E

TABLE 83 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1601 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 1602 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 1603 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 1604 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 1605 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 1606 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 1607 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 1608 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 1609 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 1610 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 1611 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 1612 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 1613 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 1614 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 1615 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 1616 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 1617 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 1618 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 1619 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 1620 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1601 2 64.5 47 Urethane resin 112 Spray E 1602 6 68.9 48 Alkali silicate 24 Spray E 1603 7 64.7 51 Urethane resin 150 Spray E 1604 6 77.9 53 Alkali silicate 18 Spray E 1605 7 43.7 88 Alkyl silicate 19 Brush E 1606 6 7.8 85 Alkyl silicate 24 Spray E 1607 2 16.0 83 Urethane resin 99 Spray E 1608 2 89.6 82 Alkyl silicate 7 Spray E 1609 6 11.8 83 Epoxy resin 100 Spray E 1610 7 4.6 47 Alkyl silicate 27 Brush E 1611 6 2.5 51 Alkali silicate 15 Spray E 1612 6 18.9 52 Alkyl silicate 14 Spray E 1613 2 75.9 51 Urethane resin 55 Spray E 1614 7 55.9 52 Alkyl silicate 8 Spray E 1615 2 53.8 89 Urethane resin 122 Brush E 1616 2 97.5 85 Alkyl silicate 54 Spray E 1617 6 88.4 82 Alkali silicate 19 Spray E 1618 7 54.8 87 Alkyl silicate 25 Brush E 1619 7 45.7 88 Alkyl silicate 58 Spray E 1620 6 34.7 49 Alkyl silicate 21 Spray E

TABLE 84 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1621 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 1622 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 1623 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 1624 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 1625 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 1626 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 1627 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 1628 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 1629 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 1630 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 1631 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 1632 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 1633 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 1634 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 1635 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 1636 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 1637 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 1638 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 1639 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 1640 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Number fine metal content Coat Invention of grains of coat thickness Coating Example No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1621 7 57.9 50 Alkali silicate 19 Brush E 1622 7 65.4 51 Urethane resin 56 Spray E 1623 6 87.9 52 Alkyl silicate 77 Spray E 1624 7 2.9 53 Alkyl silicate 12 Spray E 1625 2 12.6 88 Alkyl silicate 64 Spray E 1626 7 53.8 85 Alkyl silicate 34 Brush E 1627 7 17.8 83 Alkali silicate 28 Spray E 1628 2 34.7 81 Urethane resin 109 Brush E 1629 6 55.7 80 Alkyl silicate 15 Spray E 1630 6 64.5 47 Alkyl silicate 14 Spray E 1631 7 68.9 49 Alkyl silicate 18 Spray E 1632 7 64.7 50 Urethane resin 122 Brush E 1633 6 77.9 51 Alkyl silicate 54 Spray E 1634 7 43.7 52 Alkali silicate 19 Spray E 1635 2 7.8 83 Alkyl silicate 25 Brush E 1636 2 16.0 88 Alkyl silicate 58 Spray E 1637 6 89.6 85 Alkyl silicate 21 Spray E 1638 7 11.8 83 Alkali silicate 19 Brush E 1639 6 4.6 82 Urethane resin 56 Spray E 1640 2 2.5 47 Alkyl silicate 77 Spray E

TABLE 85 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1641 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 1642 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 1643 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 1644 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 1645 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 1646 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 1647 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 1648 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 1649 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 1650 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 1651 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 1652 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 1653 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 1654 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 1655 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 1656 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 1657 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 1658 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 1659 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 1660 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1641 2 18.9 46 Alkyl silicate 54 Spray E 1642 7 75.9 49 Alkali silicate 2 Spray G 1643 6 55.9 50 Alkali silicate 20 Spray E 1644 7 53.8 51 Alkali silicate 5 Spray G 1645 7 97.5 83 Alkyl silicate 20 Spray E 1646 6 88.4 82 Alkali silicate 15 Brush E 1647 2 54.8 88 Alkyl silicate 57 Brush E 1648 7 45.7 85 Alkali silicate 13 Brush E 1649 2 34.7 86 Alkyl silicate 22 Brush E 1650 2 57.9 47 Alkali silicate 20 Spray E 1651 7 65.4 48 Alkyl silicate 27 Spray E 1652 2 87.9 50 Alkali silicate 15 Spray E 1653 7 2.9 51 Alkyl silicate 35 Spray E 1654 2 12.6 52 Alkali silicate 34 Brush E 1655 6 53.8 88 Alkyl silicate 45 Brush E 1656 6 17.8 89 Alkali silicate 52 Brush E 1657 7 34.7 86 Alkyl silicate 23 Brush E 1658 6 76.8 87 Alkali silicate 5 Spray E 1659 2 58.9 86 Alkyl silicate 52 Brush E 1660 2 50.8 46 Alkali silicate 150 Brush E

TABLE 86 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1661 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 1662 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 1663 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 1664 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 1665 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 1666 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 1667 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 1668 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 1669 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 1670 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 1671 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 1672 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 1673 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 1674 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 1675 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 1676 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 1677 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 1678 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 1679 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 1680 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1661 2 46.8 49 Alkyl silicate 60 Brush E 1662 2 23.7 35 Alkali silicate 15 Spray E 1663 2 53.8 37 Alkyl silicate 24 Spray E 1664 2 53.8 36 Alkali silicate 34 Spray E 1665 6 43.7 38 Alkyl silicate 20 Brush E 1666 6 55.9 48 Alkali silicate 200 Brush E 1667 7 65.8 46 Alkyl silicate 56 Brush E 1668 6 55.7 51 Alkali silicate 34 Spray E 1669 2 64.5 46 Alkyl silicate 2 Spray G 1670 7 68.9 38 Alkali silicate 15 Spray E 1671 2 64.7 48 Alkali silicate 10 Spray E 1672 6 77.9 52 Alkyl silicate 125 Brush E 1673 6 43.7 30 Alkali silicate 24 Brush E 1674 2 7.8 76 Alkyl silicate 110 Brush E 1675 2 16.0 72 Alkali silicate 24 Brush E 1676 7 89.6 81 Alkyl silicate 2 Spray G 1677 6 11.8 64 Alkali silicate 37 Spray E 1678 7 4.6 69 Alkyl silicate 113 Brush E 1679 2 2.5 83 Alkali silicate 2 Spray G 1680 7 18.9 30 Alkyl silicate 75 Brush E

TABLE 87 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1681 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 1682 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 1683 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 1684 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 1685 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 1686 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 1687 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 1688 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 1689 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 1690 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 1691 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 1692 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 1693 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 1694 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 1695 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 1696 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 1697 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 1698 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 1699 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 1700 2.54 11.99 37.95 88.9 9.4 0.7 0 Yes 1.08 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1681 6 75.9 83 Alkali silicate 30 Brush E 1682 7 55.9 75 Alkyl silicate 34 Brush E 1683 6 53.8 76 Epoxy resin 124 Brush E 1684 7 97.5 72 Acrylic resin 15 Spray E 1685 6 88.4 71 Urethane resin 23 Spray E 1686 2 54.8 82 Polyester resin 157 Brush E 1687 7 45.7 81 Epoxy resin 26 Spray E 1688 6 34.7 83 Acrylic resin 38 Spray E 1689 6 57.9 50 Urethane resin 160 Brush E 1690 6 65.4 72 Polyester resin 27 Brush E 1691 2 87.9 47 Epoxy resin 180 Brush E 1692 6 2.9 47 Acrylic resin 26 Spray E 1693 7 12.6 52 Urethane resin 180 Brush E 1694 2 53.8 52 Polyester resin 15 Spray E 1695 6 17.8 50 Epoxy resin 2 Spray G 1696 2 34.7 46 Acrylic resin 28 Spray E 1697 6 55.7 47 Urethane resin 30 Spray E 1698 7 64.5 83 Polyester resin 2 Spray G 1699 7 68.9 52 Epoxy resin 157 Brush E 1700 2 64.7 89 Acrylic resin 28 Brush E

TABLE 88 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1701 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 1702 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 1703 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 1704 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 1705 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 1706 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 1707 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 1708 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 1709 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 1710 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 1711 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 1712 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 1713 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 1714 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 1715 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 1716 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 1717 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 1718 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 1719 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 1720 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1701 2 77.9 85 Alkyl silicate 130 Brush E 1702 6 43.7 53 Alkyl silicate 29 Brush E 1703 7 7.8 88 Epoxy resin 30 Brush E 1704 6 16.0 85 Acrylic resin 120 Brush E 1705 7 89.6 52 Urethane resin 187 Brush E 1706 6 11.8 83 Polyester resin 28 Spray E 1707 2 4.6 88 Epoxy resin 5 Spray E 1708 2 2.5 49 Acrylic resin 35 Spray E 1709 6 18.9 50 Urethane resin 5 Spray G 1710 7 75.9 51 Polyester resin 200 Brush E 1711 6 55.9 83 Alkali silicate 25 Spray E 1712 6 53.8 82 Alkali silicate 15 Spray E 1713 2 97.5 88 Alkyl silicate 20 Spray E 1714 7 88.4 85 Alkali silicate 18 Spray E 1715 2 54.8 87 Alkyl silicate 22 Spray E 1716 2 45.7 86 Alkali silicate 19 Spray E 1717 6 34.7 46 Alkyl silicate 29 Spray E 1718 7 57.9 49 Alkali silicate 23 Spray E 1719 7 65.4 35 Alkyl silicate 21 Spray E 1720 6 87.9 30 Alkali silicate 19 Spray E

TABLE 89 Percent Diameter of fine- distribution grain (peak metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1721 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 1722 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 1723 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 1724 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 1725 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 1726 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 1727 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 1728 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 1729 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 1730 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 1731 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 1732 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 1733 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 1734 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 1735 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 1736 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 1737 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 1738 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 1739 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 1740 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 1741 2.57 11.9 45.90 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1721 7 2.9 76 Alkyl silicate 15 Spray E 1722 7 12.6 72 Alkali silicate 18 Spray E 1723 6 53.8 30 Alkyl silicate 22 Spray E 1724 7 17.8 83 Alkyl silicate 21 Spray E 1725 2 34.7 75 Alkyl silicate 29 Spray E 1726 7 76.8 76 Alkali silicate 23 Spray E 1727 7 58.9 72 Alkyl silicate 21 Spray E 1728 2 50.8 83 Alkali silicate 19 Spray E 1729 6 46.8 50 Alkyl silicate 21 Spray E 1730 6 23.7 72 Alkali silicate 19 Spray E 1731 2 87.9 50 Acrylic resin 654 Spray E 1732 6 2.9 48 Alkali silicate 700 Spray E 1733 7 12.6 75 Alkyl silicate 555 Spray E 1734 7 53.8 55 Alkyl silicate 321 Spray E 1735 6 17.8 38 Alkyl silicate 152 Brush E 1736 7 34.7 48 Urethane resin 674 Spray E 1737 7 76.8 76 Polyester resin 325 Spray E 1738 6 58.9 72 Alkyl silicate 665 Spray E 1739 7 50.8 75 Alkyl silicate 354 Brush E 1740 6 46.8 76 Alkyl silicate 165 Spray E 1741 7 23.7 72 Urethane resin 354 Spray E

TABLE 90 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1742 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 1743 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 1744 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes Yes 1745 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 1746 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 1747 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 1748 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 1749 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 1750 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 1751 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 1752 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 1753 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 1754 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 1755 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 1756 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 1757 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 1758 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 1759 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 1760 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 1761 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1742 2 55.7 49 Alkyl silicate 14 Spray E 1743 2 64.5 89 Urethane resin 55 Spray E 1744 2 68.9 90 Alkyl silicate 8 Spray E 1745 2 64.7 86 Urethane resin 122 Brush E 1746 6 77.9 48 Alkyl silicate 555 Spray E 1747 6 43.7 47 Alkali silicate 19 Spray E 1748 7 7.8 47 Alkyl silicate 25 Brush E 1749 6 16.0 47 Alkyl silicate 58 Spray E 1750 2 89.6 52 Alkyl silicate 685 Spray E 1751 7 11.8 52 Alkali silicate 19 Brush E 1752 2 4.6 52 Urethane resin 700 Spray E 1753 6 2.5 88 Alkyl silicate 77 Spray E 1754 6 18.9 87 Alkyl silicate 54 Spray E 1755 2 75.9 89 Alkyl silicate 64 Spray E 1756 2 55.9 90 Alkyl silicate 34 Brush E 1757 7 53.8 91 Alkali silicate 28 Spray E 1758 6 97.5 46 Urethane resin 109 Brush E 1759 7 88.4 47 Alkyl silicate 15 Spray E 1760 2 54.8 47 Alkyl silicate 14 Spray E 1761 7 45.7 49 Alkyl silicate 18 Spray E

TABLE 91 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1762 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 1763 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 1764 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 1765 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 1766 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 1767 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 1768 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 1769 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 1770 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 1771 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 1772 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 1773 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 1774 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 1775 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 1776 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 1777 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 1778 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 1779 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 1780 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 1781 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1762 6 34.7 50 Alkali silicate 2 Spray G 1763 7 57.9 87 Alkyl silicate 37 Spray E 1764 6 65.4 83 Alkali silicate 12 Spray E 1765 7 87.9 48 Alkyl silicate 160 Brush E 1766 6 2.9 51 Alkali silicate 5 Brush G 1767 2 12.6 51 Alkyl silicate 56 Brush E 1768 7 53.8 87 Alkali silicate 2 Spray G 1769 6 17.8 85 Alkyl silicate 18 Spray E 1770 6 34.7 86 Alkyl silicate 23 Spray E 1771 6 76.8 50 Epoxy resin 30 Brush E 1772 2 58.9 51 Acrylic resin 77 Brush E 1773 6 50.8 51 Urethane resin 655 Brush E 1774 7 46.8 80 Polyester resin 47 Spray E 1775 2 23.7 46 Epoxy resin 43 Spray E 1776 6 53.8 51 Acrylic resin 52 Brush E 1777 2 53.8 86 Urethane resin 20 Brush E 1778 6 43.7 85 Polyester resin 200 Brush E 1779 7 55.9 82 Alkali silicate 22 Spray E 1780 7 65.8 81 Alkyl silicate 25 Spray E 1781 2 55.7 46 Alkali silicate 14 Spray E

TABLE 92 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1782 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 1783 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 1784 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 1785 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 1786 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 1787 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 1788 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 1789 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 1790 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 1791 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 1792 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 1793 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 1794 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 1795 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 1796 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 1797 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 1798 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 1799 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 1800 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 1801 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1782 2 64.5 47 Urethane resin 112 Spray E 1783 6 68.9 48 Alkali silicate 24 Spray E 1784 7 64.7 51 Urethane resin 150 Spray E 1785 6 77.9 53 Alkali silicate 18 Spray E 1786 7 43.7 88 Alkyl silicate 19 Brush E 1787 6 7.8 85 Alkyl silicate 24 Spray E 1788 2 16.0 83 Urethane resin 99 Spray E 1789 2 89.6 82 Alkyl silicate 7 Spray E 1790 6 11.8 83 Epoxy resin 100 Spray E 1791 7 4.6 47 Alkyl silicate 27 Brush E 1792 6 2.5 51 Alkali silicate 15 Spray E 1793 6 18.9 52 Alkyl silicate 14 Spray E 1794 2 75.9 51 Urethane resin 55 Spray E 1795 7 55.9 52 Alkyl silicate 8 Spray E 1796 2 53.8 89 Urethane resin 122 Brush E 1797 2 97.5 85 Alkyl silicate 54 Spray E 1798 6 88.4 82 Alkali silicate 19 Spray E 1799 7 54.8 87 Alkyl silicate 25 Brush E 1800 7 45.7 88 Alkyl silicate 58 Spray E 1801 6 34.7 49 Alkyl silicate 21 Spray E

TABLE 93 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1802 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 1803 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 1804 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 1805 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 1806 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 1807 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 1808 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 1809 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 1810 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 1811 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 1812 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 1813 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 1814 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 1815 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 1816 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 1817 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 1818 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 1819 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 1820 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 1821 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Number fine metal content Coat Invention of grains of coat thickness Coating Example No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1802 7 57.9 50 Alkali silicate 19 Brush E 1803 7 65.4 51 Urethane resin 56 Spray E 1804 6 87.9 52 Alkyl silicate 77 Spray E 1805 7 2.9 53 Alkyl silicate 12 Spray E 1806 2 12.8 88 Alkyl silicate 64 Spray E 1807 7 53.8 85 Alkyl silicate 34 Brush E 1808 7 17.8 83 Alkali silicate 28 Spray E 1809 2 34.7 81 Urethane resin 109 Brush E 1810 6 55.7 80 Alkyl silicate 15 Spray E 1811 6 64.5 47 Alkyl silicate 14 Spray E 1812 7 68.9 49 Alkyl silicate 18 Spray E 1813 7 64.7 50 Urethane resin 122 Brush E 1814 6 77.9 51 Alkyl silicate 54 Spray E 1815 7 43.7 52 Alkali silicate 19 Spray E 1816 2 7.8 83 Alkyl silicate 25 Brush E 1817 2 16.0 88 Alkyl silicate 58 Spray E 1818 6 89.6 85 Alkyl silicate 21 Spray E 1819 7 11.8 83 Alkali silicate 19 Brush E 1820 6 4.6 82 Urethane resin 56 Spray E 1821 2 2.5 47 Alkyl silicate 77 Spray E

TABLE 94 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1822 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 1823 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 1824 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 1825 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 1826 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 1827 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 1828 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 1829 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 1830 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 1831 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 1832 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 1833 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 1834 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 1835 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 1836 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 1837 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 1838 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 1839 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 1840 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 1841 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1822 2 18.9 46 Alkyl silicate 54 Spray E 1823 7 75.9 49 Alkali silicate 2 Spray G 1824 6 55.9 50 Alkali silicate 20 Spray E 1825 7 53.8 51 Alkali silicate 5 Spray G 1826 7 97.5 83 Alkyl silicate 20 Spray E 1827 6 88.4 82 Alkali silicate 15 Brush E 1828 2 54.8 88 Alkyl silicate 57 Brush E 1829 7 45.7 85 Alkali silicate 13 Brush E 1830 2 34.7 86 Alkyl silicate 22 Brush E 1831 2 57.9 47 Alkali silicate 20 Spray E 1832 7 65.4 48 Alkyl silicate 27 Spray E 1833 2 87.9 50 Alkali silicate 15 Spray E 1834 7 2.9 51 Alkyl silicate 35 Spray E 1835 2 12.6 52 Alkali silicate 34 Brush E 1836 6 53.8 88 Alkyl silicate 45 Brush E 1837 6 17.8 89 Alkali silicate 52 Brush E 1838 7 34.7 86 Alkyl silicate 23 Brush E 1839 6 76.8 87 Alkali silicate 5 Spray E 1840 2 58.9 86 Alkyl silicate 52 Brush E 1841 2 50.8 46 Alkali silicate 150 Brush E

TABLE 95 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1842 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 1843 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 1844 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 1845 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 1846 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 1847 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 1848 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 1849 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 1850 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 1851 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 1852 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 1853 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 1854 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 1855 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 1856 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 1857 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 1858 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 1859 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 1860 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 1861 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1842 2 46.8 49 Alkyl silicate 60 Brush E 1843 2 23.7 35 Alkali silicate 15 Spray E 1844 2 53.8 37 Alkyl silicate 24 Spray E 1845 2 53.8 36 Alkali silicate 34 Spray E 1846 6 43.7 38 Alkyl silicate 20 Brush E 1847 6 55.9 48 Alkali silicate 200 Brush E 1848 7 65.8 46 Alkyl silicate 56 Brush E 1849 6 55.7 51 Alkali silicate 34 Spray E 1850 2 64.5 46 Alkyl silicate 2 Spray G 1851 7 68.9 38 Alkali silicate 15 Spray E 1852 2 64.7 48 Alkali silicate 10 Spray E 1853 6 77.9 52 Alkyl silicate 125 Brush E 1854 6 43.7 30 Alkali silicate 24 Brush E 1855 2 7.8 76 Alkyl silicate 110 Brush E 1856 2 16.0 72 Alkali silicate 24 Brush E 1857 7 89.6 81 Alkyl silicate 2 Spray G 1858 6 11.8 64 Alkali silicate 37 Spray E 1859 7 4.6 69 Alkyl silicate 113 Brush E 1860 2 2.5 83 Alkali silicate 2 Spray G 1861 7 18.9 30 Alkyl silicate 75 Brush E

TABLE 96 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1862 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 1863 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 1864 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 1865 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 1866 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 1867 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 1868 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 1869 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 1870 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 1871 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 1872 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 1873 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 1874 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 1875 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 1876 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 1877 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 1878 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 1879 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 1880 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 1881 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1862 6 75.9 83 Alkali silicate 30 Brush E 1863 7 55.9 75 Alkyl silicate 34 Brush E 1864 6 53.8 76 Epoxy resin 124 Brush E 1865 7 97.5 72 Acrylic resin 15 Spray E 1866 6 88.4 71 Urethane resin 23 Spray E 1867 2 54.8 82 Polyester resin 157 Brush E 1868 7 45.7 81 Epoxy resin 26 Spray E 1869 6 34.7 83 Acrylic resin 38 Spray E 1870 6 57.9 50 Urethane resin 160 Brush E 1871 6 65.4 72 Polyester resin 27 Brush E 1872 2 87.9 47 Epoxy resin 180 Brush E 1873 6 2.9 47 Acrylic resin 26 Spray E 1874 7 12.6 52 Urethane resin 180 Brush E 1875 2 53.8 52 Polyester resin 15 Spray E 1876 6 17.8 50 Epoxy resin 2 Spray G 1877 2 34.7 46 Acrylic resin 28 Spray E 1878 6 55.7 47 Urethane resin 30 Spray E 1879 7 64.5 83 Polyester resin 2 Spray G 1880 7 68.9 52 Epoxy resin 157 Brush E 1881 2 64.7 89 Acrylic resin 28 Brush E

TABLE 97 Percent Diameter of fine- distribution grain (Ave metal Mg solid diameter) of grains Alloy solution phase Any of Zn metal among Zn Chemical component grain and Zn—Mg MgZn2, grains/Zn metal content of Zn metal fracture intermetallic Mg2Zn11, alloy grains grains/ grains/Zn alloy surfaces compounds Mg2Zn3, Invention (μm) Zn alloy grains or Ave present on MgZn, Example Fine Coarse grains (Mass %) cracks aspect grain Mg7Zn3 No metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 1882 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 1883 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 1884 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 1885 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 1886 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 1887 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 1888 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 1889 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 1890 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 1891 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 1892 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 1893 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 1894 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 1895 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 1896 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 1897 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 1898 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 1899 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 1900 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 1901 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes Coating details Ratio of fine metal grains in coat outermost surface layer 10% Total thickness metal to total grain Invention Number fine metal content Coat Example of grains of coat thickness Coating No faces (Mass %) (Mass %) Base resin type (μm) method Corrosion Test Results 1882 2 77.9 85 Alkyl silicate 130 Brush E 1883 6 43.7 53 Alkyl silicate 29 Brush E 1884 7 7.8 88 Epoxy resin 30 Brush E 1885 6 16.0 85 Acrylic resin 120 Brush E 1886 7 89.6 52 Urethane resin 187 Brush E 1887 6 11.8 83 Polyester resin 28 Spray E 1888 2 4.6 88 Epoxy resin 5 Spray E 1889 2 2.5 49 Acrylic resin 35 Spray E 1890 6 18.9 50 Urethane resin 5 Spray G 1891 7 75.9 51 Polyester resin 200 Brush E 1892 6 55.9 83 Alkali silicate 25 Spray E 1893 6 53.8 82 Alkali silicate 15 Spray E 1894 2 97.5 88 Alkyl silicate 20 Spray E 1895 7 88.4 85 Alkali silicate 18 Spray E 1896 2 54.8 87 Alkyl silicate 22 Spray E 1897 2 45.7 86 Alkali silicate 19 Spray E 1898 6 34.7 46 Alkyl silicate 29 Spray E 1899 7 57.9 49 Alkali silicate 23 Spray E 1900 7 65.4 35 Alkyl silicate 21 Spray E 1901 6 87.9 30 Alkali silicate 19 Spray E

TABLE 98 Percent of fine- Diameter grain distribution metal Mg solid (Ave grains Alloy solution phase diameter) of among Zn Chemical component grain and Zn—Mg Zn metal metal content of Zn metal fracture intermetallic alloy grains grains/ grains/Zn alloy surfaces compounds Invention (μm) Zn alloy grains or present on Example Fine Coarse grains (Mass %) cracks grain No metal metal (Vol %) Zn Mg Al Si present? Ave aspect ratio surfaces? 1902 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes 1903 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes 1904 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes 1905 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes 1906 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes 1907 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes 1908 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes 1909 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes 1910 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes 1911 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes 1912 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes 1913 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes 1914 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes 1915 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes 1916 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes 1917 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes 1918 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes 1919 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes 1920 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes 1921 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes 1922 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Yes Coating details Ratio of fine metal grains in coat outermost Any of surface MgZn2, layer 10% Total Mg2Zn11, thickness metal Mg2Zn3, to total grain Invention MgZn, Number fine metal content Coat Example Mg7Zn3, of grains of coat thickness Coating Corrosion No present? faces (Mass %) (Mass %) Base resin type (μm) method Test Results 1902 Yes 7 2.9 76 Alkyl silicate 15 Spray E 1903 Yes 7 12.6 72 Alkali silicate 18 Spray E 1904 Yes 6 53.8 30 Alkyl silicate 22 Spray E 1905 Yes 7 17.8 83 Alkyl silicate 21 Spray E 1906 Yes 2 34.7 75 Alkyl silicate 29 Spray E 1907 Yes 7 76.8 76 Alkali silicate 23 Spray E 1908 Yes 7 58.9 72 Alkyl silicate 21 Spray E 1909 Yes 2 50.8 83 Alkali silicate 19 spray E 1910 Yes 6 46.8 50 Alkyl silicate 21 Spray E 1911 Yes 6 23.7 72 Alkali silicate 19 Spray E 1912 Yes 2 87.9 50 Acrylic resin 654 Spray E 1913 Yes 6 2.9 48 Alkali silicate 700 Spray E 1914 Yes 7 12.6 75 Alkyl silicate 555 Spray E 1915 Yes 7 53.8 55 Alkyl silicate 321 Spray E 1916 Yes 6 17.8 38 Alkyl silicate 152 Brush E 1917 Yes 7 34.7 48 Urethane resin 674 Spray E 1918 Yes 7 76.8 76 Polyester resin 325 Spray E 1919 Yes 6 58.9 72 Alkyl silicate 665 Spray E 1920 Yes 7 50.8 75 Alkyl silicate 354 Brush E 1921 Yes 6 46.8 76 Alkyl silicate 165 Spray E 1922 Yes 7 23.7 72 Urethane resin 354 Spray E

TABLE 99 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks No (μm) metal metal (Vol %) Zn Mg Al Si present? Ave aspect ratio 1923 23.5 2.65 9.56 5.66 100 0 0 0 No — 1924 5.96 0.05 6.5 16.55 100 0 0 0 No — 1925 10.64 4.6 65.5 21.55 100 0 0 0 No — 1926 16.5 3.56 13.5 5.66 100 0 0 0 No — 1927 7.95 4.55 16.7 33.66 100 0 0 0 No — 1928 7.95 2.15 9.89 45.65 100 0 0 0 No — 1929 9.64 3.22 10.55 49.88 100 0 0 0 No — 1930 0.96 2.99 9.64 42.33 100 0 0 0 No — 1931 5.26 3.65 11.22 65.44 100 0 0 0 No — 1932 13.5 4.55 13.5 77.55 100 0 0 0 No — 1933 13.5 3.57 22.5 96.55 100 0 0 0 No — 1934 9.64 1.99 8.56 5.97 100 0 0 0 No — 1935 16.5 2.12 9.46 87.77 100 0 0 0 No — 1936 20.59 2.45 11.1 86.55 100 0 0 0 No — 1937 0.96 1.85 8.92 15.67 100 0 0 0 No — 1938 6.54 1.65 9.23 31.55 100 0 0 0 No — 1939 5.26 2.45 9.05 26.76 100 0 0 0 No — 1940 10.64 2.01 10.91 67.89 100 0 0 0 No — 1941 9.64 1.99 11.12 56.89 100 0 0 0 No — 1942 6.9 2.38 10.93 45.67 100 0 0 0 No — 1943 10.5 2.49 9.34 34.67 100 0 0 0 No — Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 1923 1 299.5 — 35 Alkali silicate 2 Spray G 1924 1 12.5 — 66 Alkyl silicate 37 Spray E 1925 1 3.5 — 38 Alkali silicate 12 Spray E 1926 1 1.4 — 84 Alkyl silicate 160 Brush E 1927 1 6.8 — 39 Alkali silicate 5 Brush G 1928 1 136.5 — 85 Alkyl silicate 12 Brush E 1929 1 14.5 — 36 Alkali silicate 2 Spray G 1930 1 0.08 — 56 Alkyl silicate 18 Spray E 1931 1 1.6 — 42 Alkyl silicate 23 Spray E 1932 1 3.9 — 31 Epoxy resin 30 Brush E 1933 1 10.5 — 88 Acrylic resin 77 Brush E 1934 1 4.9 — 78 Urethane resin 254 Brush E 1935 1 33.5 — 36 Polyester resin 47 Spray E 1936 1 2.5 — 37 Epoxy resin 43 Spray E 1937 1 1.9 — 45 Acrylic resin 322 Brush E 1938 1 7.1 — 68 Urethane resin 20 Brush E 1939 1 9.4 — 79 Polyester resin 700 Brush E 1940 1 16.8 — 47 Alkali silicate 22 Spray E 1941 1 75.5 — 56 Alkyl silicate 25 Spray E 1942 1 4.5 — 37 Alkali silicate 14 Spray E 1943 1 0.9 — 90 Urethane resin 112 Spray E

TABLE 100 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn Alloy of later- grains/Zn metal Chemical component grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks No (μm) metal metal (Vol %) Zn Mg Al Si present? Ave aspect ratio 1944 13.5 2.34 8.77 95.66 100 0 0 0 No — 1945 20.59 3.99 27.6 34.21 100 0 0 0 No — 1946 7.82 1.02 21.9 7.88 100 0 0 0 No — 1947 5.26 0.05 22.5 92.32 100 0 0 0 No — 1948 7.06 2.01 17.5 11.22 100 0 0 0 No — 1949 0.64 1.51 6.99 55.66 100 0 0 0 No — 1950 46.8 2.38 7.65 78.99 100 0 0 0 No — 1951 9.64 1.99 8.56 5.97 100 0 0 0 No — 1952 16.5 2.49 9.34 34.67 100 0 0 0 No — 1953 20.59 1.02 21.9 7.88 100 0 0 0 No — 1954 16.5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 1955 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 1956 0.96 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 1957 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 1958 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 1959 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 1960 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 1961 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 1962 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 1963 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 1964 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 1944 1 3.2 — 43 Alkali silicate 554 Spray E 1945 1 5.2 — 38 Urethane resin 150 Spray E 1946 1 1.6 — 56 Alkali silicate 18 Spray E 1947 1 85.5 — 89 Alkyl silicate 657 Brush E 1948 1 52.2 — 32 Alkyl silicate 24 Spray E 1949 1 3.6 — 55 Urethane resin 99 Spray E 1950 1 1.7 — 79 Alkyl silicate 7 Spray E 1951 1 4.9 — 78 Epoxy resin 100 Spray E 1952 1 33.5 — 77 Alkyl silicate 27 Brush E 1953 1 2.5 — 56 Alkali silicate 15 Spray E 1954 1 5 1.867 49 Alkyl silicate 14 Spray E 1955 1 198.7 0.047 89 Urethane resin 55 Spray E 1956 1 36 0.500 90 Alkyl silicate 8 Spray E 1957 1 1.5 0.012 86 Urethane resin 122 Brush E 1958 1 0.008 1.587 48 Alkyl silicate 555 Spray E 1959 1 1.4 2.833 47 Alkali silicate 19 Spray E 1960 1 4.2 2.673 47 Alkyl silicate 25 Brush E 1961 1 1.6 0.731 47 Alkyl silicate 58 Spray E 1962 1 7.5 0.671 52 Alkyl silicate 685 Spray E 1963 1 1.6 3.538 52 Alkali silicate 19 Brush E 1964 1 2 5.133 52 Urethane resin 700 Spray E

TABLE 101 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 1965 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 1966 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 1967 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 1968 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 1969 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 1970 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 1971 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 1972 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 1973 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 1974 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 1975 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 1976 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 1977 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 1978 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 1979 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 1980 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 1981 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 1982 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 1983 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 1984 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 1985 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 1965 1 270 0.069 88 Alkyl silicate 77 Spray E 1966 1 7.5 0.424 87 Alkyl silicate 54 Spray E 1967 1 2.9 1.385 89 Alkyl silicate 64 Spray E 1968 1 2.6 2.111 90 Alkyl silicate 34 Brush E 1969 1 0.1 22.273 91 Alkali silicate 28 Spray E 1970 1 1.2 8.000 46 Urethane resin 109 Brush E 1971 1 1.2 0.636 47 Alkyl silicate 15 Spray E 1972 1 62 0.341 47 Alkyl silicate 14 Spray E 1973 1 2.4 3.059 49 Alkyl silicate 18 Spray E 1974 1 2.1 4.129 50 Alkali silicate 2 Spray G 1975 1 34.5 0.220 87 Alkyl silicate 37 Spray E 1976 1 270 0.109 83 Alkali silicate 12 Spray E 1977 1 32.5 0.254 48 Alkyl silicate 160 Brush E 1978 1 3 6.375 51 Alkali silicate 5 Brush G 1979 1 1.5 0.028 51 Alkyl silicate 56 Brush E 1980 1 7.5 1.271 87 Alkali silicate 2 Spray G 1981 1 13.5 0.772 85 Alkyl silicate 18 Spray E 1982 1 5 4.083 86 Alkyl silicate 23 Spray E 1983 1 5 2.900 50 Epoxy resin 30 Brush E 1984 1 1 0.650 51 Acrylic resin 77 Brush E 1985 1 120 0.161 51 Urethane resin 655 Brush E

TABLE 102 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 1986 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 1987 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 1988 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 1989 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 1990 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 1991 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 1992 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 1993 16.5 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 1994 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 1995 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 1996 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 1997 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 1998 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 1999 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 2000 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 2001 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 2002 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 2003 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 2004 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 2005 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 2006 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 1986 1 3.7 2.298 80 Polyester resin 47 Spray E 1987 1 6.1 1.676 46 Epoxy resin 43 Spray E 1988 1 198.5 0.048 51 Acrylic resin 52 Brush E 1989 1 2.5 3.000 86 Urethane resin 20 Brush E 1990 1 18.5 0.774 85 Polyester resin 200 Brush E 1991 1 8 1.867 82 Alkali silicate 22 Spray E 1992 1 1.6 4.077 81 Alkyl silicate 25 Spray E 1993 1 1.2 6.045 46 Alkali silicate 14 Spray E 1994 1 0.5 0.933 47 Urethane resin 112 Spray E 1995 1 9 2.350 48 Alkali silicate 24 Spray E 1996 1 4.5 1.618 51 Urethane resin 150 Spray E 1997 1 136 0.109 53 Alkali silicate 18 Spray E 1998 1 13 1.314 88 Alkyl silicate 19 Brush E 1999 1 10.6 0.181 85 Alkyl silicate 24 Spray E 2000 1 1.6 2.000 83 Urethane resin 99 Spray E 2001 1 68 0.223 82 Alkyl silicate 7 Spray E 2002 1 4.5 1.945 83 Epoxy resin 100 Spray E 2003 1 10.5 1.452 47 Alkyl silicate 27 Brush E 2004 1 4.9 3.322 51 Alkali silicate 15 Spray E 2005 1 10.5 1.261 52 Alkyl silicate 14 Spray E 2006 1 192 0.074 51 Urethane resin 55 Spray E

TABLE 103 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2007 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 2008 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 2009 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 2010 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 2011 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 2012 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 2013 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 2014 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 2015 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 2016 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 2017 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 2018 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 2019 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 2020 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 2021 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 2022 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 2023 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 2024 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 2025 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 2026 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 2027 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2007 1 0.07 11.869 52 Alkyl silicate 8 Spray E 2008 1 9.5 1.000 89 Urethane resin 122 Brush E 2009 1 2.6 3.278 85 Alkyl silicate 54 Spray E 2010 1 4.5 2.327 82 Alkali silicate 19 Spray E 2011 1 3 1.550 87 Alkyl silicate 25 Brush E 2012 1 7.5 1.908 88 Alkyl silicate 58 Spray E 2013 1 77 0.251 49 Alkyl silicate 21 Spray E 2014 1 10.5 1.078 50 Alkali silicate 19 Brush E 2015 1 15.5 0.648 51 Urethane resin 56 Spray E 2016 1 5.8 1.250 52 Alkyl silicate 77 Spray E 2017 1 1.9 1.759 53 Alkyl silicate 12 Spray E 2018 1 16.9 1.369 88 Alkyl silicate 64 Spray E 2019 1 1.5 5.400 85 Alkyl silicate 34 Brush E 2020 1 0.05 19.048 83 Alkali silicate 28 Spray E 2021 1 215 0.072 81 Urethane resin 109 Brush E 2022 1 4.2 2.019 80 Alkyl silicate 15 Spray E 2023 1 1.5 3.160 47 Alkyl silicate 14 Spray E 2024 1 4.8 0.828 49 Alkyl silicate 18 Spray E 2025 1 0.5 12.267 50 Urethane resin 122 Brush E 2026 1 2.3 3.848 51 Alkyl silicate 54 Spray E 2027 1 0.05 9.810 52 Alkali silicate 19 Spray E

TABLE 104 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn Alloy of later- grains/Zn metal Chemical component grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2028 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 2029 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 2030 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 2031 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 2032 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 2033 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 2034 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 2035 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 2036 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 2037 9.64 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 2038 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 2039 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 2040 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 2041 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 2042 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 2043 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 2044 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 2045 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 2046 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 2047 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 2048 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2028 1 120 0.172 83 Alkyl silicate 25 Brush E 2029 1 3.7 0.532 88 Alkyl silicate 58 Spray E 2030 1 16.5 0.869 85 Alkyl silicate 21 Spray E 2031 1 24 0.768 83 Alkali silicate 19 Brush E 2032 1 0.01 13.366 82 Urethane resin 56 Spray E 2033 1 7.8 1.352 47 Alkyl silicate 77 Spray E 2034 1 1.6 4.077 46 Alkyl silicate 54 Spray E 2035 1 3.2 3.667 49 Alkali silicate 2 Spray G 2036 1 5.4 0.406 50 Alkali silicate 20 Spray E 2037 1 220 0.076 51 Alkali silicate 5 Spray G 2038 1 2.2 2.531 83 Alkyl silicate 20 Spray E 2039 1 2.8 3.605 82 Alkali silicate 15 Brush E 2040 1 12 1.423 88 Alkyl silicate 57 Brush E 2041 1 10.6 0.207 85 Alkali silicate 13 Brush E 2042 1 35 0.303 86 Alkyl silicate 22 Brush E 2043 1 125.5 0.057 47 Alkali silicate 20 Spray E 2044 1 6 2.500 48 Alkyl silicate 27 Spray E 2045 1 34 0.417 50 Alkali silicate 15 Spray E 2046 1 1.6 3.615 51 Alkyl silicate 35 Spray E 2047 1 7.5 0.835 52 Alkali silicate 34 Brush E 2048 1 200 0.112 88 Alkyl silicate 45 Brush E

TABLE 105 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2049 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 2050 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 2051 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 2052 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 2053 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 2054 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 2055 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 2056 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 2057 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 2058 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 2059 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 2060 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 2061 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 2062 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 2063 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 2064 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 2065 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 2066 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 2067 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 2068 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 2069 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2049 1 7.5 1.612 89 Alkali silicate 52 Brush E 2050 1 3.2 3.071 86 Alkyl silicate 23 Brush E 2051 1 2.6 1.194 87 Alkali silicate 5 Spray E 2052 1 3 4.400 86 Alkyl silicate 52 Brush E 2053 1 15.2 0.037 46 Alkali silicate 150 Brush E 2054 1 0.09 9.450 49 Alkyl silicate 60 Brush E 2055 1 13.5 0.483 35 Alkali silicate 15 Spray E 2056 1 135.4 0.172 37 Alkyl silicate 24 Spray E 2057 1 3 4.375 36 Alkali silicate 34 Spray E 2058 1 7.8 1.409 38 Alkyl silicate 20 Brush E 2059 1 10.2 1.330 48 Alkali silicate 200 Brush E 2060 1 7 2.588 46 Alkyl silicate 56 Brush E 2061 1 225.2 0.038 51 Alkali silicate 34 Spray E 2062 1 5.4 2.219 46 Alkyl silicate 2 Spray G 2063 1 3.2 0.019 38 Alkali silicate 15 Spray E 2064 1 13.5 1.048 48 Alkali silicate 10 Spray E 2065 1 1.6 6.692 52 Alkyl silicate 125 Brush E 2066 1 1.5 0.320 30 Alkali silicate 24 Brush E 2067 1 2.5 1.829 76 Alkyl silicate 110 Brush E 2068 1 2.6 0.889 72 Alkali silicate 24 Brush E 2069 1 126 0.072 81 Alkyl silicate 2 Spray G

TABLE 106 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2070 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 2071 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 2072 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 2073 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 2074 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 2075 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 2076 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 2077 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 2078 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 2079 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 2080 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 2081 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 2082 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 2083 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 2084 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 2085 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 2086 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 2087 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 2088 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 2089 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 2090 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2070 1 120 0.159 64 Alkali silicate 37 Spray E 2071 1 7.5 1.776 69 Alkyl silicate 113 Brush E 2072 1 6.5 1.933 83 Alkali silicate 2 Spray G 2073 1 20 0.500 30 Alkyl silicate 75 Brush E 2074 1 0.007 7.448 83 Alkali silicate 30 Brush E 2075 1 9 0.610 75 Alkyl silicate 34 Brush E 2076 1 7.5 1.976 76 Epoxy resin 124 Brush E 2077 1 50 0.539 72 Acrylic resin 15 Spray E 2078 1 0.005 2.886 71 Urethane resin 23 Spray E 2079 1 25.6 0.169 82 Polyester resin 157 Brush E 2080 1 56.5 0.001 81 Epoxy resin 26 Spray E 2081 1 1.6 1.192 83 Acrylic resin 38 Spray E 2082 1 3 5.125 50 Urethane resin 160 Brush E 2083 1 100 0.292 72 Polyester resin 27 Brush E 2084 1 65.5 0.114 47 Epoxy resin 180 Brush E 2085 1 1.9 0.241 47 Acrylic resin 26 Spray E 2086 1 2.1 1.484 52 Urethane resin 180 Brush E 2087 1 10.5 0.722 52 Polyester resin 15 Spray E 2088 1 6.5 1.573 50 Epoxy resin 2 Spray G 2089 1 19.5 0.629 46 Acrylic resin 28 Spray E 2090 1 0.8 0.333 47 Urethane resin 30 Spray E

TABLE 107 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2091 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 2092 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 2093 16.5 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 2094 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 2095 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 2096 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 2097 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 2098 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 2099 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 2100 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 2101 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 2102 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 2103 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 2104 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 2105 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 2106 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 2107 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 2108 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 2109 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 2110 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 2111 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 2112 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2091 1 18.5 0.487 83 Polyester resin 2 Spray G 2092 1 4.3 2.208 52 Epoxy resin 157 Brush E 2093 1 3.2 2.238 89 Acrylic resin 28 Brush E 2094 1 1.5 4.680 85 Alkyl silicate 130 Brush E 2095 1 4.5 0.764 53 Alkyl silicate 29 Brush E 2096 1 15.5 0.170 88 Epoxy resin 30 Brush E 2097 1 10.5 1.209 85 Acrylic resin 120 Brush E 2098 1 2.5 4.171 52 Urethane resin 187 Brush E 2099 1 9 2.640 83 Polyester resin 28 Spray E 2100 1 105 0.156 88 Epoxy resin 5 Spray E 2101 1 5.7 2.910 49 Acrylic resin 35 Spray E 2102 1 3.9 0.327 50 Urethane resin 5 Spray G 2103 1 4.5 1.091 51 Polyester resin 200 Brush E 2104 1 3.6 1.826 83 Alkali silicate 25 Spray E 2105 1 16.4 0.764 82 Alkali silicate 15 Spray E 2106 1 6 2.657 88 Alkyl silicate 20 Spray E 2107 1 7.5 0.212 85 Alkali silicate 18 Spray E 2108 1 10.5 0.357 87 Alkyl silicate 22 Spray E 2109 1 2.6 4.639 86 Alkali silicate 19 Spray E 2110 1 1.5 0.160 46 Alkyl silicate 29 Spray E 2111 1 13.5 0.731 49 Alkali silicate 23 Spray E 2112 1 2.6 1.917 35 Alkyl silicate 21 Spray E

TABLE 108 Percent Diameter of fine- distribution grain (peak metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2113 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 2114 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 2115 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 2116 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 2117 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 2118 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 2119 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 2120 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 2121 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 2122 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 2123 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 2124 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 2125 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 2126 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 2127 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 2128 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 2129 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 2130 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 2131 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 2132 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 2133 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 2134 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2113 1 6.5 0.007 30 Alkali silicate 19 Spray E 2114 1 1.6 2.462 76 Alkyl silicate 15 Spray E 2115 1 3.8 0.729 72 Alkali silicate 18 Spray E 2116 1 0.08 16.204 30 Alkyl silicate 22 Spray E 2117 1 164.5 0.022 83 Alkyl silicate 21 Spray E 2118 1 3.6 1.283 75 Alkyl silicate 29 Spray E 2119 1 8.6 1.688 76 Alkali silicate 23 Spray E 2120 1 12 1.731 72 Alkyl silicate 21 Spray E 2121 1 5.8 0.500 83 Alkali silicate 19 Spray E 2122 1 10 2.409 50 Alkyl silicate 21 Spray E 2123 1 1 12.750 72 Alkali silicate 19 Spray E 2124 1 10.5 1.113 50 Acrylic resin 654 Spray E 2125 1 6.5 1.133 48 Alkali silicate 700 Spray E 2126 1 19.5 1.195 75 Alkyl silicate 555 Spray E 2127 1 0.8 10.222 55 Alkyl silicate 321 Spray E 2128 1 5.3 0.013 38 Alkyl silicate 152 Brush E 2129 1 4.3 2.868 48 Urethane resin 674 Spray E 2130 1 3.2 1.524 76 Polyester resin 325 Spray E 2131 1 1.5 1.280 72 Alkyl silicate 665 Spray E 2132 1 4.5 1.109 75 Alkyl silicate 354 Brush E 2133 1 0.8 9.333 76 Alkyl silicate 165 Spray E 2134 1 6.5 3.667 72 Urethane resin 354 Spray E

TABLE 109 Percent Diameter of fine- distribution grain (Ave metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks No (μm) metal metal (Vol %) Zn Mg Al Si present? Ave aspect ratio 2135 23.5 2.65 9.56 5.66 100 0 0 0 No — 2136 5.96 0.05 6.5 16.55 100 0 0 0 No — 2137 10.64 4.6 65.5 21.55 100 0 0 0 No — 2138 16.5 3.56 13.5 5.66 100 0 0 0 No — 2139 7.95 4.55 16.7 33.66 100 0 0 0 No — 2140 7.95 2.15 9.89 45.65 100 0 0 0 No — 2141 9.64 3.22 10.55 49.88 100 0 0 0 No — 2142 0.96 2.99 9.64 42.33 100 0 0 0 No — 2143 5.26 3.65 11.22 65.44 100 0 0 0 No — 2144 13.5 4.55 13.5 77.55 100 0 0 0 No — 2145 13.5 3.57 22.5 96.55 100 0 0 0 No — 2146 9.64 1.99 8.56 5.97 100 0 0 0 No — 2147 16.5 2.12 9.46 87.77 100 0 0 0 No — 2148 20.59 2.45 11.1 86.55 100 0 0 0 No — 2149 0.96 1.85 8.92 15.67 100 0 0 0 No — 2150 6.54 1.65 9.23 31.55 100 0 0 0 No — 2151 5.26 2.45 9.05 26.76 100 0 0 0 No — 2152 10.64 2.01 10.91 67.89 100 0 0 0 No — 2153 9.64 1.99 11.12 56.89 100 0 0 0 No — 2154 6.9 2.38 10.93 45.67 100 0 0 0 No — 2155 10.5 2.49 9.34 34.67 100 0 0 0 No — Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2135 1 299.5 — 35 Alkali silicate 2 Spray G 2136 1 12.5 — 66 Alkyl silicate 37 Spray E 2137 1 3.5 — 38 Alkali silicate 12 Spray E 2138 1 1.4 — 84 Alkyl silicate 160 Brush E 2139 1 6.8 — 39 Alkali silicate 5 Brush G 2140 1 136.5 — 85 Alkyl silicate 12 Brush E 2141 1 14.5 — 36 Alkali silicate 2 Spray G 2142 1 0.08 — 56 Alkyl silicate 18 Spray E 2143 1 1.6 — 42 Alkyl silicate 23 Spray E 2144 1 3.9 — 31 Epoxy resin 30 Brush E 2145 1 10.5 — 88 Acrylic resin 77 Brush E 2146 1 4.9 — 78 Urethane resin 254 Brush E 2147 1 33.5 — 36 Polyester resin 47 Spray E 2148 1 2.5 — 37 Epoxy resin 43 Spray E 2149 1 1.9 — 45 Acrylic resin 322 Brush E 2150 1 7.1 — 68 Urethane resin 20 Brush E 2151 1 9.4 — 79 Polyester resin 700 Brush E 2152 1 16.8 — 47 Alkali silicate 22 Spray E 2153 1 75.5 — 56 Alkyl silicate 25 Spray E 2154 1 4.5 — 37 Alkali silicate 14 Spray E 2155 1 0.9 — 90 Urethane resin 112 Spray E

TABLE 110 Percent Diameter of fine- distribution grain (Ave metal Average diameter) of grains diameter Zn metal among Zn Alloy of later- grains/Zn metal Chemical component grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks No (μm) metal metal (Vol %) Zn Mg Al Si present? Ave aspect ratio 2156 13.5 2.34 8.77 95.66 100 0 0 0 No — 2157 20.59 3.99 27.6 34.21 100 0 0 0 No — 2158 7.82 1.02 21.9 7.88 100 0 0 0 No — 2159 5.26 0.05 22.5 92.32 100 0 0 0 No — 2160 7.06 2.01 17.5 11.22 100 0 0 0 No — 2161 0.64 1.51 6.99 55.66 100 0 0 0 No — 2162 46.8 2.38 7.65 78.99 100 0 0 0 No — 2163 9.64 1.99 8.56 5.97 100 0 0 0 No — 2164 16.5 2.49 9.34 34.67 100 0 0 0 No — 2165 20.59 1.02 21.9 7.88 100 0 0 0 No — 2166 16..5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 2167 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 2168 0.96 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 2169 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 2170 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 2171 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 2172 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 2173 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 2174 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 2175 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 2176 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2156 1 3.2 — 43 Alkali silicate 554 Spray E 2157 1 5.2 — 38 Urethane resin 150 Spray E 2158 1 1.6 — 56 Alkali silicate 18 Spray E 2159 1 85.5 — 89 Alkyl silicate 657 Brush E 2160 1 52.2 — 32 Alkyl silicate 24 Spray E 2161 1 3.6 — 55 Urethane resin 99 Spray E 2162 1 1.7 — 79 Alkyl silicate 7 Spray E 2163 1 4.9 — 78 Epoxy resin 100 Spray E 2164 1 33.5 — 77 Alkyl silicate 27 Brush E 2165 1 2.5 — 56 Alkali silicate 15 Spray E 2166 1 5 1.867 49 Alkyl silicate 14 Spray E 2167 1 198.7 0.047 89 Urethane resin 55 Spray E 2168 1 36 0.500 90 Alkyl silicate 8 Spray E 2169 1 1.5 0.012 86 Urethane resin 122 Brush E 2170 1 0.008 1.587 48 Alkyl silicate 555 Spray E 2171 1 1.4 2.833 47 Alkali silicate 19 Spray E 2172 1 4.2 2.673 47 Alkyl silicate 25 Brush E 2173 1 1.6 0.731 47 Alkyl silicate 58 Spray E 2174 1 7.5 0.671 52 Alkyl silicate 685 Spray E 2175 1 1.6 3.538 52 Alkali silicate 19 Brush E 2176 1 2 5.133 52 Urethane resin 700 Spray E

TABLE 111 Percent Diameter of fine- distribution grain (Ave metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2177 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 2178 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 2179 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 2180 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 2181 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 2182 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 2183 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 2184 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 2185 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 2186 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 2187 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 2188 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 2189 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 2190 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 2191 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 2192 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 2193 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 2194 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 2195 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 2196 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 2197 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2177 1 270 0.069 88 Alkyl silicate 77 Spray E 2178 1 7.5 0.424 87 Alkyl silicate 54 Spray E 2179 1 2.9 1.385 89 Alkyl silicate 64 Spray E 2180 1 2.6 2.111 90 Alkyl silicate 34 Brush E 2181 1 0.1 22.273 91 Alkali silicate 28 Spray E 2182 1 1.2 8.000 46 Urethane resin 109 Brush E 2183 1 1.2 0.636 47 Alkyl silicate 15 Spray E 2184 1 62 0.341 47 Alkyl silicate 14 Spray E 2185 1 2.4 3.059 49 Alkyl silicate 18 Spray E 2186 1 2.1 4.129 50 Alkali silicate 2 Spray G 2187 1 34.5 0.220 87 Alkyl silicate 37 Spray E 2188 1 270 0.109 83 Alkali silicate 12 Spray E 2189 1 32.5 0.254 48 Alkyl silicate 160 Brush E 2190 1 3 6.375 51 Alkali silicate 5 Brush G 2191 1 1.5 0.028 51 Alkyl silicate 56 Brush E 2192 1 7.5 1.271 87 Alkali silicate 2 Spray G 2193 1 13.5 0.772 85 Alkyl silicate 18 Spray E 2194 1 5 4.083 86 Alkyl silicate 23 Spray E 2195 1 5 2.900 50 Epoxy resin 30 Brush E 2196 1 1 0.650 51 Acrylic resin 77 Brush E 2197 1 120 0.161 51 Urethane resin 655 Brush E

TABLE 112 Percent Diameter of fine- distribution grain (Ave metal Average diameter) of grains diameter Zn metal among Zn of later- grains/Zn metal Chemical component Alloy grain added Zn alloy grains grains/ content of Zn metal fracture Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Example grains Fine Coarse grains (Mass %) or cracks Ave No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio 2198 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 2199 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 2200 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 2201 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 2202 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 2203 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 2204 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 2205 16.5 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 2206 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 2207 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 2208 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 2209 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 2210 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 2211 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 2212 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 2213 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 2214 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 2215 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 2216 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 2217 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 2218 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Ratio of (Zn metal grains or Zn alloy Coating details grains):(Later-added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat thickness Coating Test No grains grains (Mass %) (Mass %) Base resin type (μm) method Results 2198 1 3.7 2.298 80 Polyester resin 47 Spray E 2199 1 6.1 1.676 46 Epoxy resin 43 Spray E 2200 1 198.5 0.048 51 Acrylic resin 52 Brush E 2201 1 2.5 3.000 86 Urethane resin 20 Brush E 2202 1 18.5 0.774 85 Polyester resin 200 Brush E 2203 1 8 1.867 82 Alkali silicate 22 Spray E 2204 1 1.6 4.077 81 Alkyl silicate 25 Spray E 2205 1 1.2 6.045 46 Alkali silicate 14 Spray E 2206 1 0.5 0.933 47 Urethane resin 112 Spray E 2207 1 9 2.350 48 Alkali silicate 24 Spray E 2208 1 4.5 1.618 51 Urethane resin 150 Spray E 2209 1 136 0.109 53 Alkali silicate 18 Spray E 2210 1 13 1.314 88 Alkyl silicate 19 Brush E 2211 1 10.6 0.181 85 Alkyl silicate 24 Spray E 2212 1 1.6 2.000 83 Urethane resin 99 Spray E 2213 1 68 0.223 82 Alkyl silicate 7 Spray E 2214 1 4.5 1.945 83 Epoxy resin 100 Spray E 2215 1 10.5 1.452 47 Alkyl silicate 27 Brush E 2216 1 4.9 3.322 51 Alkali silicate 15 Spray E 2217 1 10.5 1.261 52 Alkyl silicate 14 Spray E 2218 1 192 0.074 51 Urethane resin 55 Spray E

TABLE 113 Percent Diameter of fine- distribution grain Ratio of (Zn (Ave metal metal grains or Average diameter) of grains Zn alloy grains):(Later- diameter Zn metal among Zn Alloy added of later- grains/Zn metal Chemical component grain Zn metal grains) added Zn alloy grains grains/ content of Zn metal fracture Zn metal Later- Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Ave grains/ added Zn Example grains Fine Coarse grains (Mass %) or cracks aspect Zn alloy metal No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio grains grains 2219 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 1 0.07 2220 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 1 9.5 2221 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 1 2.6 2222 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 1 4.5 2223 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 1 3 2224 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 1 7.5 2225 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 1 77 2226 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 1 10.5 2227 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 1 15.5 2228 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 1 5.8 2229 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 1 1.9 2230 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 1 16.9 2231 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 1 1.5 2232 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 1 0.05 2233 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 1 215 2234 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 1 4.2 2235 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 1 1.5 2236 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 1 4.8 2237 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 1 0.5 2238 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 1 2.3 2239 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 1 0.05 Coating details Mg Total content metal of all grain Invention metal content Coat Example grains of coat thickness Coating Corrosion No (Mass %) (Mass %) Base resin type (μm) method Test Results 2219 11.869 52 Alkyl silicate 8 Spray E 2220 1.000 89 Urethane resin 122 Brush E 2221 3.278 85 Alkyl silicate 54 Spray E 2222 2.327 82 Alkali silicate 19 Spray E 2223 1.550 87 Alkyl silicate 25 Brush E 2224 1.906 88 Alkyl silicate 58 Spray E 2225 0.251 49 Alkyl silicate 21 Spray E 2226 1.078 50 Alkali silicate 19 Brush E 2227 0.648 51 Urethane resin 56 Spray E 2228 1.250 52 Alkyl silicate 77 Spray E 2229 1.759 53 Alkyl silicate 12 Spray E 2230 1.369 88 Alkyl silicate 64 Spray E 2231 5.400 85 Alkyl silicate 34 Brush E 2232 19.048 83 Alkali silicate 28 Spray E 2233 0.072 81 Urethane resin 109 Brush E 2234 2.019 80 Alkyl silicate 15 Spray E 2235 3.160 47 Alkyl silicate 14 Spray E 2236 0.828 49 Alkyl silicate 18 Spray E 2237 12.267 50 Urethane resin 122 Brush E 2238 3.848 51 Alkyl silicate 54 Spray E 2239 9.810 52 Alkali silicate 19 Spray E

TABLE 114 Percent Diameter of fine- distribution grain Ratio of (Zn (Ave metal metal grains or Average diameter) of grains Zn alloy grains):(Later- diameter Zn metal among Zn Alloy added of later- grains/Zn metal Chemical component grain Zn metal grains) added Zn alloy grains grains/ content of Zn metal fracture Zn metal Later- Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Ave grains/ added Zn Example grains Fine Coarse grains (Mass %) or cracks aspect Zn alloy metal No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio grains grains 2240 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 1 120 2241 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 1 3.7 2242 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 1 16.5 2243 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 1 24 2244 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 1 0.01 2245 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 1 7.8 2246 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 1 1.6 2247 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 1 3.2 2248 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 1 5.4 2249 9.64 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 1 220 2250 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 1 2.2 2251 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 1 2.8 2252 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 1 12 2253 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 1 10.6 2254 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 1 35 2255 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 1 125.5 2256 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 1 6 2257 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 1 34 2258 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 1 1.6 2259 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 1 7.5 2260 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 1 200 Coating details Mg Total content metal of all grain Invention metal content Coat Example grains of coat thickness Coating Corrosion No (Mass %) (Mass %) Base resin type (μm) method Test Results 2240 0.172 83 Alkyl silicate 25 Brush E 2241 0.532 88 Alkyl silicate 58 Spray E 2242 0.869 85 Alkyl silicate 21 Spray E 2243 0.768 83 Alkali silicate 19 Brush E 2244 13.366 82 Urethane resin 56 Spray E 2245 1.352 47 Alkyl silicate 77 Spray E 2246 4.077 46 Alkyl silicate 54 Spray E 2247 3.667 49 Alkali silicate 2 Spray G 2248 0.406 50 Alkali silicate 20 Spray E 2249 0.076 51 Alkali silicate 5 Spray G 2250 2.531 83 Alkyl silicate 20 Spray E 2251 3.605 82 Alkali silicate 15 Brush E 2252 1.423 88 Alkyl silicate 57 Brush E 2253 0.207 85 Alkali silicate 13 Brush E 2254 0.303 86 Alkyl silicate 22 Brush E 2255 0.057 47 Alkali silicate 20 Spray E 2256 2.500 48 Alkyl silicate 27 Spray E 2257 0.417 50 Alkali silicate 15 Spray E 2258 3.615 51 Alkyl silicate 35 Spray E 2259 0.835 52 Alkali silicate 34 Brush E 2260 0.112 88 Alkyl silicate 45 Brush E

TABLE 115 Percent Diameter of fine- distribution grain Ratio of (Zn (Ave metal metal grains or Average diameter) of grains Zn alloy grains):(Later- diameter Zn metal among Zn Alloy added of later- grains/Zn metal Chemical component grain Zn metal grains) added Zn alloy grains grains/ content of Zn metal fracture Zn metal Later- Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Ave grains/ added Zn Example grains Fine Coarse grains (Mass %) or cracks aspect Zn alloy metal No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio grains grains 2261 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 1 7.5 2262 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 1 3.2 2263 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 1 2.6 2264 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 1 3 2265 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 1 15.2 2266 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 1 0.09 2267 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 1 13.5 2268 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 1 135.4 2269 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 1 3 2270 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 1 7.8 2271 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 1 10.2 2272 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 1 7 2273 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 1 225.2 2274 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 1 5.4 2275 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 1 3.2 2276 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 1 13.5 2277 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 1 1.6 2278 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 1 1.5 2279 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 1 2.5 2280 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 1 2.6 2281 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 1 126 Coating details Mg Total content metal of all grain Invention metal content Coat Example grains of coat thickness Coating Corrosion No (Mass %) (Mass %) Base resin type (μm) method Test Results 2261 1.612 89 Alkali silicate 52 Brush E 2262 3.071 86 Alkyl silicate 23 Brush E 2263 1.194 87 Alkali silicate 5 Spray E 2264 4.400 86 Alkyl silicate 52 Brush E 2265 0.037 46 Alkali silicate 150 Brush E 2266 9.450 49 Alkyl silicate 60 Brush E 2267 0.483 35 Alkali silicate 15 Spray E 2268 0.172 37 Alkyl silicate 24 Spray E 2269 4.375 36 Alkali silicate 34 Spray E 2270 1.409 38 Alkyl silicate 20 Brush E 2271 1.330 48 Alkali silicate 200 Brush E 2272 2.588 46 Alkyl silicate 56 Brush E 2273 0.038 51 Alkali silicate 34 Spray E 2274 2.219 46 Alkyl silicate 2 Spray G 2275 0.019 38 Alkali silicate 15 Spray E 2276 1.048 48 Alkali silicate 10 Spray E 2277 6.692 52 Alkyl silicate 125 Brush E 2278 0.320 30 Alkali silicate 24 Brush E 2279 1.829 76 Alkyl silicate 110 Brush E 2280 0.889 72 Alkali silicate 24 Brush E 2281 0.072 81 Alkyl silicate 2 Spray G

TABLE 116 Percent Diameter of fine- distribution grain Ratio of (Zn (Ave metal metal grains or Average diameter) of grains Zn alloy grains):(Later- diameter Zn metal among Zn Alloy added of later- grains/Zn metal Chemical component grain Zn metal grains) added Zn alloy grains grains/ content of Zn metal fracture Zn metal Later- Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Ave grains/ added Zn Example grains Fine Coarse grains (Mass %) or cracks aspect Zn alloy metal No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio grains grains 2282 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 1 120 2283 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 1 7.5 2284 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 1 6.5 2285 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 1 20 2286 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 1 0.007 2287 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 1 9 2288 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 1 7.5 2289 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 1 50 2290 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 1 0.005 2291 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 1 25.6 2292 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 1 56.5 2293 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 1 1.6 2294 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 1 3 2295 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 1 100 2296 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 1 65.5 2297 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 1 1.9 2298 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 1 2.1 2299 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 1 10.5 2300 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 1 6.5 2301 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 1 19.5 2302 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 1 0.8 Coating details Mg Total content metal of all grain Invention metal content Coat Example grains of coat thickness Coating Corrosion No (Mass %) (Mass %) Base resin type (μm) method Test Results 2282 0.159 64 Alkali silicate 37 Spray E 2283 1.776 69 Alkyl silicate 113 Brush E 2284 1.933 83 Alkali silicate 2 Spray G 2285 0.500 30 Alkyl silicate 75 Brush E 2286 7.448 83 Alkali silicate 30 Brush E 2287 0.610 75 Alkyl silicate 34 Brush E 2288 1.976 76 Epoxy resin 124 Brush E 2289 0.539 72 Acrylic resin 15 Spray E 2290 2.886 71 Urethane resin 23 Spray E 2291 0.169 82 Polyester resin 157 Brush E 2292 0.001 81 Epoxy resin 26 Spray E 2293 1.192 83 Acrylic resin 38 Spray E 2294 5.125 50 Urethane resin 160 Brush E 2295 0.292 72 Polyester resin 27 Brush E 2296 0.114 47 Epoxy resin 180 Brush E 2297 0.241 47 Acrylic resin 26 Spray E 2298 1.484 52 Urethane resin 180 Brush E 2299 0.722 52 Polyester resin 15 Spray E 2300 1.573 50 Epoxy resin 2 Spray G 2301 0.629 46 Acrylic resin 28 Spray E 2302 0.333 47 Urethane resin 30 Spray E

TABLE 117 Percent Diameter of fine- distribution grain Ratio of (Zn (Ave metal metal grains or Average diameter) of grains Zn alloy grains):(Later- diameter Zn metal among Zn Alloy added of later- grains/Zn metal Chemical component grain Zn metal grains) added Zn alloy grains grains/ content of Zn metal fracture Zn metal Later- Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Ave grains/ added Zn Example grains Fine Coarse grains (Mass %) or cracks aspect Zn alloy metal No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio grains grains 2303 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 1 18.5 2304 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 1 4.3 2305 16.5 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 1 3.2 2306 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 1 1.5 2307 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 1 4.5 2308 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 1 15.5 2309 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 1 10.5 2310 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 1 2.5 2311 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 1 9 2312 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 1 105 2313 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 1 5.7 2314 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 1 3.9 2315 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 1 4.5 2316 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 1 3.6 2317 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 1 16.4 2318 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 1 6 2319 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 1 7.5 2320 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 1 10.5 2321 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 1 2.6 2322 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 1 1.5 2323 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 1 13.5 2324 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 1 2.6 Coating details Mg Total content metal of all grain Invention metal content Coat Example grains of coat thickness Coating Corrosion No (Mass %) (Mass %) Base resin type (μm) method Test Results 2303 0.487 83 Polyester resin 2 Spray G 2304 2.208 52 Epoxy resin 157 Brush E 2305 2.238 89 Acrylic resin 28 Brush E 2306 4.680 85 Alkyl silicate 130 Brush E 2307 0.764 53 Alkyl silicate 29 Brush E 2308 0.170 88 Epoxy resin 30 Brush E 2309 1.209 85 Acrylic resin 120 Brush E 2310 4.171 52 Urethane resin 187 Brush E 2311 2.640 83 Polyester resin 28 Spray E 2312 0.156 88 Epoxy resin 5 Spray E 2313 2.910 49 Acrylic resin 35 Spray E 2314 0.327 50 Urethane resin 5 Spray G 2315 1.091 51 Polyester resin 200 Brush E 2316 1.826 83 Alkali silicate 25 Spray E 2317 0.764 82 Alkali silicate 15 Spray E 2318 2.657 88 Alkyl silicate 20 Spray E 2319 0.212 85 Alkali silicate 18 Spray E 2320 0.357 87 Alkyl silicate 22 Spray E 2321 4.639 86 Alkali silicate 19 Spray E 2322 0.160 46 Alkyl silicate 29 Spray E 2323 0.731 49 Alkali silicate 23 Spray E 2324 1.917 35 Alkyl silicate 21 Spray E

TABLE 118 Percent Diameter of fine- distribution grain Ratio of (Zn (Ave metal metal grains or Average diameter) of grains Zn alloy grains):(Later- diameter Zn metal among Zn Alloy added of later- grains/Zn metal Chemical component grain Zn metal grains) added Zn alloy grains grains/ content of Zn metal fracture Zn metal Later- Invention metal (μm) Zn alloy grains/Zn alloy grains surfaces Ave grains/ added Zn Example grains Fine Coarse grains (Mass %) or cracks aspect Zn alloy metal No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio grains grains 2325 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 1 6.5 2326 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 1 1.6 2327 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 1 3.8 2328 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 1 0.08 2329 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 1 164.5 2330 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 1 3.6 2331 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 1 8.6 2332 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 1 12 2333 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 1 5.8 2334 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 1 10 2335 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 1 1 2336 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 1 10.5 2337 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 1 6.5 2338 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 1 19.5 2339 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 1 0.8 2340 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 1 5.3 2341 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 1 4.3 2342 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 1 3.2 2343 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 1 1.5 2344 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 1 4.5 2345 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 1 0.8 2346 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 1 6.5 Coating details Mg Total content metal of all grain Invention metal content Coat Example grains of coat thickness Coating Corrosion No (Mass %) (Mass %) Base resin type (μm) method Test Results 2325 0.007 30 Alkali silicate 19 Spray E 2326 2.462 76 Alkyl silicate 15 Spray E 2327 0.729 72 Alkali silicate 18 Spray E 2328 16.204 30 Alkyl silicate 22 Spray E 2329 0.022 83 Alkyl silicate 21 Spray E 2330 1.283 75 Alkyl silicate 29 Spray E 2331 1.688 76 Alkali silicate 23 Spray E 2332 1.731 72 Alkyl silicate 21 Spray E 2333 0.500 83 Alkali silicate 19 Spray E 2334 2.409 50 Alkyl silicate 21 Spray E 2335 12.750 72 Alkali silicate 19 Spray E 2336 1.113 50 Acrylic resin 654 Spray E 2337 1.133 48 Alkali silicate 700 Spray E 2338 1.195 75 Alkyl silicate 555 Spray E 2339 10.222 55 Alkyl silicate 321 Spray E 2340 0.013 38 Alkyl silicate 152 Brush E 2341 2.868 48 Urethane resin 674 Spray E 2342 1.524 76 Polyester resin 325 Spray E 2343 1.280 72 Alkyl silicate 665 Spray E 2344 1.109 75 Alkyl silicate 354 Brush E 2345 9.333 76 Alkyl silicate 165 Spray E 2346 3.667 72 Urethane resin 354 Spray E

TABLE 119 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2347 16.5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 2348 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 2349 0.96 2.56 9.84 6.55 81.45 18.5 0 0.5 Yes 1.22 Yes Yes 2350 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 2351 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 2352 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 2353 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 2354 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 2355 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 2356 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 2357 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 2358 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 2359 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 2360 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 2361 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 2362 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 2363 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 2364 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 2365 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 2366 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2347 1 5 1.867 49 Alkyl 14 Spray E silicate 2348 1 198.7 0.047 89 Urethane 55 Spray E resin 2349 1 1 9.250 90 Alkyl 8 Spray E silicate 2350 1 1.5 0.012 86 Urethane 122 Brush E resin 2351 1 0.008 1.587 48 Alkyl 555 Spray E silicate 2352 1 1.4 2.833 47 Alkali 19 Spray E silicate 2353 1 4.2 2.673 47 Alkyl 25 Brush E silicate 2354 1 1.6 0.731 47 Alkyl 58 Spray E silicate 2355 1 7.5 0.671 52 Alkyl 685 Spray E silicate 2356 1 1.6 3.538 52 Alkali 19 Brush E silicate 2357 1 2 5.133 52 Urethane 700 Spray E resin 2358 1 270 0.069 88 Alkyl 77 Spray E silicate 2359 1 7.5 0.424 87 Alkyl 54 Spray E silicate 2360 1 2.9 1.385 89 Alkyl 64 Spray E silicate 2361 1 2.6 2.111 90 Alkyl 34 Brush E silicate 2362 1 0.1 22.273 91 Alkali 28 Spray E silicate 2363 1 1.2 8.000 46 Urethane 109 Brush E resin 2364 1 1.2 0.636 47 Alkyl 15 Spray E silicate 2365 1 62 0.341 47 Alkyl 14 Spray E silicate 2366 1 2.4 3.059 49 Alkyl 18 Spray E silicate

TABLE 120 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2367 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 2368 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 2369 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 2370 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 2371 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 2372 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 2373 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 2374 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 2375 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 2376 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 2377 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 2378 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 2379 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 2380 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 2381 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 2382 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 2383 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 2384 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 2385 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 2386 16.5 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2367 1 2.1 4.129 50 Alkali 2 Spray G silicate 2368 1 34.5 0.220 87 Alkyl 37 Spray E silicate 2369 1 270 0.109 83 Alkali 12 Spray E silicate 2370 1 32.5 0.254 48 Alkyl 160 Brush E silicate 2371 1 3 6.375 51 Alkali 5 Brush G silicate 2372 1 1.5 0.028 51 Alkyl 56 Brush E silicate 2373 1 7.5 1.271 87 Alkali 2 Spray G silicate 2374 1 13.5 0.772 85 Alkyl 18 Spray E silicate 2375 1 5 4.083 86 Alkyl 23 Spray E silicate 2376 1 5 2.900 50 Epoxy resin 30 Brush E 2377 1 1 0.650 51 Acrylic resin 77 Brush E 2378 1 120 0.161 51 Urethane 655 Brush E resin 2379 1 3.7 2.298 80 Polyester 47 Spray E resin 2380 1 6.1 1.676 46 Epoxy resin 43 Spray E 2381 1 198.5 0.048 51 Acrylic resin 52 Brush E 2382 1 2.5 3.000 86 Urethane 20 Brush E resin 2383 1 18.5 0.774 85 Polyester 200 Brush E resin 2384 1 8 1.867 82 Alkali 22 Spray E silicate 2385 1 1.6 4.077 81 Alkyl 25 Spray E silicate 2386 1 1.2 6.045 46 Alkali 14 Spray E silicate

TABLE 121 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2387 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 2388 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 2389 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 2390 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 2391 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 2392 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 2393 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 2394 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 2395 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 2396 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 2397 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 2398 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 2399 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 2400 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 2401 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 2402 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 2403 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 2404 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 2405 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 2406 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2387 1 0.5 0.933 47 Urethane 112 Spray E resin 2388 1 9 2.350 48 Alkali 24 Spray E silicate 2389 1 4.5 1.618 51 Urethane 150 Spray E resin 2390 1 136 0.109 53 Alkali 18 Spray E silicate 2391 1 13 1.314 88 Alkyl 19 Brush E silicate 2392 1 10.6 0.181 85 Alkyl 24 Spray E silicate 2393 1 1.6 2.000 83 Urethane 99 Spray E resin 2394 1 68 0.223 82 Alkyl 7 Spray E silicate 2395 1 4.5 1.945 83 Epoxy resin 100 Spray E 2396 1 10.5 1.452 47 Alkyl 27 Brush E silicate 2397 1 4.9 3.322 51 Alkali 15 Spray E silicate 2398 1 10.5 1.261 52 Alkyl 14 Spray E silicate 2399 1 192 0.074 51 Urethane 55 Spray E resin 2400 1 0.07 11.869 52 Alkyl 8 Spray E silicate 2401 1 9.5 1.000 89 Urethane 122 Brush E resin 2402 1 2.6 3.278 85 Alkyl 54 Spray E silicate 2403 1 4.5 2.327 82 Alkali 19 Spray E silicate 2404 1 3 1.550 87 Alkyl 25 Brush E silicate 2405 1 7.5 1.906 88 Alkyl 58 Spray E silicate 2406 1 77 0.251 49 Alkyl 21 Spray E silicate

TABLE 122 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2407 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 2408 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 2409 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 2410 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 2411 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 2412 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 2413 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 2414 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 2415 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 2416 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 2417 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 2418 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 2419 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 2420 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 2421 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 2422 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 2423 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 2424 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 2425 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2407 1 10.5 1.078 50 Alkali 19 Brush E silicate 2408 1 15.5 0.648 51 Urethane 56 Spray E resin 2409 1 5.8 1.250 22 Alkyl 77 Spray E silicate 2410 1 1.9 1.759 53 Alkyl 12 Spray E silicate 2411 1 16.9 1.369 88 Alkyl 64 Spray E silicate 2412 1 1.5 5.400 85 Alkyl 34 Brush E silicate 2413 1 0.05 19.048 83 Alkali 28 Spray E silicate 2414 1 215 0.072 81 Urethane 109 Brush E resin 2415 1 4.2 2.019 80 Alkyl 15 Spray E silicate 2416 1 1.5 3.160 47 Alkyl 14 Spray E silicate 2417 1 4.8 0.828 49 Alkyl 18 Spray E silicate 2418 1 0.5 12.267 50 Urethane 122 Brush E resin 2419 1 2.3 3.848 51 Alkyl 54 Spray E silicate 2420 1 0.05 9.810 52 Alkali 19 Spray E silicate 2421 1 120 0.172 83 Alkyl 25 Brush E silicate 2422 1 3.7 0.532 88 Alkyl 58 Spray E silicate 2423 1 16.5 0.869 85 Alkyl 21 Spray E silicate 2424 1 24 0.768 83 Alkali 19 Brush E silicate 2425 1 0.01 13.366 82 Urethane 56 Spray E resin

TABLE 123 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2426 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes 2427 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 2428 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 2429 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 2430 9.64 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 2431 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 2432 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 2433 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 2434 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 2435 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 2436 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 2437 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 2438 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 2439 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 2440 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 2441 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 2442 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 2443 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 2444 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 2445 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2426 1 7.8 1.352 47 Alkyl 77 Spray E silicate 2427 1 1.6 4.077 46 Alkyl 54 Spray E silicate 2428 1 3.2 3.667 49 Alkali 2 Spray G silicate 2429 1 5.4 0.406 50 Alkali 20 Spray E silicate 2430 1 220 0.076 51 Alkali 5 Spray G silicate 2431 1 2.2 2.531 83 Alkyl 20 Spray E silicate 2432 1 2.8 3.605 82 Alkali 15 Brush E silicate 2433 1 12 1.423 88 Alkyl 57 Brush E silicate 2434 1 10.6 0.207 85 Alkali 13 Brush E silicate 2435 1 35 0.303 86 Alkyl 22 Brush E silicate 2436 1 125.5 0.057 47 Alkali 20 Spray E silicate 2437 1 6 2.500 48 Alkyl 27 Spray E silicate 2438 1 34 0.417 50 Alkali 15 Spray E silicate 2439 1 1.6 3.615 51 Alkyl 35 Spray E silicate 2440 1 7.5 0.835 52 Alkali 34 Brush E silicate 2441 1 200 0.112 88 Alkyl 45 Brush E silicate 2442 1 7.5 1.612 89 Alkali 52 Brush E silicate 2443 1 3.2 3.071 86 Alkyl 23 Brush E silicate 2444 1 2.6 1.194 87 Alkali 5 Spray E silicate 2445 1 3 4.400 86 Alkyl 52 Brush E silicate

TABLE 124 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2446 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes 2447 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 2448 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 2449 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 2450 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 2451 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 2452 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 2453 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 2454 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 2455 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 2456 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 2457 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 2458 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 2459 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 2460 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 2461 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 2462 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 2463 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 2464 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 2465 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2446 1 15.2 0.037 46 Alkali 150 Brush E silicate 2447 1 0.09 9.450 49 Alkyl 60 Brush E silicate 2448 1 13.5 0.483 35 Alkali 15 Spray E silicate 2449 1 135.4 0.172 37 Alkyl 24 Spray E silicate 2450 1 3 4.375 36 Alkali 34 Spray E silicate 2451 1 7.8 1.409 38 Alkyl 20 Brush E silicate 2452 1 10.2 1.330 48 Alkali 200 Brush E silicate 2453 1 7 2.588 46 Alkyl 56 Brush E silicate 2454 1 225.2 0.038 51 Alkali 34 Spray E silicate 2455 1 5.4 2.219 46 Alkyl 2 Spray G silicate 2456 1 3.2 0.019 38 Alkali 15 Spray E silicate 2457 1 13.5 1.048 48 Alkali 10 Spray E silicate 2458 1 1.6 6.692 52 Alkyl 125 Brush E silicate 2459 1 1.5 0.320 30 Alkali 24 Brush E silicate 2460 1 2.5 1.829 76 Alkyl 110 Brush E silicate 2461 1 2.6 0.889 72 Alkali 24 Brush E silicate 2462 1 126 0.072 81 Alkyl 2 Spray G silicate 2463 1 120 0.159 64 Alkali 37 Spray E silicate 2464 1 7.5 1.776 69 Alkyl 113 Brush E silicate 2465 1 6.5 1.933 83 Alkali 2 Spray G silicate

TABLE 125 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2466 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes 2467 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 2468 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 2469 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 2470 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 2471 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 2472 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 2473 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 2474 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 2475 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 2476 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 2477 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 2478 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 2479 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 2480 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 2481 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 2482 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 2483 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 2484 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 2485 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2466 1 20 0.500 30 Alkyl 75 Brush E silicate 2467 1 0.007 7.448 83 Alkali 30 Brush E silicate 2468 1 9 0.610 75 Alkyl 34 Brush E silicate 2469 1 7.5 1.976 76 Epoxy resin 124 Brush E 2470 1 50 0.539 72 Acrylic resin 15 Spray E 2471 1 0.005 2.886 71 Urethane 23 Spray E resin 2472 1 25.6 0.169 82 Polyester 157 Brush E resin 2473 1 56.5 0.001 81 Epoxy resin 26 Spray E 2474 1 1.6 1.192 83 Acrylic resin 38 Spray E 2475 1 3 5.125 50 Urethane 160 Brush E resin 2476 1 100 0.292 72 Polyester 27 Brush E resin 2477 1 65.5 0.114 47 Epoxy resin 180 Brush E 2478 1 1.9 0.241 47 Acrylic resin 26 Spray E 2479 1 2.1 1.484 52 Urethane 180 Brush E resin 2480 1 10.5 0.722 52 Polyester 15 Spray E resin 2481 1 6.5 1.573 50 Epoxy resin 2 Spray G 2482 1 19.5 0.629 46 Acrylic resin 28 Spray E 2483 1 0.8 0.333 47 Urethane 30 Spray E resin 2484 1 18.5 0.487 83 Polyester 2 Spray G resin 2485 1 4.3 2.208 52 Epoxy resin 157 Brush E

TABLE 126 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2487 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 2488 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 2489 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 2490 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 2491 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 2492 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 2493 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 2494 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 2495 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 2496 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 2497 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 2498 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 2499 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 2500 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 2501 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 2502 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 2503 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 2504 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 2505 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 2506 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2487 1 1.5 4.680 85 Alkyl 130 Brush E silicate 2488 1 4.5 0.764 53 Alkyl 29 Brush E silicate 2489 1 15.5 0.170 88 Epoxy resin 30 Brush E 2490 1 10.5 1.209 85 Acrylic resin 120 Brush E 2491 1 2.5 4.171 52 Urethane 187 Brush E resin 2492 1 9 2.640 83 Polyester 28 Spray E resin 2493 1 10.5 0.156 88 Epoxy resin 5 Spray E 2494 1 5.7 2.910 49 Acrylic resin 35 Spray E 2495 1 3.9 0.327 50 Urethane 5 Spray G resin 2496 1 4.5 1.091 51 Polyester 200 Brush E resin 2497 1 3.6 1.826 83 Alkali 25 Spray E silicate 2498 1 16.4 0.764 82 Alkali 15 Spray E silicate 2499 1 6 2.657 88 Alkyl 20 Spray E silicate 2500 1 7.5 0.212 85 Alkali 18 Spray E silicate 2501 1 10.5 0.357 87 Alkyl 22 Spray E silicate 2502 1 2.6 4.639 86 Alkali 19 Spray E silicate 2503 1 1.5 0.160 46 Alkyl 29 Spray E silicate 2504 1 13.5 0.731 49 Alkali 23 Spray E silicate 2505 1 2.6 1.917 35 Alkyl 21 Spray E silicate 2506 1 6.5 0.007 30 Alkali 19 Spray E silicate

TABLE 127 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains phase and Any of diameter Zn metal among Zn Chemical component Alloy Zn—Mg MgZn2, of later- grains/Zn metal content of Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2507 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 2508 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 2509 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 2510 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 2511 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 2512 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 2513 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 2514 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 2515 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 2516 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 2517 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 2518 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 2519 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 2520 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 2521 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 2522 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 2523 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 2524 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 2525 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 2526 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 2527 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Example Zn alloy metal grains of coat Base resin thickness Coating Corrosion No grains grains (Mass %) (Mass %) type (μm) method Test Results 2507 1 1.6 2.462 76 Alkyl 15 Spray E silicate 2508 1 3.8 0.729 72 Alkali 18 Spray E silicate 2509 1 0.08 16.204 30 Alkyl 22 Spray E silicate 2510 1 164.5 0.022 83 Alkyl 21 Spray E silicate 2511 1 3.6 1.283 75 Alkyl 29 Spray E silicate 2512 1 8.6 1.688 76 Alkali 23 Spray E silicate 2513 1 12 1.731 72 Alkyl 21 Spray E silicate 2514 1 5.8 0.500 83 Alkali 19 Spray E silicate 2515 1 10 2.409 50 Alkyl 21 Spray E silicate 2516 1 1 12.750 72 Alkali 19 Spray E silicate 2517 1 10.5 1.113 50 Acrylic resin 654 Spray E 2518 1 6.5 1.133 48 Alkali 700 Spray E silicate 2519 1 19.5 1.195 75 Alkyl 555 Spray E silicate 2520 1 0.8 10.222 55 Alkyl 12 Spray E silicate 2521 1 5.3 0.013 38 Alkyl 678 Brush E silicate 2522 1 4.3 2.868 48 Urethane 674 Spray E resin 2523 1 3.2 1.524 76 Polyester 325 Spray E resin 2524 1 1.5 1.280 72 Alkyl 665 Spray E silicate 2525 1 4.5 1.109 75 Alkyl 354 Brush E silicate 2526 1 0.8 9.333 76 Alkyl 165 Spray E silicate 2527 1 6.5 3.667 72 Urethane 354 Spray E resin

TABLE 128 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2528 16.5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 2529 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 2530 0.96 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes Yes 2531 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 2532 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 2533 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 2534 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 2535 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 2536 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 2537 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 2538 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 2539 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 2540 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 2541 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 2542 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 2543 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 2544 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 2545 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 2546 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 2547 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2528 1 5 1.867 49 Alkyl 14 Spray E silicate 2529 1 198.7 0.047 89 Urethane 55 Spray E resin 2530 1 36 0.500 90 Alkyl 8 Spray E silicate 2531 1 1.5 0.012 86 Urethane 122 Brush E resin 2532 1 0.008 1.587 48 Alkyl 555 Spray E silicate 2533 1 1.4 2.833 47 Alkali 19 Spray E silicate 2534 1 4.2 2.673 47 Alkyl 25 Brush E silicate 2535 1 1.6 0.731 47 Alkyl 58 Spray E silicate 2536 1 7.5 0.671 52 Alkyl 685 Spray E silicate 2537 1 1.6 3.538 52 Alkali 19 Brush E silicate 2538 1 2 5.133 52 Urethane 700 Spray E resin 2539 1 270 0.069 88 Alkyl 77 Spray E silicate 2540 1 7.5 0.424 87 Alkyl 54 Spray E silicate 2541 1 2.9 1.385 89 Alkyl 64 Spray E silicate 2542 1 2.6 2.111 90 Alkyl 34 Brush E silicate 2543 1 0.1 22.273 91 Alkali 28 Spray E silicate 2544 1 1.2 8.000 46 Urethane 109 Brush E resin 2545 1 1.2 0.636 47 Alkyl 15 Spray E silicate 2546 1 62 0.341 47 Alkyl 14 Spray E silicate 2547 1 2.4 3.059 49 Alkyl 18 Spray E silicate

TABLE 129 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2548 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 2549 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 2550 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 2551 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 2552 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yea 1.05 Yes Yes 2553 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 2554 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 2555 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 2556 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 2557 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 2558 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 2559 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 2560 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 2561 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 2562 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 2563 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 2564 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 2565 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 2566 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 2567 16.5 2.6 49.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2548 1 2.1 4.129 50 Alkali 2 Spray G silicate 2549 1 34.5 0.220 87 Alkyl 37 Spray E silicate 2550 1 270 0.109 83 Alkali 12 Spray E silicate 2551 1 32.5 0.254 48 Alkyl 160 Brush E silicate 2552 1 3 6.375 51 Alkali 5 Brush G silicate 2553 1 1.5 0.028 51 Alkyl 56 Brush E silicate 2554 1 7.5 1.271 87 Alkali 2 Spray G silicate 2555 1 13.5 0.772 85 Alkyl 18 Spray E silicate 2556 1 5 4.083 86 Alkyl 23 Spray E silicate 2557 1 5 2.900 50 Epoxy resin 30 Brush E 2558 1 1 0.650 51 Acrylic resin 77 Brush E 2559 1 120 0.161 51 Urethane 655 Brush E resin 2560 1 3.7 2.298 80 Polyester 47 Spray E resin 2561 1 6.1 1.676 46 Epoxy resin 43 Spray E 2562 1 198.5 0.048 51 Acrylic resin 52 Brush E 2563 1 2.5 3.000 86 Urethane 20 Brush E resin 2564 1 18.5 0.774 85 Polyester 200 Brush E resin 2565 1 8 1.867 82 Alkali 22 Spray E silicate 2566 1 1.6 4.077 81 Alkyl 25 Spray E silicate 2567 1 1.2 6.045 46 Alkali 14 Spray E silicate

TABLE 130 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2568 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 2569 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 2570 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 2571 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 2572 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 2573 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 2574 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 2575 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 2576 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 2577 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 2578 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 2579 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 2580 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 2581 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 2582 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 2583 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 2584 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 2585 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 2586 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 2587 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2568 1 0.5 0.933 47 Urethane 112 Spray E resin 2569 1 9 2.350 48 Alkali 24 Spray E silicate 2570 1 4.5 1.618 51 Urethane 150 Spray E resin 2571 1 136 0.109 53 Alkali 18 Spray E silicate 2572 1 13 1.314 88 Alkyl 19 Brush E silicate 2573 1 10.6 0.181 85 Alkyl 24 Spray E silicate 2574 1 1.6 2.000 83 Urethane 99 Spray E resin 2575 1 68 0.223 82 Alkyl 7 Spray E silicate 2576 1 4.5 1.945 83 Epoxy resin 100 Spray E 2577 1 10.5 1.452 47 Alkyl 27 Brush E silicate 2578 1 4.9 3.322 51 Alkali 15 Spray E silicate 2579 1 10.5 1.261 52 Alkyl 14 Spray E silicate 2580 1 192 0.074 51 Urethane 55 Spray E resin 2581 1 0.07 11.869 52 Alkyl 8 Spray E silicate 2582 1 9.5 1.000 89 Urethane 122 Brush E resin 2583 1 2.6 3.278 85 Alkyl 54 Spray E silicate 2584 1 4.5 2.327 82 Alkali 19 Spray E silicate 2585 1 3 1.550 87 Alkyl 25 Brush E silicate 2586 1 7.5 1.906 88 Alkyl 58 Spray E silicate 2587 1 77 0.251 49 Alkyl 21 Spray E silicate

TABLE 131 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2588 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 2589 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 2590 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 2591 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 2592 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 2593 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 2594 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 2595 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 2596 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 2597 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 2598 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 2599 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 2600 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 2601 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 2602 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 2603 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 2604 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 2605 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 2606 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 2607 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2588 1 10.5 1.078 50 Alkali 19 Brush E silicate 2589 1 15.5 0.648 51 Urethane 56 Spray E resin 2590 1 5.8 1.250 52 Alkyl 77 Spray E silicate 2591 1 1.9 1.759 53 Alkyl 12 Spray E silicate 2592 1 16.9 1.369 88 Alkyl 64 Spray E silicate 2593 1 1.5 5.400 85 Alkyl 34 Brush E silicate 2594 1 0.05 19.048 83 Alkali 28 Spray E silicate 2595 1 215 0.072 81 Urethane 109 Brush E resin 2596 1 4.2 2.019 80 Alkyl 15 Spray E silicate 2597 1 1.5 3.160 47 Alkyl 14 Spray E silicate 2598 1 4.8 0.828 49 Alkyl 18 Spray E silicate 2599 1 0.5 12.267 50 Urethane 122 Brush E resin 2600 1 2.3 3.848 51 Alkyl 54 Spray E silicate 2601 1 0.05 9.810 52 Alkali 19 Spray E silicate 2602 1 120 0.172 83 Alkyl 25 Brush E silicate 2603 1 3.7 0.532 88 Alkyl 58 Spray E silicate 2604 1 16.5 0.869 85 Alkyl 21 Spray E silicate 2605 1 24 0.768 83 Alkali 19 Brush E silicate 2606 1 0.01 13.366 82 Urethane 56 Spray E resin 2607 1 7.8 1.352 47 Alkyl 77 Spray E silicate

TABLE 132 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2608 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 2609 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 2610 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 2611 9.64 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 2612 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 2613 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 2614 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 2615 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 2616 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 2617 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 2618 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 2619 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 2620 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 2621 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 2622 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 2623 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 2624 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 2625 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 2626 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2608 1 1.6 4.077 46 Alkyl 54 Spray E silicate 2609 1 3.2 3.667 49 Alkali 2 Spray G silicate 2610 1 5.4 0.406 50 Alkali 20 Spray E silicate 2611 1 220 0.076 51 Alkali 5 Spray G silicate 2612 1 2.2 2.531 83 Alkyl 20 Spray E silicate 2613 1 2.8 3.605 82 Alkali 15 Brush E silicate 2614 1 12 1.423 88 Alkyl 57 Brush E silicate 2615 1 10.6 0.207 85 Alkali 13 Brush E silicate 2616 1 35 0.303 86 Alkyl 22 Brush E silicate 2617 1 125.5 0.057 47 Alkali 20 Spray E silicate 2618 1 6 2.500 48 Alkyl 27 Spray E silicate 2619 1 34 0.417 50 Alkali 15 Spray E silicate 2620 1 1.6 3.615 51 Alkyl 35 Spray E silicate 2621 1 7.5 0.835 52 Alkali 34 Brush E silicate 2622 1 200 0.112 88 Alkyl 45 Brush E silicate 2623 1 7.5 1.612 89 Alkali 52 Brush E silicate 2624 1 3.2 3.071 86 Alkyl 23 Brush E silicate 2625 1 2.6 1.194 87 Alkali 23 Spray E silicate 2626 1 3 4.400 86 Alkyl 52 Brush E silicate

TABLE 133 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2627 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes 2628 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 2629 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 2630 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 2631 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 2632 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 2633 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 2634 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 2635 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 2636 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 2637 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 2638 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 2639 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 2640 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 2641 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 2642 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 2643 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 2644 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 2645 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 2646 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 2647 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2627 1 15.2 0.037 46 Alkali 150 Brush E silicate 2628 1 0.09 9.450 49 Alkyl 60 Brush E silicate 2629 1 13.5 0.483 35 Alkali 15 Spray E silicate 2630 1 135.4 0.172 37 Alkyl 24 Spray E silicate 2631 1 3 4.375 36 Alkali 34 Spray E silicate 2632 1 7.8 1.409 38 Alkyl 20 Brush E silicate 2633 1 10.2 1.330 48 Alkali 200 Brush E silicate 2634 1 7 2.588 46 Alkyl 56 Brush E silicate 2635 1 225.2 0.038 51 Alkali 34 Spray E silicate 2636 1 5.4 2.219 46 Alkyl 2 Spray G silicate 2637 1 3.2 0.019 38 Alkali 15 Spray E silicate 2638 1 13.5 1.048 48 Alkali 10 Spray E silicate 2639 1 1.6 6.692 52 Alkyl 125 Brush E silicate 2640 1 1.5 0.320 30 Alkali 24 Brush E silicate 2641 1 2.5 1.829 76 Alkyl 110 Brush E silicate 2642 1 2.6 0.889 72 Alkali 24 Brush E silicate 2643 1 126 0.072 81 Alkyl 2 Spray G silicate 2644 1 120 0.159 64 Alkali 37 Spray E silicate 2645 1 7.5 1.776 69 Alkyl 113 Brush E silicate 2646 1 6.5 1.933 83 Alkali 2 Spray G silicate 2647 1 2.0 0.500 30 Alkyl 75 Brush E silicate

TABLE 134 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2648 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 2649 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 2650 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 2651 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 2652 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 2653 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 2654 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 2655 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 2656 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 2657 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 2658 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 2659 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 2660 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 2661 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 2662 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 2663 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 2664 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 2665 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 2666 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 2667 16.5 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2648 1 0.007 7.448 83 Alkali 30 Brush E silicate 2649 1 9 0.610 75 Alkyl 34 Brush E silicate 2650 1 7.5 1.976 76 Epoxy resin 124 Brush E 2651 1 50 0.539 72 Acrylic resin 15 Spray E 2652 1 0.005 2.886 71 Urethane 23 Spray E resin 2653 1 25.6 0.169 82 Polyester 157 Brush E resin 2654 1 56.5 0.001 81 Epoxy resin 26 Spray E 2655 1 1.6 1.192 83 Acrylic resin 38 Spray E 2656 1 3 5.125 50 Urethane 160 Brush E resin 2657 1 100 0.292 72 Polyester 27 Brush E resin 2658 1 65.5 0.114 47 Epoxy resin 180 Brush E 2659 1 1.9 0.241 47 Acrylic resin 26 Spray E 2660 1 2.1 1.484 52 Urethane 180 Brush E resin 2661 1 10.5 0.722 52 Polyester 15 Spray E resin 2662 1 6.5 1.573 50 Epoxy resin 2 Spray G 2663 1 19.5 0.629 46 Acrylic resin 28 Spray E 2664 1 0.8 0.333 47 Urethane 30 Spray E resin 2665 1 18.5 0.487 83 Polyester 2 Spray G resin 2666 1 4.3 2.208 52 Epoxy resin 157 Brush E 2667 1 3.2 2.238 89 Acrylic resin 28 Brush E

TABLE 135 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2668 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 2669 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 2670 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 2671 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 2672 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 2673 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 2674 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 2675 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 2676 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 2677 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 2678 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 2679 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 2680 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 2681 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 2682 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 2683 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 2684 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 2685 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 2686 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2668 1 1.5 4.680 85 Alkyl 130 Brush E silicate 2669 1 4.5 0.764 53 Alkyl 29 Brush E silicate 2670 1 15.5 0.170 88 Epoxy resin 30 Brush E 2671 1 10.5 1.209 85 Acrylic resin 120 Brush E 2672 1 2.5 4.171 52 Urethane 187 Brush E resin 2673 1 9 2.640 83 Polyester 28 Spray E resin 2674 1 10.5 0.156 88 Epoxy resin 5 Spray E 2675 1 5.7 2.910 49 Acrylic resin 35 Spray E 2676 1 3.9 0.327 50 Urethane 5 Spray G resin 2677 1 4.5 1.091 51 Polyester 200 Brush E resin 2678 1 3.6 1.826 83 Alkali 25 Spray E silicate 2679 1 16.4 0.764 82 Alkali 15 Spray E silicate 2680 1 6 2.657 88 Alkyl 20 Spray E silicate 2681 1 7.5 0.212 85 Alkali 18 Spray E silicate 2682 1 10.5 0.357 87 Alkyl 22 Spray E silicate 2683 1 2.6 4.639 86 Alkali 19 Spray E silicate 2684 1 1.5 0.160 46 Alkyl 29 Spray E silicate 2685 1 13.5 0.731 49 Alkali 23 Spray E silicate 2686 1 2.6 1.917 35 Alkyl 21 Spray E silicate

TABLE 136 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Ave present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2687 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes 2688 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 2689 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 2690 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 2691 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 2692 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 2693 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 2694 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 2695 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 2696 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 2697 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 2698 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 2699 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 2700 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 2701 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 2702 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 2703 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 2704 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 2705 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 2706 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 2707 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 2708 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention grains/ added Zn metal content Coat Corrosion Example Zn alloy metal grains of coat Base resin thickness Coating Test No grains grains (Mass %) (Mass %) type (μm) method Results 2687 1 6.5 0.007 30 Alkali 19 Spray E silicate 2688 1 1.6 2.462 76 Alkyl 15 Spray E silicate 2689 1 3.8 0.729 72 Alkali 18 Spray E silicate 2690 1 0.08 16.204 30 Alkyl 22 Spray E silicate 2691 1 164.5 0.022 83 Alkyl 21 Spray E silicate 2692 1 3.6 1.283 75 Alkyl 29 Spray E silicate 2693 1 8.6 1.688 76 Alkali 23 Spray E silicate 2694 1 12 1.731 72 Alkyl 21 Spray E silicate 2695 1 5.8 0.500 83 Alkali 19 Spray E silicate 2696 1 10 2.409 50 Alkyl 21 Spray E silicate 2697 1 1 12.750 72 Alkali 19 Spray E silicate 2698 1 10.5 1.113 50 Acrylic resin 654 Spray E 2699 1 6.5 1.133 48 Alkali 700 Spray E silicate 2700 1 19.5 1.195 75 Alkyl 555 Spray E silicate 2701 1 0.8 10.222 55 Alkyl 12 Spray E silicate 2702 1 5.3 0.013 38 Alkyl 678 Brush E silicate 2703 1 4.3 2.868 48 Urethane 674 Spray E resin 2704 1 3.2 1.524 76 Polyester 325 Spray E resin 2705 1 1.5 1.280 72 Alkyl 665 Spray E silicate 2706 1 4.5 1.109 75 Alkyl 354 Brush E silicate 2707 1 0.8 9.333 76 Alkyl 165 Spray E silicate 2708 1 6.5 3.667 72 Urethane 354 Spray E resin

TABLE 137 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Average present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2709 16..5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 2710 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 2711 0.96 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes Yes 2712 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 2713 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 2714 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 2715 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 2716 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 2717 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 2718 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 2719 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 2720 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 2721 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 2722 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 2723 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 2724 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 2725 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 2726 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 2727 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 2728 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention Number grains/ added Zn metal content Coat Corrosion Example of Zn alloy metal grains of coat Base resin thickness Coating Test No faces grains grains (Mass %) (Mass %) type (μm) method Results 2709 2 1 5 1.867 49 Alkyl 14 Spray E silicate 2710 2 1 198.7 0.047 89 Urethane 55 Spray E resin 2711 2 1 36 0.500 90 Alkyl 8 Spray E silicate 2712 2 1 1.5 0.012 86 Urethane 122 Brush E resin 2713 6 1 0.008 1.587 48 Alkyl 555 Spray E silicate 2714 6 1 1.4 2.833 47 Alkali 19 Spray E silicate 2715 7 1 4.2 2.673 47 Alkyl 25 Brush E silicate 2716 6 1 1.6 0.731 47 Alkyl 58 Spray E silicate 2717 2 1 7.5 0.671 52 Alkyl 685 Spray E silicate 2718 7 1 1.6 3.538 52 Alkali 19 Brush E silicate 2719 2 1 2 5.133 52 Urethane 700 Spray E resin 2720 6 1 270 0.069 88 Alkyl 77 Spray E silicate 2721 6 1 7.5 0.424 87 Alkyl 54 Spray E silicate 2722 2 1 2.9 1.385 89 Alkyl 64 Spray E silicate 2723 2 1 2.6 2.111 90 Alkyl 34 Brush E silicate 2724 7 1 0.1 22.273 91 Alkali 28 Spray E silicate 2725 6 1 1.2 8.000 46 Urethane 109 Brush E resin 2726 7 1 1.2 0.636 47 Alkyl 15 Spray E silicate 2727 2 1 62 0.341 47 Alkyl 14 Spray E silicate 2728 7 1 2.4 3.059 49 Alkyl 18 Spray E silicate

TABLE 138 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Average present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2729 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 2730 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 2731 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 2732 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 2733 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 2734 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 2735 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 2736 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 2737 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 2738 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 2739 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 2740 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 2741 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 2742 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 2743 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 2744 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 2745 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 2746 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 2747 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 2748 16.5 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention Number grains/ added Zn metal content Coat Corrosion Example of Zn alloy metal grains of coat Base resin thickness Coating Test No faces grains grains (Mass %) (Mass %) type (μm) method Results 2729 6 1 2.1 4.129 50 Alkali 2 Spray G silicate 2730 7 1 34.5 0.220 87 Alkyl 37 Spray E silicate 2731 6 1 270 0.109 83 Alkali 12 Spray E silicate 2732 7 1 32.5 0.254 48 Alkyl 160 Brush E silicate 2733 6 1 3 6.375 51 Alkali 5 Brush G silicate 2734 2 1 1.5 0.028 51 Alkyl 56 Brush E silicate 2735 7 1 7.5 1.271 87 Alkali 2 Spray G silicate 2736 6 1 13.5 0.772 85 Alkyl 18 Spray E silicate 2737 6 1 5 4.083 86 Alkyl 23 Spray E silicate 2738 6 1 5 2.900 50 Epoxy resin 30 Brush E 2739 2 1 1 0.650 51 Acrylic resin 77 Brush E 2740 6 1 120 0.161 51 Urethane 655 Brush E resin 2741 7 1 3.7 2.298 80 Polyester 47 Spray E resin 2742 2 1 6.1 1.676 46 Epoxy resin 43 Spray E 2743 6 1 198.5 0.048 51 Acrylic resin 52 Brush E 2744 2 1 2.5 3.000 86 Urethane 20 Brush E resin 2745 6 1 18.5 0.774 85 Polyester 200 Brush E resin 2746 7 1 8 1.867 82 Alkali 22 Spray E silicate 2747 7 1 1.6 4.077 81 Alkyl 25 Spray E silicate 2748 2 1 1.2 6.045 46 Alkali 14 Spray E silicate

TABLE 139 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Average present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2749 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 2750 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 2751 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 2752 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 2753 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 2754 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 2755 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 2756 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 2757 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 2758 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 2759 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 2760 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 2761 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 2762 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 2763 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 2764 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 2765 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 2766 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 2767 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 2768 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention Number grains/ added Zn metal content Coat Corrosion Example of Zn alloy metal grains of coat Base resin thickness Coating Test No faces grains grains (Mass %) (Mass %) type (μm) method Results 2749 2 1 0.5 0.933 47 Urethane 112 Spray E resin 2750 6 1 9 2.350 48 Alkali 24 Spray E silicate 2751 7 1 4.5 1.618 51 Urethane 150 Spray E resin 2752 6 1 136 0.109 53 Alkali 18 Spray E silicate 2753 7 1 13 1.314 88 Alkyl 19 Brush E silicate 2754 6 1 10.6 0.181 85 Alkyl 24 Spray E silicate 2755 2 1 1.6 2.000 83 Urethane 99 Spray E resin 2756 2 1 68 0.223 82 Alkyl 7 Spray E silicate 2757 6 1 4.5 1.945 83 Epoxy resin 100 Spray E 2758 7 1 10.5 1.452 47 Alkyl 27 Brush E silicate 2759 6 1 4.9 3.322 51 Alkali 15 Spray E silicate 2760 6 1 10.5 1.261 52 Alkyl 14 Spray E silicate 2761 2 1 192 0.074 51 Urethane 55 Spray E resin 2762 7 1 0.07 11.869 52 Alkyl 8 Spray E silicate 2763 2 1 9.5 1.000 89 Urethane 122 Brush E resin 2764 2 1 2.6 3.278 85 Alkyl 54 Spray E silicate 2765 6 1 4.5 2.327 82 Alkali 19 Spray E silicate 2766 7 1 3 1.550 87 Alkyl 25 Brush E silicate 2767 7 1 7.5 1.906 88 Alkyl 58 Spray E silicate 2768 6 1 77 0.251 49 Alkyl 21 Spray E silicate

TABLE 140 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Average present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2769 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 2770 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 2771 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 2772 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 2773 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 2774 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 2775 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 2776 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 2777 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 2778 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 2779 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 2780 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 2781 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 2782 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 2783 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 2784 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 2785 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 2786 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 2787 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 2788 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention Number grains/ added Zn metal content Coat Corrosion Example of Zn alloy metal grains of coat Base resin thickness Coating Test No faces grains grains (Mass %) (Mass %) type (μm) method Results 2769 7 1 10.5 1.078 50 Alkali 19 Brush E silicate 2770 7 1 15.5 0.648 51 Urethane 56 Spray E resin 2771 6 1 5.8 1.250 52 Alkyl 77 Spray E silicate 2772 7 1 1.9 1.759 53 Alkyl 12 Spray E silicate 2773 2 1 16.9 1.369 88 Alkyl 64 Spray E silicate 2774 7 1 1.5 5.400 85 Alkyl 34 Brush E silicate 2775 7 1 0.05 19.048 83 Alkali 28 Spray E silicate 2776 2 1 215 0.072 81 Urethane 109 Brush E resin 2777 6 1 4.2 2.019 80 Alkyl 15 Spray E silicate 2778 6 1 1.5 3.160 47 Alkyl 14 Spray E silicate 2779 7 1 4.8 0.828 49 Alkyl 18 Spray E silicate 2780 7 1 0.5 12.267 50 Urethane 122 Brush E resin 2781 6 1 2.3 3.848 51 Alkyl 54 Spray E silicate 2782 7 1 0.05 9.810 52 Alkali 19 Spray E silicate 2783 2 1 120 0.172 83 Alkyl 25 Brush E silicate 2784 2 1 3.7 0.532 88 Alkyl 58 Spray E silicate 2785 6 1 16.5 0.869 85 Alkyl 21 Spray E silicate 2786 7 1 24 0.768 83 Alkali 19 Brush E silicate 2787 6 1 0.01 13.366 82 Urethane 56 Spray E resin 2788 2 1 7.8 1.352 47 Alkyl 77 Spray E silicate

TABLE 141 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Average present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2789 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 2790 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 2791 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 2792 9.64 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 2793 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 2794 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 2795 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 2796 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 2797 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 2798 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 2799 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 2800 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 2801 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 2802 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 2803 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 2804 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 2805 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 2806 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 2807 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 2808 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention Number grains/ added Zn metal content Coat Corrosion Example of Zn alloy metal grains of coat Base resin thickness Coating Test No faces grains grains (Mass %) (Mass %) type (μm) method Results 2789 2 1 1.6 4.077 46 Alkyl 54 Spray E silicate 2790 7 1 3.2 3.667 49 Alkali 2 Spray G silicate 2791 6 1 5.4 0.406 50 Alkali 20 Spray E silicate 2792 7 1 220 0.076 51 Alkali 5 Spray G silicate 2793 7 1 2.2 2.531 83 Alkyl 20 Spray E silicate 2794 6 1 2.8 3.605 82 Alkali 15 Brush E silicate 2795 2 1 12 1.423 88 Alkyl 57 Brush E silicate 2796 7 1 10.6 0.207 85 Alkali 13 Brush E silicate 2797 2 1 35 0.303 86 Alkyl 22 Brush E silicate 2798 2 1 125.5 0.057 47 Alkali 20 Spray E silicate 2799 7 1 6 2.500 48 Alkyl 27 Spray E silicate 2800 2 1 34 0.417 50 Alkali 15 Spray E silicate 2801 7 1 1.6 3.615 51 Alkyl 35 Spray E silicate 2802 2 1 7.5 0.835 52 Alkali 34 Brush E silicate 2803 6 1 200 0.112 88 Alkyl 45 Brush E silicate 2804 6 1 7.5 1.612 89 Alkali 52 Brush E silicate 2805 7 1 3.2 3.071 86 Alkyl 23 Brush E silicate 2806 6 1 2.6 1.194 87 Alkali 5 Spray E silicate 2807 2 1 3 4.400 86 Alkyl 52 Brush E silicate 2808 2 1 15.2 0.037 46 Alkali 150 Brush E silicate

TABLE 142 Percent Diameter of fine- distribution grain Mg solid (peak metal solution Average diameter) of grains Chemical component phase and Any of diameter Zn metal among Zn content of Alloy Zn—Mg MgZn2, of later- grains/Zn metal Zn metal grain intermetallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces Average present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks aspect grain Mg7Zn3 No (μm) metal metal (Vol %) Zn Mg Al Si present? ratio surfaces? present? 2809 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 2810 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 2811 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 2812 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 2813 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 2814 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 2815 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 2816 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 2817 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 2818 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 2819 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 2820 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 2821 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 2822 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 2823 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 2824 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 2825 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 2826 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 2827 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 2828 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- added Coating details Zn metal Mg Total grains) content metal Zn metal Later- of all grain Invention Number grains/ added Zn metal content Coat Corrosion Example of Zn alloy metal grains of coat Base resin thickness Coating Test No faces grains grains (Mass %) (Mass %) type (μm) method Results 2809 2 1 0.09 9.450 49 Alkyl 60 Brush E silicate 2810 2 1 13.5 0.483 35 Alkali 15 Spray E silicate 2811 2 1 135.4 0.172 37 Alkyl 24 Spray E silicate 2812 2 1 3 4.375 36 Alkali 34 Spray E silicate 2813 6 1 7.8 1.409 38 Alkyl 20 Brush E silicate 2814 6 1 10.2 1.330 48 Alkali 200 Brush E silicate 2815 7 1 7 2.588 46 Alkyl 56 Brush E silicate 2816 6 1 225.2 0.038 51 Alkali 34 Spray E silicate 2817 2 1 5.4 2.219 46 Alkyl 2 Spray G silicate 2818 7 1 3.2 0.019 38 Alkali 15 Spray E silicate 2819 2 1 13.5 1.048 48 Alkali 10 Spray E silicate 2820 6 1 1.6 6.692 52 Alkyl 125 Brush E silicate 2821 6 1 1.5 0.320 30 Alkali 24 Brush E silicate 2822 2 1 2.5 1.829 76 Alkyl 110 Brush E silicate 2823 2 1 2.6 0.889 72 Alkali 24 Brush E silicate 2824 7 1 126 0.072 81 Alkyl 2 Spray G silicate 2825 6 1 120 0.159 64 Alkali 37 Spray E silicate 2826 7 1 7.5 1.776 69 Alkyl 113 Brush E silicate 2827 2 1 6.5 1.933 83 Alkali 2 Spray G silicate 2828 7 1 20 0.500 30 Alkyl 75 Brush E silicate

TABLE 143 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2829 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 2830 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 2831 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 2832 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 2833 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 2834 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 2835 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 2836 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 2837 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 2838 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 2839 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 2840 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 2841 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 2842 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 2843 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 2844 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 2845 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 2846 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 2847 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 2848 16.5 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2829 6 1 0.007 7.448 83 Alkali 30 Brush E silicate 2830 7 1 9 0.610 75 Alkyl 34 Brush E silicate 2831 6 1 7.5 1.976 76 Epoxy resin 124 Brush E 2832 7 1 50 0.539 72 Acrylic resin 15 Spray E 2833 6 1 0.005 2.886 71 Urethane 23 Spray E resin 2834 2 1 25.6 0.169 82 Polyester 157 Brush E resin 2835 7 1 56.5 0.001 81 Epoxy resin 26 Spray E 2836 6 1 1.6 1.192 83 Acrylic resin 38 Spray E 2837 6 1 3 5.125 50 Urethane 160 Brush E resin 2838 6 1 100 0.292 72 Polyester 27 Brush E resin 2839 2 1 65.5 0.114 47 Epoxy resin 180 Brush E 2840 6 1 1.9 0.241 47 Acrylic resin 26 Spray E 2841 7 1 2.1 1.484 52 Urethane 180 Brush E resin 2842 2 1 10.5 0.722 52 Polyester 15 Spray E resin 2843 6 1 6.5 1.573 50 Epoxy resin 2 Spray G 2844 2 1 19.5 0.629 46 Acrylic resin 28 Spray E 2845 6 1 0.8 0.333 47 Urethane 30 Spray E resin 2846 7 1 18.5 0.487 83 Polyester 2 Spray G resin 2847 7 1 4.3 2.208 52 Epoxy resin 157 Brush E 2848 2 1 3.2 2.238 89 Acrylic resin 28 Brush E

TABLE 144 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2849 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 2850 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 2851 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 2852 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 2853 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 2854 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 2855 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 2856 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 2857 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 2858 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 2859 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 2860 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 2861 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 2862 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 2863 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 2864 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 2865 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 2866 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 2867 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 2868 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2849 2 1 1.5 4.680 85 Alkyl 130 Brush E silicate 2850 6 1 4.5 0.764 53 Alkyl 29 Brush E silicate 2851 7 1 15.5 0.170 88 Epoxy resin 30 Brush E 2852 6 1 10.5 1.209 85 Acrylic resin 120 Brush E 2853 7 1 2.5 4.171 52 Urethane 187 Brush E resin 2854 6 1 9 2.640 83 Polyester 28 Spray E resin 2855 2 1 10.5 0.156 88 Epoxy resin 5 Spray E 2856 2 1 5.7 2.910 49 Acrylic resin 35 Spray E 2857 6 1 3.9 0.327 50 Urethane 5 Spray G resin 2858 7 1 4.5 1.091 51 Polyester 200 Brush E resin 2859 6 1 3.6 1.826 83 Alkali 25 Spray E silicate 2860 6 1 16.4 0.764 82 Alkali 15 Spray E silicate 2861 2 1 6 2.657 88 Alkyl 20 Spray E silicate 2862 7 1 7.5 0.212 85 Alkali 18 Spray E silicate 2863 2 1 10.5 0.357 87 Alkyl 22 Spray E silicate 2864 2 1 2.6 4.639 86 Alkali 19 Spray E silicate 2865 6 1 1.5 0.160 46 Alkyl 29 Spray E silicate 2866 7 1 13.5 0.731 49 Alkali 23 Spray E silicate 2867 7 1 2.6 1.917 35 Alkyl 21 Spray E silicate 2868 6 1 6.5 0.007 30 Alkali 19 Spray E silicate

TABLE 145 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2869 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 2870 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 2871 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 2872 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 2873 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 2874 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 2875 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 2876 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 2877 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 2878 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 2879 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 2880 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 2881 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 2882 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 2883 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 2884 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 2885 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 2886 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 2887 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 2888 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 2889 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2869 7 1 1.6 2.462 76 Alkyl silicate 15 Spray E 2870 7 1 3.8 0.729 72 Alkali 18 Spray E silicate 2871 6 1 0.08 16.204 30 Alkyl 22 Spray E silicate 2872 7 1 164.5 0.022 83 Alkyl 21 Spray E silicate 2873 2 1 3.6 1.283 75 Alkyl 29 Spray E silicate 2874 7 1 8.6 1.688 76 Alkali 23 Spray E silicate 2875 7 1 12 1.731 72 Alkyl 21 Spray E silicate 2876 2 1 5.8 0.500 83 Alkali 19 Spray E silicate 2877 6 1 10 2.409 50 Alkyl 21 Spray E silicate 2878 6 1 1 12.750 72 Alkali 19 Spray E silicate 2879 7 1 10.5 1.113 50 Acrylic resin 654 Spray E 2880 6 1 6.5 1.133 48 Alkali 700 Spray E silicate 2881 7 1 19.5 1.195 75 Alkyl 555 Spray E silicate 2882 7 1 0.8 10.222 55 Alkyl 12 Spray E silicate 2883 6 1 5.3 0.013 38 Alkyl 678 Brush E silicate 2884 7 1 4.3 2.868 48 Urethane 674 Spray E resin 2885 2 1 3.2 1.524 76 Polyester 325 Spray E resin 2886 7 1 1.5 1.280 72 Alkyl 665 Spray E silicate 2887 7 1 4.5 1.109 75 Alkyl 354 Brush E silicate 2888 2 1 0.8 9.333 76 Alkyl 165 Spray E silicate 2889 6 1 6.5 3.667 72 Urethane 354 Spray E resin

TABLE 146 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2890 16.5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 2891 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 2892 0.96 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes Yes 2893 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 2894 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 2895 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 2896 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 2897 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 2898 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 2899 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 2900 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 2901 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 2902 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 2903 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 2904 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 2905 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 2906 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 2907 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 2908 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 2909 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2890 2 1 5 1.867 49 Alkyl 14 Spray E silicate 2891 2 1 198.7 0.047 89 Urethane 55 Spray E resin 2892 2 1 36 0.500 90 Alkyl 8 Spray E silicate 2893 2 1 1.5 0.012 86 Urethane 122 Brush E resin 2894 6 1 0.008 1.587 48 Alkyl 555 Spray E silicate 2895 6 1 1.4 2.833 47 Alkali 19 Spray E silicate 2896 7 1 4.2 2.673 47 Alkyl 25 Brush E silicate 2897 6 1 1.6 0.731 47 Alkyl 58 Spray E silicate 2898 2 1 7.5 0.671 52 Alkyl 685 Spray E silicate 2899 7 1 1.6 3.538 52 Alkali 19 Brush E silicate 2900 2 1 2 5.133 52 Urethane 700 Spray E resin 2901 6 1 270 0.069 88 Alkyl 77 Spray E silicate 2902 6 1 7.5 0.424 87 Alkyl 54 Spray E silicate 2903 2 1 2.9 1.385 89 Alkyl 64 Spray E silicate 2904 2 1 2.6 2.111 90 Alkyl 34 Brush E silicate 2905 7 1 0.1 22.273 91 Alkali 28 Spray E silicate 2906 6 1 1.2 8.000 46 Urethane 109 Brush E resin 2907 7 1 1.2 0.636 47 Alkyl 15 Spray E silicate 2908 2 1 62 0.341 47 Alkyl 14 Spray E silicate 2909 7 1 2.4 3.059 49 Alkyl 18 Spray E silicate

TABLE 147 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2910 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 2911 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 2912 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 2913 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 2914 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 2915 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 2916 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 2917 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 2918 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 2919 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 2920 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 2921 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 2922 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 2923 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 2924 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 2925 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 2926 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 2927 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 2928 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 2929 16.5 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2910 6 1 2.1 4.129 50 Alkali 2 Spray G silicate 2911 7 1 34.5 0.220 87 Alkyl 37 Spray E silicate 2912 6 1 270 0.109 83 Alkali 12 Spray E silicate 2913 7 1 32.5 0.254 48 Alkyl 160 Brush E silicate 2914 6 1 3 6.375 51 Alkali 5 Brush G silicate 2915 2 1 1.5 0.028 51 Alkyl 56 Brush E silicate 2916 7 1 7.5 1.271 87 Alkali 2 Spray G silicate 2917 6 1 13.5 0.772 85 Alkyl 18 Spray E silicate 2918 6 1 5 4.083 86 Alkyl 23 Spray E silicate 2919 6 1 5 2.900 50 Epoxy resin 30 Brush E 2920 2 1 1 0.650 51 Acrylic resin 77 Brush E 2921 6 1 120 0.161 51 Urethane 655 Brush E resin 2922 7 1 3.7 2.298 80 Polyester 47 Spray E resin 2923 2 1 6.1 1.676 46 Epoxy resin 43 Spray E 2924 6 1 198.5 0.048 51 Acrylic resin 52 Brush E 2925 2 1 2.5 3.000 86 Urethane 20 Brush E resin 2926 6 1 18.5 0.774 85 Polyester 200 Brush E resin 2927 7 1 8 1.867 82 Alkali 22 Spray E silicate 2928 7 1 1.6 4.077 81 Alkyl 25 Spray E silicate 2929 2 1 1.2 6.045 46 Alkali 14 Spray E silicate

TABLE 148 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2930 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 2931 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 2932 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 2933 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 2934 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 2935 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 2936 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 2937 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 2938 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 2939 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 2940 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 2941 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 2942 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 2943 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 2944 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 2945 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 2946 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 2947 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 2948 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 2949 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2930 2 1 0.5 0.933 47 Urethane 112 Spray E resin 2931 6 1 9 2.350 48 Alkali 24 Spray E silicate 2932 7 1 4.5 1.618 51 Urethane 150 Spray E resin 2933 6 1 136 0.109 53 Alkali 18 Spray E silicate 2934 7 1 13 1.314 88 Alkyl 19 Brush E silicate 2935 6 1 10.6 0.181 85 Alkyl 24 Spray E silicate 2936 2 1 1.6 2.000 83 Urethane 99 Spray E resin 2937 2 1 68 0.223 82 Alkyl 7 Spray E silicate 2938 6 1 4.5 1.945 83 Epoxy resin 100 Spray E 2939 7 1 10.5 1.452 47 Alkyl 27 Brush E silicate 2940 6 1 4.9 3.322 51 Alkali 15 Spray E silicate 2941 6 1 10.5 1.261 52 Alkyl 14 Spray E silicate 2942 2 1 192 0.074 51 Urethane 55 Spray E resin 2943 7 1 0.07 11.869 52 Alkyl 8 Spray E silicate 2944 2 1 9.5 1.000 89 Urethane 122 Brush E resin 2945 2 1 2.6 3.278 85 Alkyl 54 Spray E silicate 2946 6 1 4.5 2.327 82 Alkali 19 Spray E silicate 2947 7 1 3 1.550 87 Alkyl 25 Brush E silicate 2948 7 1 7.5 1.906 88 Alkyl 58 Spray E silicate 2949 6 1 77 0.251 49 Alkyl 21 Spray E silicate

TABLE 149 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2950 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 2951 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 2952 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 2953 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 2954 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 2955 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 2956 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 2957 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 2958 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 2959 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 2960 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 2961 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 2962 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 2963 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 2964 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 2965 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 2966 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 2967 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 2968 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 2969 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2950 7 1 10.5 1.078 50 Alkali 19 Brush E silicate 2951 7 1 15.5 0.648 51 Urethane 56 Spray E resin 2952 6 1 5.8 1.250 52 Alkyl silicate 77 Spray E 2953 7 1 1.9 1.759 53 Alkyl 12 Spray E silicate 2954 2 1 16.9 1.369 88 Alkyl 64 Spray E silicate 2955 7 1 1.5 5.400 85 Alkyl 34 Brush E silicate 2956 7 1 0.05 19.048 83 Alkali 28 Spray E silicate 2957 2 1 215 0.072 81 Urethane 109 Brush E resin 2958 6 1 4.2 2.019 80 Alkyl 15 Spray E silicate 2959 6 1 1.5 3.160 47 Alkyl 14 Spray E silicate 2960 7 1 4.8 0.828 49 Alkyl 18 Spray E silicate 2961 7 1 0.5 12.267 50 Urethane 122 Brush E resin 2962 6 1 2.3 3.848 51 Alkyl 54 Spray E silicate 2963 7 1 0.05 9.810 52 Alkali 19 Spray E silicate 2964 2 1 120 0.172 83 Alkyl 25 Brush E silicate 2965 2 1 3.7 0.532 88 Alkyl 58 Spray E silicate 2966 6 1 16.5 0.869 85 Alkyl 21 Spray E silicate 2967 7 1 24 0.768 83 Alkali 19 Brush E silicate 2968 6 1 0.01 13.366 82 Urethane 56 Spray E resin 2969 2 1 7.8 1.352 47 Alkyl 77 Spray E silicate

TABLE 150 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2970 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 2971 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 2972 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 2973 9.64 2.49 9.54 53.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 2974 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 2975 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 2976 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 2977 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 2978 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 2979 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 2980 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 2981 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 2982 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 2983 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 2984 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 2985 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 2986 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 2987 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 2988 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 2989 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2970 2 1 1.6 4.077 46 Alkyl silicate 54 Spray E 2971 7 1 3.2 3.667 49 Alkali 2 Spray G silicate 2972 6 1 5.4 0.406 50 Alkali 20 Spray E silicate 2973 7 1 220 0.076 51 Alkali 5 Spray G silicate 2974 7 1 2.2 2.531 83 Alkyl 20 Spray E silicate 2975 6 1 2.8 3.605 82 Alkali 15 Brush E silicate 2976 2 1 12 1.423 88 Alkyl 57 Brush E silicate 2977 7 1 10.6 0.207 85 Alkali 13 Brush E silicate 2978 2 1 35 0.303 86 Alkyl 22 Brush E silicate 2979 2 1 125.5 0.057 47 Alkali 20 Spray E silicate 2980 7 1 6 2.500 48 Alkyl 27 Spray E silicate 2981 2 1 34 0.417 50 Alkali 15 Spray E silicate 2982 7 1 1.6 3.615 51 Alkyl 35 Spray E silicate 2983 2 1 7.5 0.835 52 Alkali 34 Brush E silicate 2984 6 1 200 0.112 88 Alkyl 45 Brush E silicate 2985 6 1 7.5 1.612 89 Alkali 52 Brush E silicate 2986 7 1 3.2 3.071 86 Alkyl 23 Brush E silicate 2987 6 1 2.6 1.194 87 Alkali 5 Spray E silicate 2988 2 1 3 4.400 86 Alkyl 52 Brush E silicate 2989 2 1 15.2 0.037 46 Alkali 150 Brush E silicate

TABLE 151 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 2990 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 2991 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 2992 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 2993 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 2994 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 2995 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 2996 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 2997 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 2998 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 2999 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 3000 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 3001 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 3002 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 3003 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 3004 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 3005 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 3006 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 3007 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 3008 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 3009 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 2990 2 1 0.09 9.450 49 Alkyl silicate 60 Brush E 2991 2 1 13.5 0.483 35 Alkyl 15 Spray E silicate 2992 2 1 135.4 0.172 37 Alkyl 24 Spray E silicate 2993 2 1 3 4.375 36 Alkali 34 Spray E silicate 2994 6 1 7.8 1.409 38 Alkyl 20 Brush E silicate 2995 6 1 10.2 1.330 48 Alkali 200 Brush E silicate 2996 7 1 7 2.588 46 Alkyl 56 Brush E silicate 2997 6 1 225.2 0.038 51 Alkali 34 Spray E silicate 2998 2 1 5.4 2.219 46 Alkyl 2 Spray G silicate 2999 7 1 3.2 0.019 38 Alkali 15 Spray E silicate 3000 2 1 13.5 1.048 48 Alkali 10 Spray E silicate 3001 6 1 1.6 6.692 52 Alkyl 125 Brush E silicate 3002 6 1 1.5 0.320 30 Alkali 24 Brush E silicate 3003 2 1 2.5 1.829 76 Alkyl 110 Brush E silicate 3004 2 1 2.6 0.889 72 Alkali 24 Brush E silicate 3005 7 1 126 0.072 81 Alkyl 2 Spray G silicate 3006 6 1 120 0.159 64 Alkali 37 Spray E silicate 3007 7 1 7.5 1.776 69 Alkyl 113 Brush E silicate 3008 2 1 6.5 1.933 83 Alkali 2 Spray G silicate 3009 7 1 20 0.500 30 Alkyl 75 Brush E silicate

TABLE 152 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 3010 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 3011 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 3012 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 3013 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 3014 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 3015 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 3016 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 3017 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 3018 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 3019 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 3020 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 3021 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 3022 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 3023 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 3024 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 3025 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 3026 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 3027 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 3028 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 3029 16.5 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 3010 6 1 0.007 7.448 83 Alkali 30 Brush E silicate 3011 7 1 9 0.610 75 Alkyl 34 Brush E silicate 3012 6 1 7.5 1.976 76 Epoxy resin 124 Brush E 3013 7 1 50 0.539 72 Acrylic resin 15 Spray E 3014 6 1 0.005 2.886 71 Urethane 23 Spray E resin 3015 2 1 25.6 0.169 82 Polyester 157 Brush E resin 3016 7 1 56.5 0.001 81 Epoxy resin 26 Spray E 3017 6 1 1.6 1.192 83 Acrylic resin 38 Spray E 3018 6 1 3 5.125 50 Urethane 160 Brush E resin 3019 6 1 100 0.292 72 Urethane 27 Brush E resin 3020 2 1 65.5 0.114 47 Epoxy resin 180 Brush E 3021 6 1 1.9 0.241 47 Acrylic resin 26 Spray E 3022 7 1 2.1 1.484 52 Urethane 180 Brush E resin 3023 2 1 10.5 0.722 52 Urethane 15 Spray E resin 3024 6 1 6.5 1.573 50 Epoxy resin 2 Spray G 3025 2 1 19.5 0.629 46 Acrylic resin 28 Spray E 3026 6 1 0.8 0.333 47 Urethane 30 Spray E resin 3027 7 1 18.5 0.487 83 Urethane 2 Spray G resin 3028 7 1 4.3 2.208 52 Epoxy resin 157 Brush E 3029 2 1 3.2 2.238 89 Acrylic resin 28 Brush E

TABLE 153 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 3030 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 3031 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 3032 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 3033 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 3034 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 3035 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 3036 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 3037 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 3038 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 3039 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 3040 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 3041 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 3042 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 3043 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 3044 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 3045 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 3046 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 3047 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 3048 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 3049 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 3030 2 1 1.5 4.680 85 Alkyl 130 Brush E silicate 3031 6 1 4.5 0.764 53 Alkyl 29 Brush E silicate 3032 7 1 15.5 0.170 88 Epoxy resin 30 Brush E 3033 6 1 10.5 1.209 85 Acrylic resin 120 Brush E 3034 7 1 2.5 4.171 52 Urethane 187 Brush E resin 3035 6 1 9 2.640 83 Polyester 28 Spray E resin 3036 2 1 10.5 0.156 88 Epoxy resin 5 Spray E 3037 2 1 5.7 2.910 49 Acrylic resin 35 Spray E 3038 6 1 3.9 0.327 50 Urethane 5 Spray G resin 3039 7 1 4.5 1.091 51 Polyester 200 Brush E resin 3040 6 1 3.6 1.826 83 Alkali 25 Spray E silicate 3041 6 1 16.4 0.764 82 Alkali 15 Spray E silicate 3042 2 1 6 2.657 88 Alkyl 20 Spray E silicate 3043 7 1 7.5 0.212 85 Alkali 18 Spray E silicate 3044 2 1 10.5 0.357 87 Alkyl 22 Spray E silicate 3045 2 1 2.6 4.639 86 Alkali 19 Spray E silicate 3046 6 1 1.5 0.160 46 Alkyl 29 Spray E silicate 3047 7 1 13.5 0.731 49 Alkali 23 Spray E silicate 3048 7 1 2.6 1.917 35 Alkyl 21 Spray E silicate 3049 6 1 6.5 0.007 30 Alkali 19 Spray E silicate

TABLE 154 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 3050 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 3051 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 3052 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 3053 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 3054 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 3055 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 3056 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 3057 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 3058 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 3059 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 3060 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 3061 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 3062 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 3063 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 3064 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 3065 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 3066 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 3067 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 3068 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 3069 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 3070 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes Ratio of (Zn metal grains or Zn alloy grains):(Later- Coating details added Mg Total Zn metal grains) content metal Zn metal Later- of all grain grains/ added Zn metal content Coat Invention Number of Zn alloy metal grains of coat Base resin thickness Coating Corrosion Example No faces grains grains (Mass %) (Mass %) type (μm) method Test Results 3050 7 1 1.6 2.462 76 Alkyl 15 Spray E silicate 3051 7 1 3.8 0.729 72 Alkali 18 Spray E silicate 3052 6 1 0.08 16.204 30 Alkyl 22 Spray E silicate 3053 7 1 164.5 0.022 83 Alkyl 21 Spray E silicate 3054 2 1 3.6 1.283 75 Alkyl 29 Spray E silicate 3055 7 1 8.6 1.688 76 Alkali 23 Spray E silicate 3056 7 1 12 1.731 72 Alkyl 21 Spray E silicate 3057 2 1 5.8 0.500 83 Alkali 19 Spray E silicate 3058 6 1 10 2.409 50 Alkyl 21 Spray E silicate 3059 6 1 1 12.750 72 Alkali 19 Spray E silicate 3060 6 1 10.5 1.113 50 Acrylic resin 654 Spray E 3061 7 1 6.5 1.133 48 Alkali 700 Spray E silicate 3062 7 1 19.5 1.195 75 Alkyl 555 Spray E silicate 3063 6 1 0.8 10.222 55 Alkyl 12 Spray E silicate 3064 7 1 5.3 0.013 38 Alkyl 678 Brush E silicate 3065 2 1 4.3 2.868 48 Urethane 674 Spray E resin 3066 7 1 3.2 1.524 76 Polyester 325 Spray E resin 3067 7 1 1.5 1.280 72 Alkyl 665 Spray E silicate 3068 2 1 4.5 1.109 75 Alkyl 354 Brush E silicate 3069 6 1 0.8 9.333 76 Alkyl 165 Spray E silicate 3070 6 1 6.5 3.667 72 Urethane 354 Spray E resin

TABLE 155 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 3071 16.5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 3072 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 3073 0.96 2.56 9.84 6.55 81.45 18.5 0 0.5 Yes 1.22 Yes Yes 3074 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 3075 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 3076 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 3077 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 3078 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 3079 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 3080 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 3081 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 3082 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 3083 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 3084 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 3085 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 3086 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 3087 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 3088 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 3089 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 3090 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Number of Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No faces grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3071 2 1 5 1.867 55.7 49 Alkyl 14 Spray E silicate 3072 2 1 198.7 0.047 64.5 89 Urethane 55 Spray E resin 3073 2 1 36 0.500 68.9 90 Alkyl 8 Spray E silicate 3074 2 1 1.5 0.012 64.7 86 Urethane 122 Brush E resin 3075 6 1 0.008 1.587 77.9 48 Alkyl 555 Spray E silicate 3076 6 1 1.4 2.833 43.7 47 Alkali 19 Spray E silicate 3077 7 1 4.2 2.673 7.8 47 Alkyl 25 Brush E silicate 3078 6 1 1.6 0.731 16.0 47 Alkyl 58 Spray E silicate 3079 2 1 7.5 0.671 89.6 52 Alkyl 685 Spray E silicate 3080 7 1 1.6 3.538 11.8 52 Alkali 19 Brush E silicate 3081 2 1 2 5.133 4.6 52 Urethane 700 Spray E resin 3082 6 1 270 0.069 2.5 88 Alkyl 77 Spray E silicate 3083 6 1 7.5 0.424 18.9 87 Alkyl 54 Spray E silicate 3084 2 1 2.9 1.385 75.9 89 Alkyl 64 Spray E silicate 3085 2 1 2.6 2.111 55.9 90 Alkyl 34 Brush E silicate 3086 7 1 0.1 22.273 53.8 91 Alkali 28 Spray E silicate 3087 6 1 1.2 8.000 97.5 46 Urethane 109 Brush E resin 3088 7 1 1.2 0.636 88.4 47 Alkyl 15 Spray E silicate 3089 2 1 62 0.341 54.8 47 Alkyl 14 Spray E silicate 3090 7 1 2.4 3.059 45.7 49 Alkyl 18 Spray E silicate

TABLE 156 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 3091 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 3092 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 3093 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 3094 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 3095 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 3096 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 3097 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 3098 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 3099 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 3100 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 3101 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 3102 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 3103 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 3104 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 3105 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 3106 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 3107 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 3108 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 3109 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 3110 16.5 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Number of Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No faces grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3091 6 1 2.1 4.129 34.7 50 Alkali 2 Spray G silicate 3092 7 1 34.5 0.220 57.9 87 Alkyl 37 Spray E silicate 3093 6 1 270 0.109 65.4 83 Alkali 12 Spray E silicate 3094 7 1 32.5 0.254 87.9 48 Alkyl 160 Brush E silicate 3095 6 1 3 6.375 2.9 51 Alkali 5 Brush G silicate 3096 2 1 1.5 0.028 12.6 51 Alkyl 56 Brush E silicate 3097 7 1 7.5 1.271 53.8 87 Alkali 2 Spray G silicate 3098 6 1 13.5 0.772 17.8 85 Alkyl 18 Spray E silicate 3099 6 1 5 4.083 34.7 86 Alkyl 23 Spray E silicate 3100 6 1 5 2.900 76.8 50 Epoxy 30 Brush E resin 3101 2 1 1 0.650 58.9 51 Acrylic 77 Brush E resin 3102 6 1 120 0.161 50.8 51 Urethane 655 Brush E resin 3103 7 1 3.7 2.298 46.8 80 Polyester 47 Spray E resin 3104 2 1 6.1 1.676 23.7 46 Epoxy 43 Spray E resin 3105 6 1 198.5 0.048 53.8 51 Acrylic 52 Brush E resin 3106 2 1 2.5 3.000 53.8 86 Urethane 20 Brush E resin 3107 6 1 18.5 0.774 43.7 85 Polyester 200 Brush E resin 3108 7 1 8 1.867 55.9 82 Alkali 22 Spray E silicate 3109 7 1 1.6 4.077 65.8 81 Alkyl 25 Spray E silicate 3110 2 1 1.2 6.045 55.7 46 Alkali 14 Spray E silicate

TABLE 157 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and Average diameter) of grains Zn—Mg Any of diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, metal (μm) Zn alloy grains surfaces present MgZn, Invention grains Fine Coarse grains (Mass %) or cracks Average on grain Mg7Zn3 Example No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? 3111 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 3112 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 3113 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 3114 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 3115 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 3116 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 3117 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 3118 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 3119 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 3120 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 3121 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 3122 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 3123 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 3124 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 3125 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 3126 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 3127 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 3128 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 3129 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 3130 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Number of Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No faces grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3111 2 1 0.5 0.933 64.5 47 Urethane 112 Spray E resin 3112 6 1 9 2.350 68.9 48 Alkali 24 Spray E silicate 3113 7 1 4.5 1.618 64.7 51 Urethane 150 Spray E resin 3114 6 1 136 0.109 77.9 53 Alkali 18 Spray E silicate 3115 7 1 13 1.314 43.7 88 Alkyl 19 Brush E silicate 3116 6 1 10.6 0.181 7.8 85 Alkyl 24 Spray E silicate 3117 2 1 1.6 2.000 16.0 83 Urethane 99 Spray E resin 3118 2 1 68 0.223 89.6 82 Alkyl 7 Spray E silicate 3119 6 1 4.5 1.945 11.8 83 Epoxy 100 Spray E resin 3120 7 1 10.5 1.452 4.6 47 Alkyl 27 Brush E silicate 3121 6 1 4.9 3.322 2.5 51 Alkali 15 Spray E silicate 3122 6 1 10.5 1.261 18.9 52 Alkyl 14 Spray E silicate 3123 2 1 192 0.074 75.9 51 Urethane 55 Spray E resin 3124 7 1 0.07 11.869 55.9 52 Alkyl 8 Spray E silicate 3125 2 1 9.5 1.000 53.8 89 Urethane 122 Brush E resin 3126 2 1 2.6 3.278 97.5 85 Alkyl 54 Spray E silicate 3127 6 1 4.5 2.327 88.4 82 Alkali 19 Spray E silicate 3128 7 1 3 1.550 54.8 87 Alkyl 25 Brush E silicate 3129 7 1 7.5 1.906 45.7 88 Alkyl 58 Spray E silicate 3130 6 1 77 0.251 34.7 49 Alkyl 21 Spray E silicate

TABLE 158 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3131 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 7 3132 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 7 3133 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 6 3134 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 7 3135 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 2 3136 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 7 3137 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 7 3138 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 2 3139 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 6 3140 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 6 3141 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 7 3142 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 7 3143 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 6 3144 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 7 3145 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 2 3146 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 2 3147 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 6 3148 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 7 3149 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 6 3150 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes 2 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3131 1 10.5 1.078 57.9 50 Alkali 19 Brush E silicate 3132 1 15.5 0.648 65.4 51 Urethane 56 Spray E resin 3133 1 5.8 1.250 87.9 52 Alkyl 77 Spray E silicate 3134 1 1.9 1.759 2.9 53 Alkyl 12 Spray E silicate 3135 1 16.9 1.369 12.6 88 Alkyl 64 Spray E silicate 3136 1 1.5 5.400 53.8 85 Alkyl 34 Brush E silicate 3137 1 0.05 19.048 17.8 83 Alkali 28 Spray E silicate 3138 1 215 0.072 34.7 81 Urethane 109 Brush E resin 3139 1 4.2 2.019 55.7 80 Alkyl 15 Spray E silicate 3140 1 1.5 3.160 64.5 47 Alkyl 14 Spray E silicate 3141 1 4.8 0.828 68.9 49 Alkyl 18 Spray E silicate 3142 1 0.5 12.267 64.7 50 Urethane 122 Brush E resin 3143 1 2.3 3.848 77.9 51 Alkyl 54 Spray E silicate 3144 1 0.05 9.810 43.7 52 Alkali 19 Spray E silicate 3145 1 120 0.172 7.8 83 Alkyl 25 Brush E silicate 3146 1 3.7 0.532 16.0 88 Alkyl 58 Spray E silicate 3147 1 16.5 0.869 89.6 85 Alkyl 21 Spray E silicate 3148 1 24 0.768 11.8 83 Alkali 19 Brush E silicate 3149 1 0.01 13.366 4.6 82 Urethane 56 Spray E resin 3150 1 7.8 1.352 2.5 47 Alkyl 77 Spray E silicate

TABLE 159 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3151 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 2 3152 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 7 3153 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 6 3154 9.64 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 7 3155 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 7 3156 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 6 3157 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 2 3158 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 7 3159 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 2 3160 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 2 3161 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 7 3162 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 2 3163 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 7 3164 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 2 3165 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 6 3166 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 6 3167 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 7 3168 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 6 3169 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 2 3170 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes 2 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3151 1 1.6 4.077 18.9 46 Alkyl 54 Spray E silicate 3152 1 3.2 3.667 75.9 49 Alkali 2 Spray G silicate 3153 1 5.4 0.406 55.9 50 Alkali 20 Spray E silicate 3154 1 220 0.076 53.8 51 Alkali 5 Spray G silicate 3155 1 2.2 2.531 97.5 83 Alkyl 20 Spray E silicate 3156 1 2.8 3.605 88.4 82 Alkali 15 Brush E silicate 3157 1 12 1.423 54.8 88 Alkyl 57 Brush E silicate 3158 1 10.6 0.207 45.7 85 Alkali 13 Brush E silicate 3159 1 35 0.303 34.7 86 Alkyl 22 Brush E silicate 3160 1 125.5 0.057 57.9 47 Alkali 20 Spray E silicate 3161 1 6 2.500 65.4 48 Alkyl 27 Spray E silicate 3162 1 34 0.417 87.9 50 Alkali 15 Spray E silicate 3163 1 1.6 3.615 2.9 51 Alkyl 35 Spray E silicate 3164 1 7.5 0.835 12.6 52 Alkali 34 Brush E silicate 3165 1 200 0.112 53.8 88 Alkyl 45 Brush E silicate 3166 1 7.5 1.612 17.8 89 Alkali 52 Brush E silicate 3167 1 3.2 3.071 34.7 86 Alkyl 23 Brush E silicate 3168 1 2.6 1.194 76.8 87 Alkali 5 Spray E silicate 3169 1 3 4.400 58.9 86 Alkyl 52 Brush E silicate 3170 1 15.2 0.037 50.8 46 Alkali 150 Brush E silicate

TABLE 160 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3171 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 2 3172 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 2 3173 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 2 3174 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 2 3175 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 6 3176 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 6 3177 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 7 3178 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 6 3179 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 2 3180 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 7 3181 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 2 3182 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 6 3183 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 6 3184 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 2 3185 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 2 3186 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 7 3187 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 6 3188 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 7 3189 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 2 3190 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes 7 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3171 1 0.09 9.450 46.8 49 Alkyl 60 Brush E silicate 3172 1 13.5 0.483 23.7 35 Alkali 15 Spray E silicate 3173 1 135.4 0.172 53.8 37 Alkyl 24 Spray E silicate 3174 1 3 4.375 53.8 36 Alkali 34 Spray E silicate 3175 1 7.8 1.409 43.7 38 Alkyl 20 Brush E silicate 3176 1 10.2 1.330 55.9 48 Alkali 200 Brush E silicate 3177 1 7 2.588 65.8 46 Alkyl 56 Brush E silicate 3178 1 225.2 0.038 55.7 51 Alkali 34 Spray E silicate 3179 1 5.4 2.219 64.5 46 Alkyl 2 Spray G silicate 3180 1 3.2 0.019 68.9 38 Alkali 15 Spray E silicate 3181 1 13.5 1.048 64.7 48 Alkali 10 Spray E silicate 3182 1 1.6 6.692 77.9 52 Alkyl 125 Brush E silicate 3183 1 1.5 0.320 43.7 30 Alkali 24 Brush E silicate 3184 1 2.5 1.829 7.8 76 Alkyl 110 Brush E silicate 3185 1 2.6 0.889 16.0 72 Alkali 24 Brush E silicate 3186 1 126 0.072 89.6 81 Alkyl 2 Spray G silicate 3187 1 120 0.159 11.8 64 Alkali 37 Spray E silicate 3188 1 7.5 1.776 4.6 69 Alkyl 113 Brush E silicate 3189 1 6.5 1.933 2.5 83 Alkali 2 Spray G silicate 3190 1 20 0.500 18.9 30 Alkyl 75 Brush E silicate

TABLE 161 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3191 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 6 3192 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 7 3193 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 6 3194 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 7 3195 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 6 3196 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 2 3197 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 7 3198 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 6 3199 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 6 3200 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 6 3201 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 2 3202 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 6 3203 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 7 3204 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 2 3205 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 6 3206 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 2 3207 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 6 3208 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 7 3209 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 7 3210 16.5 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes 2 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3191 1 0.007 7.448 75.9 83 Alkali 30 Brush E silicate 3192 1 9 0.610 55.9 75 Alkyl 34 Brush E silicate 3193 1 7.5 1.976 53.8 76 Epoxy 124 Brush E resin 3194 1 50 0.539 97.5 72 Acrylic 15 Spray E resin 3195 1 0.005 2.886 88.4 71 Urethane 23 Spray E resin 3196 1 25.6 0.169 54.8 82 Polyester 157 Brush E resin 3197 1 56.5 0.001 45.7 81 Epoxy 26 Spray E resin 3198 1 1.6 1.192 34.7 83 Acrylic 38 Spray E resin 3199 1 3 5.125 57.9 50 Urethane 160 Brush E resin 3200 1 100 0.292 65.4 72 Polyester 27 Brush E resin 3201 1 65.5 0.114 87.9 47 Epoxy 180 Brush E resin 3202 1 1.9 0.241 2.9 47 Acrylic 26 Spray E resin 3203 1 2.1 1.484 12.6 52 Urethane 180 Brush E resin 3204 1 10.5 0.722 53.8 52 Polyester 15 Spray E resin 3205 1 6.5 1.573 17.8 50 Epoxy 2 Spray G resin 3206 1 19.5 0.629 34.7 46 Acrylic 28 Spray E resin 3207 1 0.8 0.333 55.7 47 Urethane 30 Spray E resin 3208 1 18.5 0.487 64.5 83 Polyester 2 Spray G resin 3209 1 4.3 2.208 68.9 52 Epoxy 157 Brush E resin 3210 1 3.2 2.238 64.7 89 Acrylic 28 Brush E resin

TABLE 162 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3211 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 2 3212 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 6 3213 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 7 3214 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 6 3215 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 7 3216 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 6 3217 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 2 3218 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 2 3219 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 6 3220 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 7 3221 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 6 3222 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 6 3223 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 2 3224 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 7 3225 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 2 3226 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 2 3227 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 6 3228 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 7 3229 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 7 3230 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes 6 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3211 1 1.5 4.680 77.9 85 Alkyl 130 Brush E silicate 3212 1 4.5 0.764 43.7 53 Alkyl 29 Brush E silicate 3213 1 15.5 0.170 7.8 88 Epoxy 30 Brush E resin 3214 1 10.5 1.209 16.0 85 Acrylic 120 Brush E resin 3215 1 2.5 4.171 89.6 52 Urethane 187 Brush E resin 3216 1 9 2.640 11.8 83 Polyester 28 Spray E resin 3217 1 10.5 0.156 4.6 88 Epoxy 5 Spray E resin 3218 1 5.7 2.910 2.5 49 Acrylic 35 Spray E resin 3219 1 3.9 0.327 18.9 50 Urethane 5 Spray G resin 3220 1 4.5 1.091 75.9 51 Polyester 200 Brush E resin 3221 1 3.6 1.826 55.9 83 Alkali 25 Spray E silicate 3222 1 16.4 0.764 53.8 82 Alkali 15 Spray E silicate 3223 1 6 2.657 97.5 88 Alkyl 20 Spray E silicate 3224 1 7.5 0.212 88.4 85 Alkali 18 Spray E silicate 3225 1 10.5 0.357 54.8 87 Alkyl 22 Spray E silicate 3226 1 2.6 4.639 45.7 86 Alkali 19 Spray E silicate 3227 1 1.5 0.160 34.7 46 Alkyl 29 Spray E silicate 3228 1 13.5 0.731 57.9 49 Alkali 23 Spray E silicate 3229 1 2.6 1.917 65.4 35 Alkyl 21 Spray E silicate 3230 1 6.5 0.007 87.9 30 Alkali 19 Spray E silicate

TABLE 163 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3231 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 7 3232 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 7 3233 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 6 3234 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 7 3235 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 2 3236 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 7 3237 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 7 3238 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 2 3239 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 6 3240 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 6 3241 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 6 3242 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 7 3243 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 7 3244 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 6 3245 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 7 3246 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 2 3247 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 7 3248 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 7 3249 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 2 3250 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 6 3251 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes 6 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3231 1 1.6 2.462 2.9 76 Alkyl 15 Spray E silicate 3232 1 3.8 0.729 12.6 72 Alkali 18 Spray E silicate 3233 1 0.08 16.204 53.8 30 Alkyl 22 Spray E silicate 3234 1 164.5 0.022 17.8 83 Alkyl 21 Spray E silicate 3235 1 3.6 1.283 34.7 75 Alkyl 29 Spray E silicate 3236 1 8.6 1.688 76.8 76 Alkali 23 Spray E silicate 3237 1 12 1.731 58.9 72 Alkyl 21 Spray E silicate 3238 1 5.8 0.500 50.8 83 Alkali 19 Spray E silicate 3239 1 10 2.409 46.8 50 Alkyl 21 Spray E silicate 3240 1 1 12.750 23.7 72 Alkali 19 Spray E silicate 3241 1 10.5 1.113 87.9 50 Acrylic 654 Spray E resin 3242 1 6.5 1.133 2.9 48 Alkali 700 Spray E silicate 3243 1 19.5 1.195 12.6 75 Alkyl 555 Spray E silicate 3244 1 0.8 10.222 53.8 55 Alkyl 12 Spray E silicate 3245 1 5.3 0.013 17.8 38 Alkyl 152 Brush E silicate 3246 1 4.3 2.868 34.7 48 Urethane 674 Spray E resin 3247 1 3.2 1.524 76.8 76 Polyester 325 Spray E resin 3248 1 1.5 1.280 58.9 72 Alkyl 665 Spray E silicate 3249 1 4.5 1.109 50.8 75 Alkyl 354 Brush E silicate 3250 1 0.8 9.333 46.8 76 Alkyl 165 Spray E silicate 3251 1 6.5 3.667 23.7 72 Urethane 354 Spray E resin

TABLE 164 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3252 16.5 2.35 9.25 35.87 88.8 11.2 0 0 Yes 1.12 Yes Yes 2 3253 13.5 2.57 9.56 42.04 90.6 9.4 0 0 No 1.38 Yes Yes 2 3254 0.96 2.56 9.84 6.55 81.45 18.5 0 0.05 Yes 1.22 Yes Yes 2 3255 0.96 2.21 9.75 43.60 99.97 0.03 0 0 Yes 1.14 Yes Yes 2 3256 8.45 2.64 9.85 44.12 98.4 1.6 0 0 No 1.02 Yes Yes 6 3257 2.9 1.99 8.56 37.21 93.2 6.8 0 0 Yes 1.05 Yes Yes 6 3258 5.4 2.94 8.21 43.38 84.5 13.9 0 1.6 No 1.36 No Yes 7 3259 10.6 2.58 8.33 13.52 98.1 1.9 0 0 Yes 1.11 No Yes 6 3260 2.32 2.37 8 44.94 94.3 5.7 0 0 No 1.07 Yes Yes 2 3261 7.8 2.15 9.22 45.46 90.8 9.2 0 0 No 1.42 Yes Yes 7 3262 7.95 2.96 9.36 35.96 83.3 15.4 0 1.3 Yes 1.38 No Yes 2 3263 20.59 2.85 9.45 42.13 79.84 18.6 0 1.56 Yes 1.22 No Yes 6 3264 22.5 2.94 9.61 7.56 96.4 3.6 0 0 Yes 1.14 Yes Yes 6 3265 4.6 2.11 9.85 43.69 94.6 5.4 0 0 Yes 1.13 Yes Yes 2 3266 4.9 2.68 9.23 44.21 92.4 7.6 0 0 Yes 1.02 No Yes 2 3267 10.5 2.99 9.08 39.51 75.5 24.5 0 0 Yes 1.06 Yes Yes 7 3268 8.45 2.78 9.87 45.68 82.4 17.6 0 0 Yes 1.05 Yes Yes 6 3269 30.5 2.96 9.46 65.58 98.6 1.4 0 0 Yes 1.24 No Yes 7 3270 49.5 2.85 9.28 47.24 78.5 21.5 0 0 Yes 1.33 No Yes 2 3271 5.9 2.64 9.45 47.76 89.6 10.4 0 0 Yes 1.27 Yes Yes 7 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3252 1 5 1.867 55.7 49 Alkyl 14 Spray E silicate 3253 1 198.7 0.047 64.5 89 Urethane 55 Spray E resin 3254 1 36 0.500 68.9 90 Alkyl 8 Spray E silicate 3255 1 1.5 0.012 64.7 86 Urethane 122 Brush E resin 3256 1 0.008 1.587 77.9 48 Alkyl 555 Spray E silicate 3257 1 1.4 2.833 43.7 47 Alkali 19 Spray E silicate 3258 1 4.2 2.673 7.8 47 Alkyl 25 Brush E silicate 3259 1 1.6 0.731 16.0 47 Alkyl 58 Spray E silicate 3260 1 7.5 0.671 89.6 52 Alkyl 685 Spray E silicate 3261 1 1.6 3.538 11.8 52 Alkali 19 Brush E silicate 3262 1 2 5.133 4.6 52 Urethane 700 Spray E resin 3263 1 270 0.069 2.5 88 Alkyl 77 Spray E silicate 3264 1 7.5 0.424 18.9 87 Alkyl 54 Spray E silicate 3265 1 2.9 1.385 75.9 89 Alkyl 64 Spray E silicate 3266 1 2.6 2.111 55.9 90 Alkyl 34 Brush E silicate 3267 1 0.1 22.273 53.8 91 Alkali 28 Spray E silicate 3268 1 1.2 8.000 97.5 46 Urethane 109 Brush E resin 3269 1 1.2 0.636 88.4 47 Alkyl 15 Spray E silicate 3270 1 62 0.341 54.8 47 Alkyl 14 Spray E silicate 3271 1 2.4 3.059 45.7 49 Alkyl 18 Spray E silicate

TABLE 165 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3272 4.52 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 6 3273 5.96 2.12 9.46 47.02 92.2 7.8 0 0 Yes 1.22 No Yes 7 3274 5.5 2.34 9.46 7.66 70.5 29.5 0 0 Yes 1.13 No Yes 6 3275 3.6 2.33 9.46 15.20 91.5 8.5 0 0 Yes 1.06 Yes Yes 7 3276 16.5 2.23 9.06 43.16 74.5 25.5 0 0 Yes 1.05 Yes Yes 6 3277 12.5 2.12 9.3 49.33 99.93 0.07 0 0 Yes 1.24 Yes Yes 2 3278 16.5 2.21 8.68 19.47 89.2 10.8 0 0 No 1.05 Yes Yes 7 3279 10.9 1.38 8.53 69.55 86 11.2 1.6 1.2 No 1.12 Yes Yes 6 3280 5.6 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 No Yes 6 3281 22.6 2.26 8.95 75.88 82.6 17.4 0 0 Yes 1.13 No Yes 6 3282 20.59 2.05 12.54 48.08 98.7 1.3 0 0 Yes 1.33 Yes Yes 2 3283 20.59 1.65 8.7 66.85 80.5 19.5 0 0 Yes 1.27 Yes Yes 6 3284 9.56 2.35 8.55 7.68 88.85 10.8 0.05 0.3 No 1.23 No Yes 7 3285 5.9 1.62 8.91 8.64 87.7 11.9 0.4 0 Yes 1.11 Yes Yes 2 3286 6.54 1.88 9.91 16.58 90.5 9.5 0 0 Yes 1.42 Yes Yes 6 3287 21.4 2.35 9.25 35.87 89.5 10.5 0 0 Yes 1.06 No Yes 2 3288 9.8 2.57 9.56 42.04 84.9 15.1 0 0 Yes 1.05 Yes Yes 6 3289 6.59 2.56 9.84 38.41 83.2 16.8 0 0 Yes 1.07 Yes Yes 7 3290 6.54 2.21 9.75 6.99 89.4 10.6 0 0 Yes 1.42 No Yes 7 3291 16.5 2.64 9.85 44.12 84.3 13.3 2.4 0 Yes 1.38 Yes Yes 2 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3272 1 2.1 4.129 34.7 50 Alkali 2 Spray G silicate 3273 1 34.5 0.220 57.9 87 Alkyl 37 Spray E silicate 3274 1 270 0.109 65.4 83 Alkali 12 Spray E silicate 3275 1 32.5 0.254 87.9 48 Alkyl 160 Brush E silicate 3276 1 3 6.375 2.9 51 Alkali 5 Brush G silicate 3277 1 1.5 0.028 12.6 51 Alkyl 56 Brush E silicate 3278 1 7.5 1.271 53.8 87 Alkali 2 Spray E silicate 3279 1 13.5 0.772 17.8 85 Alkyl 18 Spray E silicate 3280 1 5 4.083 34.7 86 Alkyl 23 Spray E silicate 3281 1 5 2.900 76.8 50 Epoxy 30 Brush E resin 3282 1 1 0.650 58.9 51 Acrylic 77 Brush E resin 3283 1 120 0.161 50.8 51 Urethane 655 Brush E resin 3284 1 3.7 2.298 46.8 80 Polyester 47 Spray E resin 3285 1 6.1 1.676 23.7 46 Epoxy 43 Spray E resin 3286 1 198.5 0.048 53.8 51 Acrylic 52 Brush E resin 3287 1 2.5 3.000 53.8 86 Urethane 20 Brush E resin 3288 1 18.5 0.774 43.7 85 Polyester 200 Brush E resin 3289 1 8 1.867 55.9 82 Alkali 22 Spray E silicate 3290 1 1.6 4.077 65.8 81 Alkyl 25 Spray E silicate 3291 1 1.2 6.045 55.7 46 Alkali 14 Spray E silicate

TABLE 166 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3292 7.8 2.65 8.56 66.99 98.6 1.4 0 0 No 1.22 Yes Yes 2 3293 16.5 2.94 8.21 43.38 76.45 23.5 0 0.05 Yes 1.14 Yes Yes 6 3294 6.54 2.58 8.33 39.75 91.1 8.9 0 0 Yes 1.13 Yes Yes 7 3295 8.45 2.37 8 65.38 85.1 14.9 0 0 Yes 1.02 Yes Yes 6 3296 8.5 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 7 3297 13.6 2.96 9.36 22.55 97.9 2.1 0 0 Yes 1.05 Yes Yes 6 3298 12.33 2.85 9.45 42.13 94.8 5.2 0 0 Yes 1.24 Yes Yes 2 3299 16.5 2.94 9.61 38.50 84.6 15.4 0 0 Yes 1.33 Yes Yes 2 3300 7.9 2.11 9.85 64.13 89.3 10.7 0 0 Yes 1.27 Yes Yes 6 3301 10.5 2.68 9.23 44.21 83.3 16.7 0 0 Yes 1.05 Yes Yes 7 3302 16.5 2.99 9.08 39.51 80.05 19.6 0.35 0 No 1.12 Yes Yes 6 3303 10.64 1.82 9.87 78.64 85.5 14.5 0 0 No 1.23 Yes Yes 6 3304 10.5 1.42 9.46 42.05 85 14.2 0 0.8 No 1.36 Yes Yes 2 3305 20.59 2.12 9.28 64.58 87.3 12.7 0 0 No 1.11 Yes Yes 7 3306 8.5 1.92 9.45 47.76 89.5 10.5 0 0 Yes 1.07 Yes Yes 2 3307 0.5 2.11 9.63 24.10 87.3 11.8 0 0.9 Yes 1.42 Yes Yes 2 3308 10.5 2.97 9.16 39.11 86.4 12.8 0.5 0.3 Yes 1.38 Yes Yes 6 3309 11.5 2.36 10.39 19.65 93.8 6.2 0 0 Yes 1.22 Yes Yes 7 3310 36.5 3.05 10.56 65.39 83.8 16.2 0 0 Yes 1.14 Yes Yes 7 3311 1.5 2.15 10.74 48.57 80.4 19.6 0 0 Yes 1.13 Yes Yes 6 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3292 1 0.5 0.933 64.5 47 Urethane 112 Spray E resin 3293 1 9 2.350 68.9 48 Alkali 24 Spray E silicate 3294 1 4.5 1.618 64.7 51 Urethane 150 Spray E resin 3295 1 136 0.109 77.9 53 Alkali 18 Spray E silicate 3296 1 13 1.314 43.7 88 Alkyl 19 Brush E silicate 3297 1 10.6 0.181 7.8 85 Alkyl 24 Spray E silicate 3298 1 1.6 2.000 16.0 83 Urethane 99 Spray E resin 3299 1 68 0.223 89.6 82 Alkyl 7 Spray E silicate 3300 1 4.5 1.945 11.8 83 Epoxy 100 Spray E resin 3301 1 10.5 1.452 4.6 47 Alkyl 27 Brush E silicate 3302 1 4.9 3.322 2.5 51 Alkali 15 Spray E silicate 3303 1 10.5 1.261 18.9 52 Alkyl 14 Spray E silicate 3304 1 192 0.074 75.9 51 Urethane 55 Spray E resin 3305 1 0.07 11.869 55.9 52 Alkyl 8 Spray E silicate 3306 1 9.5 1.000 53.8 89 Urethane 122 Brush E resin 3307 1 2.6 3.278 97.5 85 Alkyl 54 Spray E silicate 3308 1 4.5 2.327 88.4 82 Alkali 19 Spray E silicate 3309 1 3 1.550 54.8 87 Alkyl 25 Brush E silicate 3310 1 7.5 1.906 45.7 88 Alkyl 58 Spray E silicate 3311 1 77 0.251 34.7 49 Alkyl 21 Spray E silicate

TABLE 167 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3312 8.7 2.19 10.27 24.91 87.6 12.4 0 0 Yes 1.02 Yes Yes 7 3313 7.8 2.48 11.5 39.92 89.3 10.7 0 0 Yes 1.06 Yes Yes 7 3314 5.96 2.85 11.67 22.65 91.5 8.5 0 0 Yes 1.05 Yes Yes 6 3315 0.06 2.75 11.85 66.20 94.9 5.1 0 0 Yes 1.24 Yes Yes 7 3316 0.9 2.46 11.38 49.38 75.5 24.5 0 0 Yes 1.33 Yes Yes 2 3317 3.6 2.71 12.61 30.58 86.5 13.5 0 0 Yes 1.27 Yes Yes 7 3318 10.5 2.36 12.78 45.59 80 20 0 0 Yes 1.05 Yes Yes 7 3319 0.05 2.16 9.57 28.32 84.5 15.5 0 0 Yes 1.12 Yes Yes 2 3320 2.32 2.46 9.81 71.87 88 10.5 1.5 0 Yes 1.23 Yes Yes 6 3321 20.4 2.49 8.43 53.05 92.1 7.9 0 0 Yes 1.36 Yes Yes 6 3322 7.34 2.95 8.55 27.74 95.2 4.8 0 0 Yes 1.11 Yes Yes 7 3323 9.4 2.36 8.22 42.75 81.6 18.4 0 0 Yes 1.07 Yes Yes 7 3324 23.43 2.21 9.44 23.29 86.8 12.7 0 0.5 Yes 1.42 Yes Yes 6 3325 5.96 2.25 9.58 61.12 89.7 10.3 0 0 No 1.38 Yes Yes 7 3326 10.64 2.44 9.67 44.30 71.2 20.8 8 0 Yes 1.22 Yes Yes 2 3327 16.5 2.78 9.83 23.96 97.5 2.5 0 0 No 1.14 Yes Yes 2 3328 7.95 2.15 10.07 44.09 84.8 15.2 0 0 Yes 1.13 Yes Yes 6 3329 7.95 2.19 9.45 24.63 80.8 19.2 0 0 No 1.02 Yes Yes 7 3330 9.64 2.48 9.3 62.46 78.7 13.5 7.8 0 Yes 1.06 Yes Yes 6 3331 0.96 2.59 9.99 45.64 88.1 11.9 0 0 No 1.05 Yes Yes 2 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3312 1 10.5 1.078 57.9 50 Alkali 19 Brush E silicate 3313 1 15.5 0.648 65.4 51 Urethane 56 Spray E resin 3314 1 5.8 1.250 87.9 52 Alkyl 77 Spray E silicate 3315 1 1.9 1.759 2.9 53 Alkyl 12 Spray E silicate 3316 1 16.9 1.369 12.6 88 Alkyl 64 Spray E silicate 3317 1 1.5 5.400 53.8 85 Alkyl 34 Brush E silicate 3318 1 0.05 19.048 17.8 83 Alkali 28 Spray E silicate 3319 1 215 0.072 34.7 81 Urethane 109 Brush E resin 3320 1 4.2 2.019 55.7 80 Alkyl 15 Spray E silicate 3321 1 1.5 3.160 64.5 47 Alkyl 14 Spray E silicate 3322 1 4.8 0.828 68.9 49 Alkyl 18 Spray E silicate 3323 1 0.5 12.267 64.7 50 Urethane 122 Brush E resin 3324 1 2.3 3.848 77.9 51 Alkyl 54 Spray E silicate 3325 1 0.05 9.810 43.7 52 Alkali 19 Spray E silicate 3326 1 120 0.172 7.8 83 Alkyl 25 Brush E silicate 3327 1 3.7 0.532 16.0 88 Alkyl 58 Spray E silicate 3328 1 16.5 0.869 89.6 85 Alkyl 21 Spray E silicate 3329 1 24 0.768 11.8 83 Alkali 19 Brush E silicate 3330 1 0.01 13.366 4.6 82 Urethane 56 Spray E resin 3331 1 7.8 1.352 2.5 47 Alkyl 77 Spray E silicate

TABLE 168 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3332 5.26 2.47 9.58 25.30 88.5 10.6 0 0.9 Yes 1.24 Yes Yes 2 3333 13.5 2.69 9.4 42.84 84.6 15.4 0 0 Yes 1.33 Yes Yes 7 3334 13.5 2.57 9.57 25.44 97.4 2.6 0 0 Yes 1.27 Yes Yes 6 3335 9.64 2.49 9.54 63.27 83.3 16.7 0 0 Yes 1.37 Yes Yes 7 3336 16.5 2.68 9.58 46.45 91.9 8.1 0 0 Yes 1.10 Yes Yes 7 3337 20.59 2.35 9.25 46.45 86.3 13.7 0 0 Yes 1.04 Yes Yes 6 3338 0.96 2.48 10.04 50.91 81.5 18.5 0 0 Yes 1.02 Yes Yes 2 3339 6.54 2.13 11.27 27.25 97.6 2.4 0 0 Yes 1.01 Yes Yes 7 3340 5.26 1.93 11.44 42.26 89.1 10.9 0 0 Yes 1.08 Yes Yes 2 3341 10.64 2.05 8.9 33.69 92.8 7.2 0 0 Yes 1.14 Yes Yes 2 3342 9.64 1.42 8.75 48.70 81.96 17.5 0.5 0.04 No 1.23 Yes Yes 7 3343 6.9 1.46 9.44 29.24 85.4 14.6 0 0 No 1.33 Yes Yes 2 3344 10.5 1.75 9.03 67.07 90.6 9.4 0 0 Yes 1.37 Yes Yes 7 3345 13.5 1.86 8.85 50.25 92.9 7.1 0 0 Yes 1.44 Yes Yes 2 3346 20.59 1.74 8.95 29.91 77.5 22.5 0 0 Yes 1.21 Yes Yes 6 3347 7.82 1.96 12.54 87.50 84.8 13.7 1.5 0 No 1.22 Yes Yes 6 3348 5.26 1.65 8.7 30.58 87.1 12.9 0 0 No 1.23 Yes Yes 7 3349 7.06 2.35 8.55 68.41 95.7 4.3 0 0 Yes 1.47 Yes Yes 6 3350 0.64 1.62 10.72 54.59 80.2 17.6 1 1.2 No 1.01 Yes Yes 2 3351 46.8 2.25 9.9 34.25 98.8 0.6 0.6 0 Yes 1.04 Yes Yes 2 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3332 1 1.6 4.077 18.9 46 Alkyl 54 Spray E silicate 3333 1 3.2 3.667 75.9 49 Alkali 2 Spray G silicate 3334 1 5.4 0.406 55.9 50 Alkali 20 Spray E silicate 3335 1 220 0.076 53.8 51 Alkali 5 Spray G silicate 3336 1 2.2 2.531 97.5 83 Alkyl 20 Spray E silicate 3337 1 2.8 3.605 88.4 82 Alkali 15 Brush E silicate 3338 1 12 1.423 54.8 88 Alkyl 57 Brush E silicate 3339 1 10.6 0.207 45.7 85 Alkali 13 Brush E silicate 3340 1 35 0.303 34.7 86 Alkyl 22 Brush E silicate 3341 1 125.5 0.057 57.9 47 Alkali 20 Spray E silicate 3342 1 6 2.500 65.4 48 Alkyl 27 Spray E silicate 3343 1 34 0.417 87.9 50 Alkali 15 Spray E silicate 3344 1 1.6 3.615 2.9 51 Alkyl 35 Spray E silicate 3345 1 7.5 0.835 12.6 52 Alkali 34 Brush E silicate 3346 1 200 0.112 53.8 88 Alkyl 45 Brush E silicate 3347 1 7.5 1.612 17.8 89 Alkali 52 Brush E silicate 3348 1 3.2 3.071 34.7 86 Alkyl 23 Brush E silicate 3349 1 2.6 1.194 76.8 87 Alkali 5 Spray E silicate 3350 1 3 4.400 58.9 86 Alkyl 52 Brush E silicate 3351 1 15.2 0.037 50.8 46 Alkali 150 Brush E silicate

TABLE 169 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3352 16.5 2.36 9.57 37.61 86.9 10.3 1.6 1.2 Yes 1.05 Yes Yes 2 3353 13.5 2.24 10.79 45.60 92.98 7 0.02 0 Yes 1.12 Yes Yes 2 3354 0.96 2.46 10.93 46.70 75.5 23.5 1 0 Yes 1.11 Yes Yes 2 3355 0.96 1.56 11.02 41.22 82.5 17.5 0 0 No 1.08 Yes Yes 2 3356 8.45 1.24 11.18 45.68 80.1 12.4 7.5 0 Yes 1.47 Yes Yes 6 3357 2.9 1.68 11.42 22.02 85.09 14.9 0 0.01 Yes 1.50 Yes Yes 6 3358 5.4 2.65 10.8 37.03 78.7 20.7 0 0.6 No 1.13 Yes Yes 7 3359 10.6 2.22 10.65 28.46 91.29 8.6 0 0.11 Yes 1.26 Yes Yes 6 3360 2.32 2.45 11.34 43.47 85.8 14.2 0 0 Yes 1.14 Yes Yes 2 3361 7.8 2.23 11.62 35.19 98.12 0.08 0 1.8 Yes 1.49 Yes Yes 7 3362 7.95 2.26 11.15 73.02 83.46 15.2 0 1.34 No 1.34 Yes Yes 2 3363 20.59 2.72 12.38 56.20 73.17 17.4 9 0.43 Yes 1.18 Yes Yes 6 3364 22.5 2.13 12.55 35.86 98.6 0.8 0.6 0 Yes 1.17 Yes Yes 6 3365 4.6 1.98 9.34 93.45 93.55 6.4 0.05 0 Yes 1.48 Yes Yes 2 3366 4.9 2.02 9.58 30.66 96.78 3.2 0.02 0 No 1.49 Yes Yes 2 3367 10.5 2.21 9.88 74.21 83 9.2 7.8 0 Yes 1.27 Yes Yes 7 3368 8.45 2.55 10 55.39 70.92 19.2 9.88 0 Yes 1.17 Yes Yes 6 3369 30.5 1.92 10.67 30.08 80.25 15.1 4.65 0 Yes 1.16 Yes Yes 7 3370 49.5 1.96 11.89 45.09 81.85 14.5 3.65 0 Yes 1.27 Yes Yes 2 3371 5.9 2.11 12.03 41.41 89.45 10.5 0.05 0 Yes 1.27 Yes Yes 7 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3352 1 0.09 9.450 46.8 49 Alkyl 60 Brush E silicate 3353 1 13.5 0.483 23.7 35 Alkali 15 Spray E silicate 3354 1 135.4 0.172 53.8 37 Alkyl 24 Spray E silicate 3355 1 3 4.375 53.8 36 Alkali 34 Spray E silicate 3356 1 7.8 1.409 43.7 38 Alkyl 20 Brush E silicate 3357 1 10.2 1.330 55.9 48 Alkali 200 Brush E silicate 3358 1 7 2.588 65.8 46 Alkyl 56 Brush E silicate 3359 1 225.2 0.038 55.7 51 Alkali 34 Spray E silicate 3360 1 5.4 2.219 64.5 46 Alkyl 2 Spray G silicate 3361 1 3.2 0.019 68.9 38 Alkali 15 Spray E silicate 3362 1 13.5 1.048 64.7 48 Alkali 10 Spray E silicate 3363 1 1.6 6.692 77.9 52 Alkyl 125 Brush E silicate 3364 1 1.5 0.320 43.7 30 Alkali 24 Brush E silicate 3365 1 2.5 1.829 7.8 76 Alkyl 110 Brush E silicate 3366 1 2.6 0.889 16.0 72 Alkali 24 Brush E silicate 3367 1 126 0.072 89.6 81 Alkyl 2 Spray G silicate 3368 1 120 0.159 11.8 64 Alkali 37 Spray E silicate 3369 1 7.5 1.776 4.6 69 Alkyl 113 Brush E silicate 3370 1 6.5 1.933 2.5 83 Alkali 2 Spray G silicate 3371 1 2.0 0.500 18.9 30 Alkyl 75 Brush E silicate

TABLE 170 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3372 4.52 2.97 12.12 17.75 87.3 7.5 5.2 0 Yes 1.49 Yes Yes 6 3373 5.96 2.36 12.28 32.76 93.9 6.1 0 0.001 Yes 1.29 Yes Yes 7 3374 5.5 3.05 12.52 30.89 82.55 16.8 0.05 0.6 Yes 1.23 Yes Yes 6 3375 3.6 2.57 11.9 45.90 70.7 27.5 1 0.8 Yes 1.23 Yes Yes 7 3376 16.5 2.65 11.75 42.22 94.6 2.9 0 2.5 Yes 1.23 Yes Yes 6 3377 12.5 2.54 12.44 18.56 94 4.5 0 1.5 No 1.23 Yes Yes 2 3378 16.5 2.85 12.03 33.57 99.43 0.07 0 0.5 Yes 1.27 Yes Yes 7 3379 10.9 2.75 10.61 31.70 96.82 3.1 0.04 0.04 Yes 1.23 Yes Yes 6 3380 5.6 2.46 11.3 46.71 76.3 20.5 1 2.2 Yes 1.36 Yes Yes 6 3381 22.6 2.71 11.58 47.89 68.84 29.5 0.06 1.6 Yes 1.11 Yes Yes 6 3382 20.59 2.36 11.11 24.23 92.33 7.6 0.07 0 Yes 1.02 Yes Yes 2 3383 20.59 2.16 12.34 39.24 95.2 0.7 1.2 2.9 Yes 1.05 Yes Yes 6 3384 9.56 2.46 12.51 37.37 91.8 4.6 1.8 1.8 Yes 1.24 Yes Yes 7 3385 5.9 2.49 11.64 50.38 82 8.3 9.2 0.5 Yes 1.33 Yes Yes 2 3386 6.54 1.63 9.16 37.14 88.2 11.8 0 0 Yes 1.27 Yes Yes 6 3387 21.4 1.51 9.46 13.48 86.06 12.9 0 1.04 Yes 1.50 Yes Yes 2 3388 9.8 3.05 9.54 40.05 99.34 0.6 0 0.06 Yes 1.13 Yes Yes 6 3389 6.59 2.57 9.56 38.18 89.51 9.5 0 0.99 No 1.04 Yes Yes 7 3390 6.54 2.65 9.46 7.63 88.3 11.7 0 0 Yes 1.02 Yes Yes 7 3391 16.5 2.54 11.99 37.95 89.9 9.4 0.7 0 Yes 1.08 Yes Yes 2 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3372 1 0.007 7.448 75.9 83 Alkali 30 Brush E silicate 3373 1 9 0.610 55.9 75 Alkyl 34 Brush E silicate 3374 1 7.5 1.976 53.8 76 Epoxy 124 Brush E resin 3375 1 50 0.539 97.5 72 Acrylic 15 Spray E resin 3376 1 0.005 2.886 88.4 71 Urethane 23 Spray E resin 3377 1 25.6 0.169 54.8 82 Polyester 157 Brush E resin 3378 1 56.5 0.001 45.7 81 Epoxy 26 Spray E resin 3379 1 1.6 1.192 34.7 83 Acrylic 38 Spray E resin 3380 1 3 5.125 57.9 50 Urethane 160 Brush E resin 3381 1 100 0.292 65.4 72 Polyester 27 Brush E resin 3382 1 65.5 0.114 87.9 47 Epoxy 180 Brush E resin 3383 1 1.9 0.241 2.9 47 Acrylic 26 Spray E resin 3384 1 2.1 1.484 12.6 52 Urethane 180 Brush E resin 3385 1 10.5 0.722 53.8 52 Polyester 15 Spray E resin 3386 1 6.5 1.573 17.8 50 Epoxy 2 Spray G resin 3387 1 19.5 0.629 34.7 46 Acrylic 28 Spray E resin 3388 1 0.8 0.333 55.7 47 Urethane 30 Spray E resin 3389 1 18.5 0.487 64.5 83 Polyester 2 Spray G resin 3390 1 4.3 2.208 68.9 52 Epoxy 157 Brush E resin 3391 1 3.2 2.238 64.7 89 Acrylic 28 Brush E resin

TABLE 171 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3392 7.8 2.85 12.08 14.29 87.8 11.7 0.5 0 Yes 1.15 Yes Yes 2 3393 16.5 2.75 12.24 40.86 95.6 4.2 0.2 0 Yes 1.34 Yes Yes 6 3394 6.54 2.46 12.48 97.50 97.13 2.8 0.07 0 Yes 1.25 Yes Yes 7 3395 8.45 2.71 11.86 13.30 86.1 13.9 0 0 Yes 1.19 Yes Yes 6 3396 8.5 2.36 11.71 43.62 82.6 14.6 1.6 1.2 No 1.18 Yes Yes 7 3397 13.6 2.46 11.35 56.93 72.95 26.4 0.65 0 Yes 1.24 Yes Yes 6 3398 12.33 1.45 12.02 36.59 83.23 16.5 0.27 0 Yes 1.11 Yes Yes 2 3399 16.5 2.42 13.24 39.95 79.4 19.5 0.45 0.65 Yes 1.27 Yes Yes 2 3400 7.9 2.11 9.46 86.50 97.08 1.6 0.33 0.99 Yes 1.31 Yes Yes 6 3401 10.5 2.97 13.47 32.87 90.5 6 1 2.5 Yes 1.26 Yes Yes 7 3402 16.5 2.36 9.46 16.23 88.93 8.4 0.87 1.8 Yes 1.14 Yes Yes 6 3403 10.64 3.05 13.87 37.40 86.7 13.3 0 0 Yes 1.34 Yes Yes 6 3404 10.5 2.57 13.25 40.76 81.4 18.6 0. 0 Yes 1.16 Yes Yes 2 3405 20.59 2.65 13.1 87.31 97.34 1.8 0.86 0 No 1.47 Yes Yes 7 3406 8.5 2.12 9.08 92.50 95.25 4.1 0.65 0 Yes 1.48 Yes Yes 2 3407 0.5 1.65 9.87 17.93 82.87 16.7 0.43 0 No 1.49 Yes Yes 2 3408 10.5 2.35 9.46 44.50 99 0.4 0.6 0 Yes 1.34 Yes Yes 6 3409 11.5 1.63 9.28 96.50 89.35 10.6 0.05 0 Yes 1.29 Yes Yes 7 3410 36.5 2.64 9.45 16.94 93.08 6.9 0.02 0 Yes 1.18 Yes Yes 7 3411 1.5 2.35 9.25 88.12 99.82 0.05 0.06 0.07 Yes 1.48 Yes Yes 6 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3392 1 1.5 4.680 77.9 85 Alkyl 130 Brush E silicate 3393 1 4.5 0.764 43.7 53 Alkyl 29 Brush E silicate 3394 1 15.5 0.170 7.8 88 Epoxy 30 Brush E resin 3395 1 10.5 1.209 16.0 85 Acrylic 120 Brush E resin 3396 1 2.5 4.171 89.6 52 Urethane 187 Brush E resin 3397 1 9 2.640 11.8 83 Polyester 28 Spray E resin 3398 1 10.5 0.156 4.6 88 Epoxy 5 Spray E resin 3399 1 5.7 2.910 2.5 49 Acrylic 35 Spray E resin 3400 1 3.9 0.327 18.9 50 Urethane 5 Spray G resin 3401 1 4.5 1.091 75.9 51 Polyester 200 Brush E resin 3402 1 3.6 1.826 55.9 83 Alkali 25 Spray E silicate 3403 1 16.4 0.764 53.8 82 Alkali 15 Spray E silicate 3404 1 6 2.657 97.5 88 Alkyl 20 Spray E silicate 3405 1 7.5 0.212 88.4 85 Alkali 18 Spray E silicate 3406 1 10.5 0.357 54.8 87 Alkyl 22 Spray E silicate 3407 1 2.6 4.639 45.7 86 Alkali 19 Spray E silicate 3408 1 1.5 0.160 34.7 46 Alkyl 29 Spray E silicate 3409 1 13.5 0.731 57.9 49 Alkali 23 Spray E silicate 3410 1 2.6 1.917 65.4 35 Alkyl 21 Spray E silicate 3411 1 6.5 0.007 87.9 30 Alkali 19 Spray E silicate

TABLE 172 Percent Diameter of fine- Mg solid distribution grain solution (peak metal phase and diameter) of grains Zn—Mg Any of Ave diameter Zn metal among Zn Chemical component Alloy inter- MgZn2, of later- grains/Zn metal content of Zn metal grain metallic Mg2Zn11, added Zn alloy grains grains/ grains/Zn alloy fracture compounds Mg2Zn3, Invention metal (μm) Zn alloy grains surfaces present on MgZn, Example grains Fine Coarse grains (Mass %) or cracks Average grain Mg7Zn3 Number of No (μm) metal metal (Vol %) Zn Mg Al Si present? aspect ratio surfaces? present? faces 3412 8.7 2.31 9.46 60.57 91.56 6.4 1.05 0.99 Yes 1.27 Yes Yes 7 3413 7.8 2.62 9.46 39.48 93.36 3.5 2.6 0.54 Yes 1.17 Yes Yes 7 3414 5.96 2.52 9.46 15.82 82.13 17.5 0.05 0.32 Yes 1.27 Yes Yes 6 3415 0.06 2.24 13.32 49.57 91.2 3.6 5.2 0 No 1.27 Yes Yes 7 3416 0.9 0.05 6.54 86.52 94.1 5.9 0 0.001 Yes 1.48 Yes Yes 2 3417 3.6 2.42 6.35 90.98 83.2 16.2 0 0.6 No 1.49 Yes Yes 7 3418 10.5 0.11 7.54 67.32 76.7 22.5 0 0.8 Yes 1.34 Yes Yes 7 3419 0.05 1.92 8.64 82.33 96.52 3.4 0.04 0.04 Yes 1.23 Yes Yes 2 3420 2.32 0.46 6.45 73.76 68.3 26.5 3 2.2 Yes 1.23 Yes Yes 6 3421 20.4 0.77 6.48 88.77 72.84 25.5 0.06 1.6 Yes 1.23 Yes Yes 6 3422 8.6 2.35 9.25 45.02 87.2 12.8 0 0 Yes 1.05 Yes Yes 6 3423 10.5 2.33 9.46 15.2 91.5 8.5 0 0 Yes 1.06 Yes Yes 7 3424 8.7 1.95 9.32 51.41 75.23 24.5 0.27 0 Yes 1.38 Yes Yes 7 3425 7.8 2.15 9.22 45.46 77.48 18.4 2.55 1.57 Yes 1.06 Yes Yes 6 3426 5.96 2.23 11.62 35.19 72.62 0.08 25.5 1.8 Yes 1.49 Yes Yes 7 3427 1.6 2.26 11.15 73.02 64.06 15.2 19.4 1.34 No 1.34 Yes Yes 2 3428 7.2 1.98 9.34 93.45 83 6.4 10.6 0 Yes 1.48 Yes Yes 7 3429 10.5 2.02 9.58 30.66 86.4 3.2 10.4 0 No 1.49 Yes Yes 7 3430 3.6 2.36 12.28 32.76 80.4 6.1 13.5 0.001 Yes 1.29 Yes Yes 2 3431 4.5 3.05 12.52 30.89 70.1 16.8 12.5 0.6 Yes 1.23 Yes Yes 6 3432 7.9 2.57 11.9 45.9 60.9 27.5 10.8 0.8 Yes 1.23 Yes Yes 6 Ratio of (Zn metal Coating details grains or Zn alloy Ratio of fine grains):(Later- metal grains added Zn metal in coat grains) Mg outermost Total Later- content surface layer metal Zn metal added of all 10% thickness grain Invention grains/ Zn metal to total fine content Base Coat Example Zn alloy Metal grains metal grains of coat resin thickness Coating Corrosion No grains grains (Mass %) (Mass % (Mass %) type (μm) method Test Results 3412 1 1.6 2.462 2.9 76 Alkyl 15 Spray E silicate 3413 1 3.8 0.729 12.6 72 Alkali 18 Spray E silicate 3414 1 0.08 16.204 53.8 30 Alkyl 22 Spray E silicate 3415 1 164.5 0.022 17.8 83 Alkyl 21 Spray E silicate 3416 1 3.6 1.283 34.7 75 Alkyl 29 Spray E silicate 3417 1 8.6 1.688 76.8 76 Alkali 23 Spray E silicate 3418 1 12 1.731 58.9 72 Alkyl 21 Spray E silicate 3419 1 5.8 0.500 50.8 83 Alkali 19 Spray E silicate 3420 1 10 2.409 46.8 50 Alkyl 21 Spray E silicate 3421 1 1 12.750 23.7 72 Alkali 19 Spray E silicate 3422 1 10.5 1.113 87.9 50 Acrylic 654 Spray E resin 3423 1 6.5 1.133 2.9 48 Alkali 700 Spray E silicate 3424 1 19.5 1.195 12.6 75 Alkyl 555 Spray E silicate 3425 1 0.8 10.222 53.8 55 Alkyl 12 Spray E silicate 3426 1 5.3 0.013 17.8 38 Alkyl 152 Brush E silicate 3427 1 4.3 2.868 34.7 48 Urethane 674 Spray E resin 3428 1 3.2 1.524 76.8 76 Polyester 325 Spray E resin 3429 1 1.5 1.280 58.9 72 Alkyl 665 Spray E silicate 3430 1 4.5 1.109 50.8 75 Alkyl 354 Brush E silicate 3431 1 0.8 9.333 46.8 76 Alkyl 165 Spray E silicate 3432 1 6.5 3.667 23.7 72 Urethane 354 Spray E resin

INDUSTRIAL APPLICABILITY

As explained in the foregoing, the present invention enables provision of highly corrosion-resistant coating material and highly corrosion-resistant steel that exhibit excellent corrosion-resistance and rust prevention unattainable using the metal particles added to conventional rust-prevention coating materials. It achieves this improvement over the prior art by producing Zn metal particles or Zn alloy particles having two grain-diameter frequency peaks in the grain-diameter frequency distribution and combining the particles with an inorganic or organic binder.

The present invention therefore can therefore be advantageously applied for primary rust proofing or combating corrosion of steel materials used in industrial machinery, vehicles, ships, chemical industry facilities, buildings, bridges and the like. As such, it has considerable industrial applicability. 

What is claimed is:
 1. A highly corrosion-resistant, rust-prevention coating material comprising: one of an organic binder and an inorganic binder; and Zn-alloy particles, the Zn-alloy particles comprising Zn, 0.1 to 30 percent Mg, and unavoidable impurities, and having physical fragmentation faces and/or cracks of 0.01 μm or greater length, or cracks of 0.01 μm or greater depth, wherein a Mg solid solution phase and Zn—Mg intermetallic compounds are present at fracture facets and/or cracks, wherein the Zn-alloy particles are dispersed in the binder in an amount of 30 mass % or greater based on a mass of a dry coating film of the coating material, wherein (i) the Zn-alloy particles include: (i-1) fine-grain Zn-alloy particles having a peak grain diameter in the range of 0.05 to 5 μm, the fine-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, and (i-2) coarse-grain Zn-alloy particles having a peak grain diameter in the range of 6 to 100 μm, the coarse-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, such that a grain-diameter frequency distribution of all the Zn-alloy particles has the grain-diameter frequency distribution peak of the fine-grain Zn-alloy particles and the grain-diameter frequency distribution peak of the coarse-grain Zn-alloy particles; and wherein (ii) 5 to 99% in volume percent of the Zn-alloy particles are Zn-alloy particles have a diameter in the range of 0.05 to 5 μm.
 2. The highly corrosion-resistant, rust-prevention coating material according to claim 1, the Zn alloy particles having an average aspect ratio value, determined from maximum grain diameter/minimum grain diameter, in a range of 1 to 1.5.
 3. The highly corrosion-resistant, rust-prevention coating material according to claim 1, wherein the Zn—Mg intermetallic compounds are selected from the group consisting of MgZn₂, Mg₂Zn₁₁, Mg₂Zn₃, MgZn, Mg₇Zn₃, and combinations thereof.
 4. The highly corrosion-resistant, rust-prevention coating material according to claim 1, wherein the Zn-alloy particles are polyhedrons having multiple flat or curved surfaces each enclosed by a single contour line.
 5. The highly corrosion-resistant, rust-prevention coating material according to claim 1, further comprising, dispersed in the binder, metal particles of Zn and a balance of unavoidable impurities, the dispersed metal particles of Zn and a balance of unavoidable impurities having an average grain diameter of 0.05 to 50 μm, wherein (a) 5 to 99% in volume percent of all metal particles are Zn-alloy particles having a grain diameter of 0.05 to 50 μm; and (b) the metal particles are dispersed in the binder in an amount of 30 mass % or greater based on a mass of a dry coating film of the coating material.
 6. The highly corrosion-resistant, rust-prevention coating material according to claim 1, wherein the binder is an organic binder.
 7. A highly corrosion-resistant, rust-prevention coating material comprising: one of an organic binder and an inorganic binder; Zn-alloy particles comprising Zn, 0.1 to 30 percent Mg, and unavoidable impurities; and metal particles of Zn and a balance of unavoidable impurities, the metal particles of Zn and a balance of unavoidable impurities having an average grain diameter of 0.05 to 50 μm; wherein the Zn-alloy particles and metal particles of Zn and a balance of unavoidable impurities are dispersed in the binder in an amount of 30 mass % or greater based on a mass of a dry coating film of the coating material; wherein (i) the Zn-alloy particles include: (i-1) fine-grain Zn-alloy particles having a peak grain diameter in the range of 0.05 to 5 μm, the fine-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, and (i-2) coarse-grain Zn-alloy particles having a peak grain diameter in the range of 6 to 100 μm, the coarse-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, such that a grain-diameter frequency distribution of all the Zn-alloy particles has the grain-diameter frequency distribution peak of the fine-grain Zn-alloy particles and the grain-diameter frequency distribution peak of the coarse-grain Zn-alloy particles; and wherein (ii) 5 to 99% in volume percent of the Zn-alloy particles are Zn-alloy particles have a diameter in the range of 0.05 to 5 μm; and wherein 5 to 99% in volume percent of all metal particles are Zn alloy particles have a grain diameter of 0.05 to 5 μm; wherein a ratio, in mass %, of one of the amount of the fine-grain and coarse-grain Zn-alloy particles or the amount of the fine-grain and coarse-grain Zn alloy particles to the amount of the Zn metal particles of an average grain diameter of 0.05 to 50 μm containing Zn and a balance of unavoidable impurities is 1/300.0 or less.
 8. The highly corrosion-resistant, rust-prevention coating material according to claim 7, wherein the Mg content of the mixed particles including the Zn alloy particles and the Zn metal particles of an average grain diameter of 0.05 to 50 μm containing Zn and a balance of unavoidable impurities is 0.01 to less than 30 mass % where the total of the mixed particles is defined as 100 mass %.
 9. A highly corrosion-resistant steel coated with a highly corrosion-resistant, rust-prevention coating material, a dry coating film of the coating material having a thickness of 2 to 700 μm, the coating material comprising: one of an organic binder and an inorganic binder; and Zn alloy particles comprising Zn, Mg: 0.01 to 30%, and unavoidable impurities, the Zn alloy particles dispersed in the binder in an amount of 30 mass % or greater based on a mass of a dry coating film of the coating material, wherein (i) the Zn alloy particles include: (i-1) fine-grain Zn alloy particles having a peak grain diameter in the range of 0.05 to 5 μM, the fine-grain Zn alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, and (i-2) coarse-grain Zn alloy particles having a peak grain diameter in the range of 6 to 100 μm, the coarse-grain Zn alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, such that a grain-diameter frequency distribution of all the Zn alloy particles has the grain-diameter frequency distribution peak of the fine-grain Zn alloy particles and the grain-diameter frequency distribution peak of the coarse-grain Zn alloy particles; and wherein (ii) 5 to 99% in volume percent of the Zn alloy particles are Zn alloy particles having a diameter in the range of 0.05 to 5 μm and wherein the fine-grain Zn alloy particles having a grain diameter of 0.05 to 5 μm are present in an amount in an outermost 10% thickness surface layer region of the dry film that is at least twice the amount of the fine-grain Zn alloy particles of a grain diameter of 0.05 to 5 μm in the dry film as a whole.
 10. A highly corrosion-resistant steel coated with a highly corrosion-resistant, rust-prevention coating material, comprising: a dry coating film of a coating material having a thickness of 2 to 700 μm, the coating material comprising: one of an organic binder and an inorganic binder; and Zn-alloy particles, the Zn-alloy particles comprising Zn, 0.1 to 30 percent Mg, and unavoidable impurities, and having physical fragmentation faces and/or cracks of 0.01 μm or greater length, or cracks of 0.01 μm or greater depth, wherein a Mg solid solution phase and Zn—Mg intermetallic compounds are present at fracture facets and/or cracks, wherein the Zn-alloy particles are dispersed in the binder in an amount of 30 mass % or greater based on a mass of a dry coating film of the coating material, wherein (i) the Zn-alloy particles include: (i-1) fine-grain Zn-alloy particles having a peak grain diameter in the range of 0.05 to 5 μm, the fine-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, and (i-2) coarse-grain Zn-alloy particles having a peak grain diameter in the range of 6 to 100 μm, the coarse-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, such that a grain-diameter frequency distribution of all the Zn-alloy particles has the grain-diameter frequency distribution peak of the fine-grain Zn-alloy particles and the grain-diameter frequency distribution peak of the coarse-grain Zn-alloy particles; and wherein (ii) 5 to 99% in volume percent of the Zn-alloy particles are Zn-alloy particles having a diameter in the range of 0.05 to 5 μm.
 11. A steel structure comprising: a highly corrosion-resistant steel coated with a highly corrosion-resistant, rust-prevention coating material, the highly corrosion-resistant, rust-prevention coating material comprising: a dry coating film of the coating material having a thickness of 2 to 700 μm, the coating material comprising: one of an organic binder and an inorganic binder; and Zn-alloy particles comprising Zn, 0.1 to 30 percent Mg, and unavoidable impurities, and having physical fragmentation faces and/or cracks of 0.01 μm or greater length, or cracks of 0.01 μm or greater depth; wherein a Mg solid solution phase and Zn—Mg intermetallic compounds are present at fracture facets and/or cracks, wherein the Zn-alloy particles are dispersed in the binder in an amount of 30 mass % or greater based on a mass of a dry coating film of the coating material, wherein (i) the Zn-alloy particles include: (i-1) fine-grain Zn-alloy particles having a peak grain diameter in the range of 0.05 to 5 μm, the fine-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, and (i-2) coarse-grain Zn-alloy particles having a peak grain diameter in the range of 6 to 100 μm, the coarse-grain Zn-alloy particles having a grain-diameter distribution, a grain-diameter frequency distribution of the grain diameter distribution having a single peak and a tail on either side of the peak, such that a grain-diameter frequency distribution of all the Zn-alloy particles has the grain-diameter frequency distribution peak of the fine-grain Zn-alloy particles and the grain-diameter frequency distribution peak of the coarse-grain Zn-alloy particles; and wherein (ii) 5 to 99% in volume percent of the Zn-alloy particles are Zn-alloy particles having a diameter in the range of 0.05 to 5 μm. 